A kind of nanoemulsion calcium-zinc stabilizer for PVC products and preparation method thereof

A calcium-zinc stabilizer and nanoemulsion technology, applied in the field of PVC heat stabilizers, can solve problems such as poor lubricity, lower softening point of products, easy occurrence of white spots, scratches, etc., to reduce the probability of measurement errors, simple supply and The effects of storage and product performance

Active Publication Date: 2022-04-19
广东原基新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Calcium zinc stabilizer is made of calcium salt, zinc salt, lubricant, antioxidant, etc. as the main components, and is made by corresponding composite technology. Calcium zinc stabilizer is usually divided into powder calcium zinc stabilizer and liquid calcium zinc stabilizer , the liquid calcium zinc stabilizer has good compatibility with resin and plasticizer, good transparency, and is not easy to precipitate, but its lubricity is poor, which will reduce the softening point of the product, and will deteriorate in long-term storage; solid calcium zinc stabilizer according to Its appearance can be divided into powder form, which is characterized by good lubricity and will not reduce the softening point of PVC hard products, but poor compatibility, precipitation and blooming, easy to absorb moisture, poor dispersion, easy to appear white spots, Scratches, etc., affect the quality of PVC products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nanoemulsion calcium-zinc stabilizer for PVC products and preparation method thereof
  • A kind of nanoemulsion calcium-zinc stabilizer for PVC products and preparation method thereof
  • A kind of nanoemulsion calcium-zinc stabilizer for PVC products and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The invention provides a nanoemulsion calcium-zinc stabilizer for PVC products, which consists of the following raw materials in parts by weight:

[0046] Powder calcium zinc composite stabilizer: 30 parts

[0047] Liquid calcium zinc composite stabilizer: 30 parts

[0048] Emulsifier: 40 parts

[0049] Auxiliary: 20 parts

[0050] The powder calcium-zinc composite stabilizer includes: 30 parts of main stabilizer, 12 parts of auxiliary stabilizer, 5 parts of antioxidant, 0.2 part of ultraviolet absorber, 0.5 part of light stabilizer and 5 parts of lubricant.

[0051] Wherein, the main stabilizer is calcium stearate, zinc stearate, magnesium stearate, the main stabilizer compounded with a mass ratio of 5:1:1.

[0052] Wherein, the auxiliary stabilizer is 4A zeolite, hydrotalcite, stearoylbenzoylmethane, dibenzoylmethane, Saike, polyhydric alcohol, carried out with a mass ratio of 8:2:1:0.5:1:5 Compound auxiliary stabilizer.

[0053] The polyhydric alcohol is one or ...

Embodiment 2

[0074] The invention provides a nanoemulsion calcium-zinc stabilizer for PVC products, which consists of the following raw materials in parts by weight:

[0075] Powder calcium zinc composite stabilizer: 35 parts

[0076] Liquid calcium zinc composite stabilizer: 20 parts

[0077] Emulsifier: 30 parts

[0078] Auxiliary: 15 parts

[0079] The powder calcium-zinc composite stabilizer includes: 45 parts of main stabilizer, 15 parts of auxiliary stabilizer, 30 parts of antioxidant, 1 part of ultraviolet absorber, 0.5 part of light stabilizer and 5 parts of lubricant.

[0080] Wherein, the main stabilizer is calcium stearate, zinc stearate, magnesium stearate, the main stabilizer compounded with a mass ratio of 4:1.5:1.2.

[0081] Wherein, the auxiliary stabilizer is 4A zeolite, hydrotalcite, stearyl benzoylmethane, dibenzoylmethane, Saike, polyhydric alcohol, and the mass ratio is 4:2:2:1:1.5:4 Compound auxiliary stabilizer.

[0082] The polyhydric alcohol is one or more of ...

Embodiment 3

[0103] The invention provides a nanoemulsion calcium-zinc stabilizer for PVC products, which consists of the following raw materials in parts by weight:

[0104] Powder calcium zinc composite stabilizer: 38 parts

[0105] Liquid calcium zinc composite stabilizer: 25 parts

[0106] Emulsifier: 38 parts

[0107] Auxiliary: 12 parts

[0108] The powder calcium-zinc composite stabilizer includes: 55 parts of main stabilizer, 38 parts of auxiliary stabilizer, 21 parts of antioxidant, 0.8 part of ultraviolet absorber, 0.3 part of light stabilizer and 12 parts of lubricant.

[0109] Wherein, the main stabilizer is calcium stearate, zinc stearate, magnesium stearate, the main stabilizer compounded with a mass ratio of 5:2:1.

[0110] Wherein, the auxiliary stabilizer is 4A zeolite, hydrotalcite, stearyl benzoylmethane, dibenzoylmethane, Saike, polyhydric alcohol, and the mass ratio is 5:2.5:3:1:1:3. Compound auxiliary stabilizer.

[0111] The polyhydric alcohol is one or more of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
turbidityaaaaaaaaaa
relative humidityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanoemulsion calcium-zinc stabilizer for PVC products, which is composed of the following raw materials in parts by weight: powder calcium-zinc composite stabilizer: 30-40 parts, liquid calcium-zinc composite stabilizer: 20-30 parts, emulsified Agent: 30-40 parts, auxiliary agent: 10-20 parts; the powder calcium-zinc composite stabilizer includes: 30-60 parts of main stabilizer, 10-40 parts of auxiliary stabilizer, 5-35 parts of antioxidant, 0.1-2 parts of ultraviolet absorber, 0.2-1 part of light stabilizer, and 1-15 parts of lubricant; adopting the nanoemulsion calcium-zinc stabilizer of the present invention can solve the problem of poor lubricity of a single liquid stabilizer and reduce the softening of products Points, long-term storage will deteriorate, and the single powder stabilizer has poor compatibility, easy to precipitate and bloom, and easy to absorb moisture, poor dispersibility, easy to appear white spots, scratches and other problems, and solve the problem of powder stabilizer Compatibility and dispersibility problems during production with liquid stabilizers ensure better product performance and a smoother finished product surface.

Description

technical field [0001] The invention relates to the technical field of PVC heat stabilizers, in particular to a nanoemulsion calcium-zinc stabilizer for PVC products and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the five general-purpose plastics. Due to its excellent comprehensive performance and low price, it has been widely used in various fields, and its consumption is second only to polyethylene. However, due to the poor thermal stability of PVC, it is necessary to add an appropriate amount of heat stabilizer to inhibit the degradation of PVC during processing. At present, the commonly used human stabilizers can be roughly divided into lead salts, metal soaps, organotins, and rare earth heat stabilizers. Under the main theme of global environmental protection, the highly toxic lead salt heat stabilizers are gradually withdrawing from the market, the organotin heat stabilizers with superior performance are difficult to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L23/30C08K13/04C08K7/26C08K3/26C08K5/098C08K5/053C08K5/3492C08K5/526C08K5/524C08K5/521C08K5/07C08K5/134C08K5/103
CPCC08L27/06C08L2201/08C08K2201/011C08K2201/014C08L23/30C08K13/04C08K7/26C08K3/26C08K5/098C08K5/053C08K5/34924C08K5/526C08K5/524C08K5/521C08K5/07C08K5/1345C08K5/103
Inventor 王国平
Owner 广东原基新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com