Plugging filtrate reducer elastic graphite for drilling fluid
A technology of fluid loss reducer and elastic graphite, which is applied in the directions of reagents, drilling compositions, products, etc., can solve the problems of large drilling fluid filtration loss, increased filtration loss, differential pressure sticking, etc. The effect of mechanical properties and wear resistance, expansion ratio improvement, and dispersion effect improvement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1
[0031] Elastomeric graphite as a plugging fluid loss reducer for drilling fluids, including the following raw materials by weight: 100 parts of fine flake graphite particles, 300 parts of mixed acid solution, 0.6 parts of potassium permanganate, 0.5 parts of ferric chloride, 20 parts of inorganic hydroxide Material, 1 part silane coupling agent, 80 parts reaction solvent, 200 parts dispersant, 30 parts modifier;
[0032] The preparation method of elastic graphite for plugging fluid loss reducer for drilling fluid is as follows:
[0033] The first step is to add fine flake graphite particles to the mixed acid solution, stir at 1000r / min for 30min, then add potassium permanganate, stir at 500r / min for 20min, let stand for 1h, and then add ferric chloride , Stirring at a speed of 1500r / min for 2 hours to obtain a mixture A;
[0034] In the second step, the inorganic hydroxide, silane coupling agent and reaction solvent are added to the mixture A, and the mixture is st...
Example Embodiment
[0048] Example 2
[0049] Elastomeric graphite as a plugging fluid loss reducer for drilling fluids, including the following raw materials by weight: 130 parts of fine flake graphite particles, 350 parts of mixed acid solution, 0.8 parts of potassium permanganate, 0.6 parts of ferric chloride, 30 parts of inorganic hydroxide Material, 6 parts silane coupling agent, 90 parts reaction solvent, 220 parts dispersant, 40 parts modifier;
[0050] The preparation method of elastic graphite for plugging fluid loss reducer for drilling fluid is as follows:
[0051] The first step is to add fine flake graphite particles to the mixed acid solution, stir at 1300r / min for 40min, then add potassium permanganate, stir at 600r / min for 30min, stand for 1h, then add ferric chloride , Stirring for 8 hours at a speed of 1700r / min, to obtain a mixture A;
[0052] In the second step, add inorganic hydroxide, silane coupling agent and reaction solvent to mixture A, and stir for 1 hour at a temperature of 1...
Example Embodiment
[0066] Example 3
[0067] Elastomeric graphite as a plugging fluid loss reducer for drilling fluids, including the following raw materials by weight: 150 parts of fine flake graphite particles, 400 parts of mixed acid solution, 1.0 part of potassium permanganate, 0.7 part of ferric chloride, 60 parts of inorganic hydroxide Material, 10 parts silane coupling agent, 100 parts reaction solvent, 250 parts dispersant, 50 parts modifier;
[0068] The preparation method of elastic graphite for plugging fluid loss reducer for drilling fluid is as follows:
[0069] The first step is to add fine flake graphite particles to the mixed acid solution, stir at 1500r / min for 60min, then add potassium permanganate, stir at 1000r / min for 40min, stand for 1h, and then add ferric chloride , Stirring at a speed of 2000r / min for 10 hours to obtain a mixture A;
[0070] In the second step, add inorganic hydroxide, silane coupling agent and reaction solvent to mixture A, and stir for 3 hours at a temperatur...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap