Wide-range sintered glass ink for automobile laminated glass and preparation method of wide-range sintered glass ink

A technology of laminated glass and sintered glass, applied in the field of ink materials, can solve the problems of only one or two, and achieve the effects of wide sintering range, increased storage stability, and increased wettability

Pending Publication Date: 2020-11-27
湖南衡义材料科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the development trend of domestic laminated glass inks is rapid, because the technical requirements of laminated glass inks are relatively low, and they have the potential to replace imported inks. However, there is no such thing on the market that has an acid resistance of more than 8 hours, a wide sintering range, and can cover different sizes. Curvature glass, can match the laminated glass ink used in silver paste, most of the products can only meet one or two requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wide-range sintered glass ink for automobile laminated glass and preparation method of wide-range sintered glass ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A wide-area sintered glass ink for automotive laminated glass. Its components are calculated by the following weight percentages: acid-resistant glass powder 58%, low temperature glass powder 5%, silver paste matching glass powder 2%, copper chrome melanin 15%, and ink blending oil 20%.

[0033] A preparation method of wide-area sintered glass ink for automobile laminated glass includes the following steps:

[0034] (1) According to the weight ratio of the above formula, first weigh the ink blending oil and copper-chromium melanin, and stir evenly at high speed, and the stirring time is 20-30min;

[0035] (2) Slowly add acid-resistant glass powder, low-temperature glass powder, and silver paste to match glass powder, stir and mix well;

[0036] (3) After stirring evenly, let it stand to cool for 16 hours and defoam;

[0037] (4) The slurry after standing is ground to a fineness of less than 10um and a viscosity of 40 Pas through a three-roller machine to obtain a wide-range sint...

Embodiment 2

[0040] A wide-area sintered glass ink for automotive laminated glass. Its components are calculated by the following weight percentages: 30% acid-resistant glass powder, 15% low-temperature glass powder, 10% silver paste matching glass powder, 30% copper-chromium melanin, and ink blending oil 15%.

[0041] A preparation method of wide-area sintered glass ink for automobile laminated glass includes the following steps:

[0042] (1) According to the weight ratio of the above formula, first weigh the ink blending oil and copper-chromium melanin, and stir evenly at high speed, and the stirring time is 20-30min;

[0043] (2) Slowly add acid-resistant glass powder, low-temperature glass powder, and silver paste to match glass powder, stir and mix well;

[0044] (3) After stirring evenly, let it stand to cool for 8 hours and defoam;

[0045] (4) The slurry after standing is ground to a fineness of 10um or less and a viscosity of 80 Pas through a three-roller machine to obtain a wide range sin...

Embodiment 3

[0048] A wide-area sintered glass ink for automobile laminated glass, the components of which are calculated by the following weight percentages: 60% acid-resistant glass powder, 7% low-temperature glass powder, 5% silver paste matching glass powder, 18% copper-chromium melanin, and ink blending oil 10%.

[0049] A preparation method of wide-area sintered glass ink for automobile laminated glass includes the following steps:

[0050] (1) According to the weight ratio of the above formula, first weigh the ink blending oil and copper-chromium melanin, and stir evenly at high speed, and the stirring time is 20-30min;

[0051] (2) Slowly add acid-resistant glass powder, low-temperature glass powder, and silver paste to match glass powder, stir and mix well;

[0052] (3) After stirring evenly, let it stand to cool for 10 hours and defoam;

[0053] (4) The slurry after standing is ground through a three-roll machine to a fineness of 10um or less and a viscosity of 50 Pas to obtain a wide-ran...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses wide-range sintered glass ink for automobile laminated glass, which belongs to the technical field of ink materials, and comprises the following components in percentage by weight: acid-resistant glass powder, low-temperature glass powder, silver paste matched glass powder, copper-chromium melanin, varnish and a diluent. The invention also discloses a preparation method ofthe wide-range sintered glass ink for the automobile laminated glass, the ink prepared by the method does not contain harmful heavy metals such as lead and cadmium, meets ROHS10 and sustainable development requirements, and is non-toxic, harmless and pollution-free in the preparation process; the softening point of the ink is 450 to 530 DEG C; the thermal expansion coefficient is 60*10 <-7 > / DEG C-90*10<-7 > / DEG C, the Toyota acid-resisting time is longer than 8 h, the sintering temperature range is 520-720 DEG C, glass of different sizes and different curvatures can be covered, silver paste sintering can be matched, cracks are not generated, and the method can be used for forming front windshield laminated glass of cars, SUVs, middle buses and buses.

Description

Technical field [0001] The invention belongs to the technical field of ink materials, and specifically relates to a wide-area sintered glass ink for automobile laminated glass and a preparation method thereof. Background technique [0002] Automobile laminated glass is made of PVB film glued between two pieces of glass. Due to its good safety performance, glass fragments will not splash but adhere to the PVB film when impacted. It is mainly used as automobile front windshield, interlayer Glass ink is applied to the edges of the glass to effectively reduce the UV transmittance, prevent chemical changes in the glue used to bond the glass and the car body, and give the car an aesthetic effect. [0003] Automobile laminated glass can be divided into small-sized laminated glass such as bridge cars and SUVs, medium-sized laminated glass such as medium-sized buses and trucks, and large-sized glass such as buses and buses according to the size of glass forming and the magnitude of curvatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/08C09D11/102C09D11/03C09D11/033C03C17/00C03C12/00
CPCC09D11/08C09D11/102C09D11/03C09D11/033C03C17/008C03C12/00C03C2217/29C03C2217/70C03C2217/72
Inventor 罗渡沙张怀宇
Owner 湖南衡义材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com