Opal glaze for electroceramics as well as preparation method and glazing process of opal glaze

A technology of milky white glaze and electric porcelain, which is applied in the field of electric porcelain, can solve problems such as yellow edges and water edges, which affect the economic benefits of large milky white glaze products, and achieve the goal of improving the whiteness of the glaze, widening the firing temperature range, and improving thermal stability. Effect

Pending Publication Date: 2020-12-04
河北宣化新迪电瓷股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of large-scale electric porcelain products, when some large-scale opalescent glaze products such as integrally formed casings with larger specifications or inorganic bonded porcelain sleeves are glazed by dipping, the middle and lower parts of the products will appear yellow edges, water edges, etc. problem, which seriously affects the economic benefits of large opalescent glaze products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a milky white glaze containing electric porcelain, and the raw materials for preparing the milky white glaze for electric porcelain include the following components by weight percentage:

[0038] Datong sand 8%, talc 10%, limestone 2%, Faku clay 7%, white dry stone 10%, feldspar 28%, silica powder 18%, barium carbonate 2%, zirconium silicate 10%, Suzhou soil 3%, Aluminum oxide 1.9%, dispersant A 150.1%.

[0039] Dry the above-mentioned solid raw material components, control the moisture content of each component within a certain range, then add all raw materials to the ball mill according to the raw material ratio, add water, according to the ratio of material: water: ball = 1:1:1.5 Ball mill for 9 hours, control the weight percentage of water to about 35%, and then pass the obtained slurry through a 300-mesh sieve to obtain glaze slurry. It should be noted that the glaze slurry has also been processed by checking iron.

[0040] The process of...

Embodiment 2

[0046] This embodiment provides a milky white glaze containing electric porcelain, and the raw materials for preparing the milky white glaze for electric porcelain include the following components by weight percentage:

[0047] Datong sand 9%, talc 12%, limestone 1%, Faku clay 4%, white dry stone 9%, feldspar 30%, silica powder 17%, barium carbonate 1.8%, zirconium silicate 12%, Suzhou soil 3%, Aluminum oxide 1%, dispersant 0.2%.

[0048] Dry the above-mentioned solid raw material components, control the moisture content of each component within a certain range, then add all raw materials to the ball mill according to the raw material ratio, add water, according to the ratio of material: water: ball = 1:2:1.5 Ball mill for 10 hours, control the weight percentage of water at about 35%, pass the obtained slurry through a 300-mesh sieve, check for iron, and obtain glaze slurry.

[0049] The process of using the above-mentioned glaze slurry for electric porcelain glazing includes...

Embodiment 3

[0055] This embodiment provides a milky white glaze containing electric porcelain, and the raw materials for preparing the milky white glaze for electric porcelain include the following components by weight percentage:

[0056] Datong sand 5%, talc 12%, limestone 1.1%, Faku clay 4%, white dry stone 10%, feldspar 30%, silica powder 18%, barium carbonate 2%, zirconium silicate 15%, Suzhou soil 3.05%, Aluminum oxide 1.8%, dispersant 0.05%.

[0057] Dry the above-mentioned solid raw material components, control the moisture content of each component within a certain range, then add all the raw materials to the ball mill according to the raw material ratio, add water, according to the ratio of material: water: ball = 1:1:1.5 Ball mill for 8 hours, control the weight percentage of water at about 35%, and then pass the obtained slurry through a 300-mesh sieve to obtain glaze slurry. It should be noted that the glaze slurry has also been processed by checking iron.

[0058] The proc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses opal glaze for electroceramics as well as a preparation method and application of the opal glaze. The opal glaze for the electroceramics is prepared from the following raw materials in percentage by weight: 5-10% of Datong sand, 8-12% of talc, 1-3% of limestone, 4-7% of Faku clay, 9-12% of Baigan stone, 26-34% of feldspar, 17-22% of silica powder, 1-4% of barium carbonate,10-15% of zirconium silicate, 3-4% of Suzhou soil, 1-3% of aluminum oxide and 0.05-0.2% of a dispersing agent. The preparation method comprises the steps of glaze dipping, glaze spraying and roasting.The components in the opal glaze are reasonably matched, aluminum oxide is added on the basis of the prior art to improve the precision of the glaze, and limestone and Suzhou soil are added to increase the high-temperature viscosity of the glaze to adjust the fluidity of the glaze in the high-temperature stage in order to overcome the problems of yellow edges and white edges. The color differenceof white exposure and yellow exposure of the edge part of the product due to too strong fluidity of the glaze in a high-temperature stage is avoided or increased.

Description

technical field [0001] The invention relates to the technical field of electric porcelain, in particular to an opalescent glaze for electric porcelain, a preparation method and a glazing process thereof. Background technique [0002] Electric porcelain is a kind of porcelain electrical insulation material with good insulation and mechanical strength, which is widely used in high and low voltage transmission lines and equipment. The glazing process of electric porcelain can generally be divided into dipping glaze, pouring glaze, spraying glaze, etc., among which the dipping glaze process is more commonly used. With the development of large-scale electric porcelain products, when some large-scale opalescent glaze products such as integrally formed sleeves with larger specifications or inorganic bonded porcelain sleeves are glazed by dipping, yellow edges and water edges will appear in the middle and lower parts of the products. problem, which has seriously affected the econom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B41/86
CPCC03C8/20C04B41/5022C04B41/86C04B41/009
Inventor 马智强董利和汤晓中
Owner 河北宣化新迪电瓷股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap