External wall thermal insulation coating as well as preparation method and application thereof

An external wall insulation and coating technology, applied in fire-resistant coatings, alkali metal silicate coatings, coatings, etc., can solve problems such as inability to meet the market, and achieve the effect of improving weather resistance, improving thermal insulation performance, and taking into account the cost of enterprises

Inactive Publication Date: 2020-12-25
HUBAO NEW MATERIAL TECH SHANGHAI CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The effect is obvious in spring and autumn, and it has a counterproductive effect in winter, which still cannot meet the further demand of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • External wall thermal insulation coating as well as preparation method and application thereof
  • External wall thermal insulation coating as well as preparation method and application thereof
  • External wall thermal insulation coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A thermal insulation coating for exterior walls, comprising the following components by weight:

[0055] 25kg of water;

[0056] Hydroxyethyl cellulose 0.4kg;

[0057] Multifunctional additive AMP-95 0.17kg;

[0058]Sodium lauryl sulfate 0.4kg;

[0059] Ethylene glycol 1.3kg;

[0060] Precipitated barium sulfate 5kg;

[0061] Rutile titanium dioxide 1kg;

[0062] Lithium silicate 36kg;

[0063] Acrylic emulsion 12kg;

[0064] Inorganic water repellent 5kg;

[0065] Glass beads 30kg;

[0066] Its preparation method comprises the following steps:

[0067] (1) Thickening

[0068] Stir 25kg of water at a speed of 600r / min, add 0.4kg of hydroxyethyl cellulose, 0.17kg of multifunctional additive AMP-95, 0.4kg of sodium lauryl sulfate and 1.5kg of ethylene glycol, Add a pH regulator to adjust the pH value to 8.0, and stir for 15 minutes to obtain a thickening system;

[0069] (2) beating

[0070] Add pigments and fillers to the thickening system, the pigments and ...

Embodiment 2

[0076] A thermal insulation coating for exterior walls, comprising the following components by weight:

[0077] 15kg of water;

[0078] Hydroxyethyl cellulose 0.2kg;

[0079] Multifunctional additive AMP-95 0.1kg;

[0080] Sodium lauryl sulfate 0.3kg;

[0081] Ethylene glycol 1kg;

[0082] Precipitated barium sulfate 5kg;

[0083] Rutile titanium dioxide 1kg;

[0084] Lithium silicate 36kg;

[0085] Acrylic emulsion 8kg;

[0086] Inorganic water repellent 3kg;

[0087] Glass beads 30kg;

[0088] Its preparation method is identical with embodiment 1.

Embodiment 3

[0090] A thermal insulation coating for exterior walls, comprising the following components by weight:

[0091] 30kg of water;

[0092] Hydroxyethyl cellulose 0.5kg;

[0093] Multifunctional additive AMP-95 0.2kg;

[0094] Sodium lauryl sulfate 0.5kg;

[0095] Ethylene glycol 1.5kg;

[0096] Precipitated barium sulfate 5kg;

[0097] Rutile titanium dioxide 1kg;

[0098] Lithium silicate 36kg;

[0099] Acrylic emulsion 15kg;

[0100] Inorganic water repellent 6kg;

[0101] Glass beads 30kg;

[0102] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an external wall thermal insulation coating as well as a preparation method and application thereof, and belongs to the field of external wall coatings. The external wall thermal insulation coating comprises the following components by weight: 15-30 parts of water; 0.2-0.5 parts of hydroxyethyl cellulose; 1-1.5 parts of ethylene glycol; 30-40 parts of inorganic resin; 8-15parts of an acrylic emulsion; 0.3-0.5 parts of lauryl sodium sulfate; 3-6 parts of an inorganic water repellent; 6-15 parts of pigment and filler; 23-38 parts of a thermal insulation filler; and 0.1-0.2 parts of a multifunctional auxiliary agent. The coating disclosed by the invention can be directly applied to a cement mortar wall reinforced by seal primer, and has the advantages of good thermalinsulation property, high fireproof grade, good hydrophobicity and good comprehensive performance.

Description

technical field [0001] This application relates to the technical field of exterior wall thermal insulation coatings, more specifically, it relates to an exterior wall thermal insulation coating, a preparation method and its application. Background technique [0002] In response to the national building energy conservation and environmental protection policy, dry-hanging external wall insulation boards are commonly used in the market. However, with the extension of use time, the insulation boards are prone to cracking, water seepage, falling off and hurting people. Later, the market switched to the combination of external wall thermal insulation mortar and internal thermal insulation desulfurized gypsum to solve the disadvantage that the thermal insulation board is easy to fall off and hurt people. Although this method can simplify the construction, it is necessary to continue to construct anti-crack putty, Sealing primers and exterior wall weather-resistant coatings not only...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D5/18C09D7/61C09D7/63C09D7/43C09D1/04
CPCC08K2003/2241C08K2003/3045C08K2201/003C08L2201/02C08L2201/08C09D1/04C09D5/18C09D133/04C09D7/43C09D7/61C09D7/63C09D7/66C09D7/70C08L1/284C08K13/04C08K3/30C08K3/22C08K3/34C08K7/20C08K7/24C08K5/17
Inventor 孟奎张强国
Owner HUBAO NEW MATERIAL TECH SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com