Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A high-strength heat-resistant oil casing material and its preparation method

A heat-resistant oil and high-strength technology, which is applied in heat treatment equipment, manufacturing tools, heat treatment furnaces, etc., can solve the problems of poor mechanical properties of high temperature resistance and anti-collapse performance, and achieve excellent anti-collapse performance, reduce costs, and improve The effect of the preparation method

Active Publication Date: 2021-12-21
DALIPAL PIPE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of poor high-temperature-resistant mechanical properties and anti-collapse performance existing in heavy oil well production casings, the present invention provides a high-strength heat-resistant oil casing material and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The embodiment of the present invention provides a high-strength heat-resistant oil casing material, the chemical composition of which is:

[0028] C 0.30%, Si 0.15%, Mn 0.9%, Cr 1.1%, V 0.06%, Ti 0.01%, Al 0.008%, and the rest are Fe and unavoidable impurities.

[0029] The preparation steps of the above-mentioned high-strength heat-resistant oil casing material are as follows:

[0030] Using scrap steel as raw material, through 80t electric arc furnace melting, ladle refining and continuous casting process, the continuous casting round billet with the same chemical composition as the above-mentioned high-strength heat-resistant oil casing material is produced; the continuous casting round billet is heated and perforated by the ring furnace Made into capillary, the capillary is rolled to get a barren tube, and the barren tube is reheated in an intermediate frequency induction furnace, and the micro tension is reduced to obtain a rolled steel pipe with a nominal outer d...

Embodiment 2

[0040] The embodiment of the present invention provides a high-strength heat-resistant oil casing material, the chemical composition of which is:

[0041] C 0.25%, Si 0.35%, Mn 1.1%, Cr 1.0%, V 0.08%, Zr 0.01%, Ti 0.02%, Al 0.006%, and the rest are Fe and unavoidable impurities.

[0042] The preparation steps of the above-mentioned high-strength heat-resistant oil casing material are as follows:

[0043] Using scrap steel as raw material, through 80t electric arc furnace melting, ladle refining and continuous casting process, the continuous casting round billet with the same chemical composition as the above-mentioned high-strength heat-resistant oil casing material is produced; the continuous casting round billet is heated and perforated by the ring furnace Made into capillary, the capillary is rolled to get a barren tube, and the barren tube is reheated in an intermediate frequency induction furnace, and the micro tension is reduced to obtain a rolled steel pipe with a nomin...

Embodiment 3

[0053] The embodiment of the present invention provides a high-strength heat-resistant oil casing material, the chemical composition of which is:

[0054] C 0.28%, Si 0.25%, Mn 1.0%, Cr 0.9%, V 0.04%, Zr 0.03%, Ti 0.03%, Al 0.005%, and the rest are Fe and unavoidable impurities.

[0055] The preparation steps of the above-mentioned high-strength heat-resistant oil casing material are as follows:

[0056] Using scrap steel as raw material, through 80t electric arc furnace melting, ladle refining and continuous casting process, the continuous casting round billet with the same chemical composition as the above-mentioned high-strength heat-resistant oil casing material is produced; the continuous casting round billet is heated and perforated by the ring furnace Made into capillary, the capillary is rolled to get a barren tube, and the barren tube is reheated in an intermediate frequency induction furnace, and the micro tension is reduced to obtain a rolled steel pipe with a nomin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength heat-resistant oil casing material and a preparation method thereof. The composition weight percentage of the oil casing material is: 0.25%≤C≤0.30%, 0.15%≤Si≤0.35%, 0.9%≤Mn ≤1.1%, 0.9%≤Cr≤1.1%, 0.04%≤V≤0.08%, 0.01%≤Ti≤0.03%, Al≤0.01%, the balance is Fe and unavoidable impurities; the oil casing provided by the invention 0.01% to 0.03% of Zr element can also be added to the material, which can further improve the heat resistance of the oil casing material. The oil and casing material of the invention has a simple composition system, low manufacturing cost, excellent high-temperature mechanical properties and anti-collapse performance, can be widely used in heavy oil thermal recovery well drilling, and has broad market prospects.

Description

technical field [0001] The invention relates to the technical field of oil casing manufacturing, in particular to a high-strength heat-resistant oil casing material and a preparation method thereof. Background technique [0002] At present, heavy oil resources in the world are relatively abundant, accounting for about 70% of the world's remaining oil resources. my country is a major producer of heavy oil, and its heavy oil resources account for a considerable proportion. The development of heavy oil covers more than ten oil reservoir areas including Liaohe, Shengli, Xinjiang, and Henan. Heavy oil has high viscosity and poor fluidity. How to effectively exploit heavy oil has always been a difficult problem for the petroleum industry. Heavy oil is extremely sensitive to temperature, and the viscosity will drop by half for every 10°C increase. Therefore, the heavy oil steam flooding method (that is, injecting high-pressure and high-temperature steam into the oil well through p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/24C22C38/28C21D1/25C21D6/00C21D8/10C21D9/08C22C33/06
CPCC22C38/02C22C38/04C22C38/24C22C38/28C22C38/06C22C33/06C21D6/005C21D6/008C21D6/002C21D8/105C21D9/085C21D1/25C21D2211/009Y02P10/20
Inventor 邓叙燕
Owner DALIPAL PIPE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com