A kind of surface treatment preparation and surface pretreatment process for galvanized steel sheet

A galvanized steel sheet and surface treatment technology, which is applied in the direction of manufacturing tools, metal processing equipment, grinding workpiece supports, etc., can solve the problems of low grinding efficiency and achieve the effects of low consumption, high surface finish and uniform corrosion rate

Active Publication Date: 2021-05-14
GUANGDONG XINTONGDA STEEL PIPE MILL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, the surface of the galvanized steel sheet needs to be polished before galvanizing, but the existing technology has the problem that the steel sheet cannot move relative to the grinding device, and the grinding efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of surface treatment preparation and surface pretreatment process for galvanized steel sheet
  • A kind of surface treatment preparation and surface pretreatment process for galvanized steel sheet
  • A kind of surface treatment preparation and surface pretreatment process for galvanized steel sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068](1) Treatment of acid wash inproduction by ultrafine pulverizer, then add an appropriate amount of water, placed in a wet ball mill for ball milling, over 100 mesh sieve;

[0069](2) Adding an appropriate amount of water into the mixed stirring vessel, maintaining water volume does not exceed 1 / 3 of the volumetric volume, weighing the feedstock according to the ratio of potassium hydrogen sulfate composite salts, 1% sulfate, aniline quaternary ammonium salt Compound 5%, 2% sodium carbonate, 2% acetate, 2% alcohol ether carboxylate, mixed in a stirred container, regulating the stirring rate of 200 rpm, and stirring until dispersion is uniform;

[0070](3) While stirring, a content of 5% phosphate compound, 1% hydroxy heod diphosphoric acid, 5% imidazoline and a derivative thereof, and 2% alkogene derivatives were added to the mixture. Add an appropriate amount of water, stir well, and prepare a mixture;

[0071](4) Place the mixed liquid in a high-speed shear dispersion machine, adding ...

Embodiment 2

[0073](1) Treatment of acid wash inproduction by ultrafine pulverizer, then add an appropriate amount of water, placed in a wet ball mill for ball milling, over 100 mesh sieve;

[0074](2) Adding an appropriate amount of water into the mixed stirring vessel, maintaining the amount of water not exceeding 1 / 3 of the device volume, weighing the feedstock according to the ratio of potassium hydrogen sulfate composite salt, 3% sulfate, aniline quaternary ammonium salt The compound is 10%, 3% sodium carbonate, 3% acetate, 3% alcohol ether carboxylate, mixed in a stirred container, and adjust the stirring rate of 300 rpm, and keep it until dispersion is uniform;

[0075](3) While stirring, an amount of 8% of a phosphate compound, 2% hydroxybethyl diphosphoric acid, 8% imidazoline and a derivative thereof, 3% alklene derivatives were added to the mixture. Add an appropriate amount of water, stir well, and prepare a mixture;

[0076](4) Place the mixture in a high speed shear dispersion, 0.75%, stabi...

Embodiment 3

[0078](1) Treatment of acid wash inproduction by ultrafine pulverizer, then add an appropriate amount of water, placed in a wet ball mill for ball milling, over 100 mesh sieve;

[0079](2) Adding an appropriate amount of water into the mixed stirring vessel, maintaining the water volume does not exceed 1 / 3 of the device volume, weighing the feedstock according to the ratio: 10%, sulfate, 5% sulfate, aniline quaternary ammonium salt The compound is 15%, 5% sodium carbonate, 5% acetate, 5% alcohol ether carboxylate, and mixed in the stirred container, and the agitation rate is 500 rpm, and stirring is kept until dispersion is uniform;

[0080](3) While stirring, an amount of 10% phosphate compound, 3% hydroxy heod diphosphoric acid, 10% imidazoline and a derivative thereof were added to the mixture, and 5% alkoiol derivatives were added to the mixture. Add an appropriate amount of water, stir well, and prepare a mixture;

[0081](4) Place the mixture in a high-speed shear dispersion machine, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a surface treatment preparation for galvanized steel sheet and a surface pretreatment process, belonging to the technical field of steel sheet surface treatment. First, the surface of the untreated steel sheet is ground and processed, and then further treated with a surface treatment agent. The surface treatment preparation for galvanized steel sheet includes the following raw materials: phosphate ester compound, potassium hydrogen persulfate compound salt, hydrogen sulfate salt, quaternary ammonium aniline compound, sodium carbonate, ammonium acetate, hydroxyethylidene phosphoric acid, imidazoline and its derivatives compounds, acid pickling fog suppressants, alkynyl alcohol derivatives, alcohol ether carboxylates, stabilizers, chelating agents, water. The surface treatment preparation for galvanized steel plate provided by the technical solution of the present invention can effectively remove oil stains, oxide films, rust spots and other adhesive impurities on the surface of the steel plate. Volatile substances, wastewater treatment is simple, safe and environmentally friendly. After the steel sheet is treated as above, it helps to improve the quality and efficiency of the galvanized steel sheet.

Description

Technical field[0001]The present invention relates to a surface treatment technique of a steel sheet, specifically a surface treatment formulation and a surface treatment process for galvanizing steel sheets.Background technique[0002]Typically, the surface residual impurities are residual, or the surface is exposed for a long time, and the surface can form a variety of oxide films, rust, etc., which cannot be directly carried out, and surface treatment is required.[0003]Metal surface acid washing treatment is an indispensable process before galvanizing. It is mainly prepared by hydrochloric acid or sulfuric acid on the market. It has the advantages of rust fast, but it has strong corrosion, it is easy to cause corrosion. The subsequent treatment of the metal surface brings a lot of unnecessary trouble and hazards, such as bad problems such as rough steel sheets. At the same time, the treatment of pickling waste after treatment, due to strong corrosion, will cause irreversible hazard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/06C23G1/08B24B21/04B24B27/033B24B21/18B24B41/06B24B47/20B24B47/16B24B55/08B24B55/12
CPCB24B21/04B24B21/18B24B27/033B24B41/06B24B47/16B24B47/20B24B55/08B24B55/12C23G1/061C23G1/066C23G1/088
Inventor 马汉荣
Owner GUANGDONG XINTONGDA STEEL PIPE MILL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products