A powder coating, ultra-thin technology, applied in the field of coatings, can solve the problems of poor leveling of the coating film, difficulty in applying thin layers of powder coatings, orange peel or pores, etc., and achieve the effect of not easy to fall off and high bonding strength
Inactive Publication Date: 2021-01-26
HUNAN LIANXIN SCI & TECH CO LTD
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, it is difficult to apply thin layers of powder coatings, and solvent-based coatings are easy to form ultra-thin coatings, but it is difficult for powder coatings to achieve such an effect when coating. The average minimum film thickness is 50-70 μm. When the coating film thickness is less than 40 μm, due to The film layer is too thin, the leveling property of the coating film is poor, so the appearance decoration effect is not good, showing serious orange peel or pores
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Embodiment 1: A kind of ultra-thin powder coating, its coating each composition raw material counts by mass parts: matrix resin 25, curing agent 15, curing accelerator 15, filler 20, graphene powder 5, metal composition 10, auxiliary agent 10. Auxiliaries include the following components in parts by mass: leveling agent 1, dispersant 1.0, anti-sedimentation agent 0.1, defoamer 0.5, antifungal agent 0.1, thickener 0.5, composite rare earth 0.01, film-forming aid Agent 5; the raw materials of the leveling agent are calculated in parts by mass: polyaspartic acid / polyethylene glycol monomethyl ether 15-20, modified fly ash 3, polyethylene oxide 2, polydipentaerythritol hexaacrylate 2. Polyvinyl butyral 0.5, pregelatinized starch 0.5, disodium lauryl sulfosuccinate 0.3, ferrocene 0.1.
[0016] The raw materials of the composite rare earth are calculated by mass parts: Y5, Sc10, Gd15, Sm9, Pr11, La 60; the matrix resin is a mixture of brominated epoxy resin emulsion, polyacry...
Embodiment 2
[0017] Embodiment 2: a kind of ultra-thin powder coating, and each composition raw material of its coating is counted by mass parts: matrix resin 30, curing agent 15, curing accelerator 10, filler 30, graphene powder 5, metal composition 20, auxiliary agent 10-25; additives include the following components in parts by mass: leveling agent 1-3, dispersant 1.5, anti-sedimentation agent 0.3, defoamer 0.8, antifungal agent 0.3, thickener: 0.5, compound rare earth 0.03, film-forming aid 8; the composition raw materials of leveling agent are calculated by mass parts: polyaspartic acid / polyethylene glycol monomethyl ether 20, modified fly ash 3, polyethylene oxide 2, polydipentaerythritol Hexaacrylate 1-2, polyvinyl butyral 1, pregelatinized starch 0.5, disodium lauryl sulfosuccinate 0.3, ferrocene 0.05.
[0018] The raw materials of the composite rare earth are calculated by mass parts: Y5, Sc10, Gd15, Sm9, Pr11, La 60; the matrix resin is a mixture of brominated epoxy resin emulsio...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention provides ultrathin powder coating which comprises the following raw materials in parts by mass: 25 to 30 parts of matrix resin, 12 to 15 parts of a curing agent, 10 to 15 parts of a curing accelerator, 20 to 30 parts of a filler, 5 to 10 parts of graphene powder, 10 to 20 parts of a metal composition and 10 to 25 parts of an auxiliary agent. The auxiliary agent comprises the following components in parts by mass: 1 to 3 parts of a leveling agent, 1.0 to 1.5 parts of a dispersing agent, 0.1 to 0.3 part of an anti-settling agent, 0.5 to 0.8 part of an antifoaming agent, 0.1 to 0.3part of a mildew preventive, 0.5 to 0.7 part of a thickener, 0.01 to 0.03 part of composite rare earth and 5 to 8 parts of a coalescing agent; the leveling agent is prepared from the following raw materials in parts by mass: 15 to 20 parts of polyaspartic acid / polyethylene glycol monomethyl ether, 2 to 3 parts of modified fly ash, 1 to 2 parts of polyoxyethylene, 1 to 2 parts of polydipentaerythritol hexaacrylate, 0.5 to 1 part of polyvinyl butyral, 0.5 to 1 part of pregelatinized starch, 0.3 to 0.5 part of disodium lauryl sulfosuccinate and 0.05 to 0.1 part of ferrocene. The coating disclosedby the invention is high in bonding strength with the surface of a base material and is not easy to fall off, and the thickness of a coating film is 30 to 50 micrometers.
Description
technical field [0001] The invention relates to the technical field of coatings, in particular to an ultra-thin powder coating. Background technique [0002] Powder coating is a new type of solvent-free 100% solid powder coating, which has the characteristics of no solvent, no pollution, recyclable, environmental protection, saving energy and resources, reducing labor intensity and high mechanical strength of the coating film. However, it is difficult to apply thin layers of powder coatings, and solvent-based coatings are easy to form ultra-thin coatings, but it is difficult for powder coatings to achieve such an effect when coating. The average minimum film thickness is 50-70 μm. When the coating film thickness is less than 40 μm, due to If the film layer is too thin, the leveling property of the coating film is poor, so the appearance decoration effect is not good, and serious orange peel or pores appear. Contents of the invention [0003] The technical problem to be so...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more