A kind of maltose derived carbon/titanium niobium oxygen composite material and its preparation method and application

A composite material and maltose technology, applied in electrochemical generators, structural parts, electrical components, etc., to achieve the effects of improving electrochemical kinetics, increasing specific surface area, and improving rate performance and cycle performance

Active Publication Date: 2022-04-12
ZHEJIANG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there has been no report on this powerful carbon composite technology, and its application value is particularly worthy of exploration and research

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of maltose derived carbon/titanium niobium oxygen composite material and its preparation method and application
  • A kind of maltose derived carbon/titanium niobium oxygen composite material and its preparation method and application
  • A kind of maltose derived carbon/titanium niobium oxygen composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Wash the purchased glutinous rice and pour it into a pot to simmer and stir it with the chopped malt, let it ferment for 4-6 hours until the juice is transformed. Then the juice is filtered out and boiled at high temperature to form a paste, and after cooling, it becomes an amber-like candy. The titanium niobium oxide powder was poured into maltose and stirred ultrasonically for 30 minutes, the mass ratio of titanium niobium oxide powder and maltose was 1:4, and then freeze-dried with a freeze dryer for 24 hours. The precursor obtained by freeze-drying was preheated at 600°C in argon for 4h, then transferred to a tube furnace for sintering at 800°C for 3h, and the heating rate was 5°C / min. After cooling, maltose-derived carbon / titanium niobium was obtained Oxygen composites.

Embodiment 2

[0031] Wash the purchased glutinous rice and pour it into a pot to simmer and stir it with the chopped malt, let it ferment for 4-6 hours until the juice is transformed. Then the juice is filtered out and boiled at high temperature to form a paste, and after cooling, it becomes an amber-like candy. The titanium niobium oxide powder was poured into maltose and stirred ultrasonically for 30 minutes, the mass ratio of titanium niobium oxide powder and maltose was 1:4, and then freeze-dried with a freeze dryer for 24 hours. The precursor obtained by freeze-drying was preheated at 600°C in argon for 4h, then transferred to a tube furnace for sintering at 800°C for 5h, and the heating rate was 5°C / min. After cooling, maltose-derived carbon / titanium niobium was obtained Oxygen composites.

Embodiment 3

[0033] Wash the purchased glutinous rice and pour it into a pot to simmer and stir it with the chopped malt, let it ferment for 4-6 hours until the juice is transformed. Then the juice is filtered out and boiled at high temperature to form a paste, and after cooling, it becomes an amber-like candy. The titanium niobium oxide powder was poured into maltose and stirred ultrasonically for 30 minutes, the mass ratio of titanium niobium oxide powder and maltose was 1:4, and then freeze-dried with a freeze dryer for 24 hours. The precursor obtained by freeze-drying was preheated in argon at 600°C for 4h, then transferred to a tube furnace for sintering at 800°C for 4h, and the heating rate was 5°C / min. After cooling, maltose-derived carbon / titanium niobium was obtained Oxygen composites.

[0034] figure 1 , 2 It is a scanning electron micrograph of the maltose-derived carbon / titanium-niobium-oxygen composite material prepared in Example 3. image 3 It is a transmission electron ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite material based on maltose-derived carbon and its preparation method and application, including: obtaining maltose; pouring titanium niobium oxide powder into maltose for ultrasonic stirring, and then freeze-drying with a freeze dryer; Transfer to a tube furnace in argon, preheat at 500-650°C for 3-6 hours in argon, and then sinter at 700-850°C for 3-6 hours. After cooling, the maltose-derived carbon / titanium-niobium-oxygen composite material is obtained. The present invention synthesizes a large number of composite materials based on maltose-derived carbon through high-temperature carbonization. The composite material electrode of the present invention has a three-dimensional porous structure, has the characteristics of high specific surface area, high cycle stability, rate performance and coulombic efficiency, and is especially suitable as a battery electrode material, which helps to promote high energy density, high power The development of commercial batteries with high density and high stability.

Description

technical field [0001] The invention relates to the technical field of positive and negative electrode materials for batteries, in particular to a maltose-derived carbon / titanium-niobium-oxygen composite material and a preparation method and application thereof. Background technique [0002] Carbon technology has a profound impact on social development and the progress of human civilization. With the technical progress of carbon materials (such as charcoal, coal, graphite), a series of reforms and leaps have taken place in the social energy system. Currently, the scientific community is still eager to explore advanced carbon-based materials for higher green energy efficiency and utilization. So far, various carbonized materials (e.g., graphene, carbon nanotubes, footballene, carbon quantum dots, and carbon micro / nanofibers) and their composites have been mainly produced by chemical vapor deposition, chemical or electrochemical exfoliation, electrospinning, etc. However, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/48H01M4/583H01M10/0525
CPCH01M4/366H01M4/483H01M4/583H01M10/0525H01M2004/021Y02E60/10
Inventor 夏新辉沈盛慧王秀丽涂江平
Owner ZHEJIANG UNIV