Inorganic water-based paint and preparation method thereof

A water-based paint and inorganic technology, applied in the field of inorganic water-based paint and its preparation, can solve the problems of poor durability and low air pollution purification ability, and achieve the effects of good purification durability, excellent storage stability and high purification efficiency.

Inactive Publication Date: 2021-04-09
四川万祺科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the defects of low air pollution purification ability and poor durability brought by the existing interior wall coatings for interior decoration, and provide people with a high purification efficiency, good purification persistence, non-toxic, and non-polluting. Inorganic water-based paint and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The inorganic water-based paint composition of this example is as follows in mass percent:

[0022] Potassium silicate 20%, modified bentonite formaldehyde adsorbent 3%, tetrapod zinc oxide whisker 3%, modified sepiolite 3%, titanium dioxide 20%, heavy calcium powder 27%, cellulose 1%, net Flavor emulsion 2%, 2-imidazolidinone 0.4%, hydrophobic enhancer 0.6%, water 20%.

[0023] The preparation method of the inorganic water-based paint of this example is as follows:

[0024] Potassium silicate, modified bentonite formaldehyde adsorbent, four needle-shaped zinc oxide whiskers, modified sepiolite, and water are stirred and mixed to obtain a mixed solution; titanium dioxide, heavy calcium powder, and cellulose are added to the mixed solution while stirring, A mixture is obtained; the odor-cleaning emulsion, 2-imidazolidinone, and a hydrophobic enhancer are added to the mixture under stirring, and the inorganic water-based paint is obtained after stirring for 1 hour.

[0...

Embodiment 2

[0033] The inorganic water-based paint composition of this example is as follows in mass percent:

[0034] Potassium silicate 24%, modified bentonite formaldehyde adsorbent 3%, tetrapod zinc oxide whisker 2%, modified sepiolite 3%, montmorillonite loaded acrylic acid 2%, titanium dioxide 16%, heavy calcium powder 20 %, bentonite inorganic gel 3%, glass powder 7%, water 20%.

[0035] The preparation method of the inorganic water-based paint of this example is as follows:

[0036] Potassium silicate, modified bentonite formaldehyde adsorbent, four needle-shaped zinc oxide whiskers, modified sepiolite, montmorillonite-loaded acrylic acid, and water were stirred and mixed to obtain a mixed solution; Calcium powder and bentonite inorganic gel are used to obtain a mixture; glass powder is added to the mixture under stirring, and then stirred for 1 hour to obtain an inorganic water-based paint.

[0037] In this example, the montmorillonite-supported acrylic acid is obtained by firs...

Embodiment 3

[0045] The inorganic water-based paint composition of this example is as follows in mass percent:

[0046] Potassium silicate 22%, modified bentonite formaldehyde adsorbent 1%, tetrapod zinc oxide whisker 3%, modified sepiolite 3%, titanium dioxide 18%, heavy calcium powder 23%, water 30%.

[0047] The preparation method of the inorganic water-based paint of this example is as follows:

[0048] Stir and mix potassium silicate, modified bentonite formaldehyde adsorbent, tetraacicular zinc oxide whiskers, modified sepiolite, and water to obtain a mixed liquid; add titanium dioxide and heavy calcium powder to the mixed liquid while stirring, and stir for 1 hour That is, the inorganic water-based paint is obtained.

[0049] All the other are the same as embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to inorganic water-based paint and a preparation method thereof in the field of environmental protection. The inorganic water-based paint comprises, by mass, 20-24% of potassium silicate, 1-3% of a modified bentonite formaldehyde adsorbent, 2-3% of tetrapod-like zinc oxide whiskers, 1-3% of modified sepiolite, 16-20% of titanium dioxide, 20-27% of heavy calcium powder, 0-2% of montmorillonite-loaded acrylic acid, 0-3% of bentonite inorganic gel, 0-7% of glass powder, 0-1% of cellulose, 0 to 2% of odorless emulsion, 0 to 0.4% of 2-imidazolidinone, 0 to 0.6% of a hydrophobic reinforcing agent and 20 to 30% of water. and potassium silicate is adopted as a main film forming substance, tetrapod-like zinc oxide whiskers, a modified bentonite formaldehyde adsorbent, modified sepiolite and the like are compounded, and the prepared inorganic water-based paint is high in purification efficiency, good in purification durability and free of toxicity and pollution.

Description

technical field [0001] The invention belongs to the field of environmental protection, and in particular relates to an inorganic water-based paint and a preparation method thereof. Background technique [0002] According to the data of the National Bureau of Professional Statistics, 80% of the air pollution caused by indoor decoration in the country comes from excessive formaldehyde. For this reason, people have done a lot of research on air purification and developed various materials with the function of purifying air, such as CN100467554 and CN102964932B , these two inventions are mainly based on the addition of four-needle zinc oxide whiskers, adsorption materials, acrylate emulsions, etc. to the latex paint. The film-forming substance is acrylate emulsion, which is not only toxic and carcinogenic, but also has poor air permeability. , resulting in the addition of four needle-shaped zinc oxide whiskers and adsorption materials can not fully play its role in purification....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B14/04C04B14/38C04B24/42C04B103/44C04B20/04C04B20/02C04B20/00
CPCC04B28/26C04B24/425C04B14/042C04B14/383C04B14/041C04B2111/00482C04B2111/00025C04B2111/00017C04B2111/28C04B2111/27C04B2111/2092C04B2103/44C04B14/104C04B14/305C04B14/28C04B24/383C04B24/128C04B2103/65C04B14/22C04B20/004C04B20/04C04B20/023
Inventor 戴祺又吴怡
Owner 四川万祺科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com