A kind of electrochromic paint and preparation method thereof, electrochromic film and preparation method thereof

An electrochromic film and electrochromic technology, applied in multi-color effect paints, coatings, instruments, etc., can solve the problems of low service life, poor resin aging resistance, and low operating temperature of electrochromic films. Achieve the effect of low saturation driving voltage and threshold voltage, better saturation driving voltage and peel strength, and excellent overall performance

Active Publication Date: 2022-04-05
ECO BAO
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, this type of electrochromic film can only be used indoors due to its low operating temperature, poor aging resistance of the resin, and low service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of electrochromic paint and preparation method thereof, electrochromic film and preparation method thereof
  • A kind of electrochromic paint and preparation method thereof, electrochromic film and preparation method thereof
  • A kind of electrochromic paint and preparation method thereof, electrochromic film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0063] The preparation steps of electrochromic paint are:

[0064] S1. First mix isobornyl methacrylate and 3,5,5-trimethylhexyl acrylate and heat to 50°C, then stir at 300rpm for 5min, so that isobornyl methacrylate and 3,5 , 5-trimethylhexyl acrylate is polymerized to obtain a liquid prepolymer in a transparent viscous state;

[0065] S2. Add benzoin bisformaldehyde to the prepolymer, and stir for 10 minutes at a speed of 200 rpm, so that the benzoin bisformaldehyde is fully dissolved;

[0066] S3. After adding β-carboxyethyl acrylate and UV curable resin 07B to the liquid obtained in S2, stir at 200 rpm for 10 minutes to form a resin;

[0067] S4. Add mixed liquid crystals to the resin, and then stir for 30 minutes at a speed of 200 rpm;

[0068] S5, then adding a 15 μm spacer, and stirring at a speed of 200 rpm for 20 min to obtain a coating mixture;

[0069] S6. Use ultrasonic waves to disperse the coating mixture of S5 for 30 minutes, so as to further fully mix all th...

Embodiment 22-28

[0109] The difference between Examples 22-28 of the electrochromic film and Example 1 of the electrochromic film is that the process parameters for preparing the electrochromic film in this electrochromic film comparative example are different, and the others are the same as in Example 1 of the electrochromic film. See Table 6.

[0110] Preparation process in Table 6 electrochromic film embodiment 22-28

[0111]

[0112] Comparative example of electrochromic film

[0113] Electrochromic film comparative example 1-12

[0114] The difference between the electrochromic film comparative examples 1-12 and the electrochromic film embodiment 1 is that the electrochromic coating selected in the electrochromic film comparative example is different, and the others are the same as the electrochromic film embodiment 1, see Table 7 for details .

[0115] Table 7 Preparation of Electrochromic Film Comparative Examples 1-12 Selection of Electrochromic Coatings

[0116]

[0117] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The application relates to the technical field of electrochromic films, and specifically discloses an electrochromic coating and a preparation method thereof, an electrochromic film and a preparation method thereof. Electrochromic coatings include the following components: 3,5,5‑trimethylhexylacrylate prepolymer, β‑carboxyethyl acrylate, photoinitiator, UV curable resin, mixed liquid crystal, spacer; electrochromic The preparation method of coating comprises the following steps: S1, preparing 3,5,5-trimethylhexyl acrylate prepolymer, S2, subsequently adding photoinitiator, β-carboxyethyl acrylate and UV curing resin, mixing liquid crystal , after the spacer and stir, S3, mix evenly; the electrochromic film is prepared from the above electrochromic coating. The electrochromic film prepared by the present application has better haze and transmittance in a wide working range, and its working voltage is low.

Description

technical field [0001] The present application relates to the technical field of electrochromic film, more specifically, it relates to an electrochromic coating and a preparation method thereof, an electrochromic film and a preparation method thereof. Background technique [0002] Electrochromism refers to the phenomenon of stable and reversible color transformation of the reflectance and transmittance of materials under the action of an external electric field. The electrochromic film (or dimming film) mainly controls the movement of liquid crystal molecules through the change of the external electric field, so as to realize the transformation of the film material from a colorless transparent state to an atomized opaque state. Because of its good optical properties, it can be used in conference offices, banks, commercial windows, and car windows. [0003] An important performance of the electrochromic film is to require low haze and high transmittance in the open state. A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/29C09D7/63C09D7/65G02F1/1516
CPCC09D4/06C09D5/29C09D7/63C09D7/65G02F1/15165
Inventor 咸才军王建平
Owner ECO BAO
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com