Preparation method of smart hydrogel wound dressing doped with abalone shell powder/zno composite material with antibacterial effect

A composite material and antibacterial technology, applied in the field of smart hydrogel wound dressing and its preparation, can solve problems such as side effects, and achieve the effects of good biocompatibility, promotion of wound repair, and simple preparation process

Active Publication Date: 2022-05-13
SHANDONG UNIV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the use of systemic antibiotics may cause side effects such as nephropathy, neuropathy, and gastrointestinal disorders

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of smart hydrogel wound dressing doped with abalone shell powder/zno composite material with antibacterial effect
  • Preparation method of smart hydrogel wound dressing doped with abalone shell powder/zno composite material with antibacterial effect
  • Preparation method of smart hydrogel wound dressing doped with abalone shell powder/zno composite material with antibacterial effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A preparation method of an intelligent hydrogel wound dressing doped with antibacterial abalone shell powder / ZnO composite material, comprising the following steps:

[0054] (1) Wash the abalone shell with tap water and soak it in 8% sodium hydroxide solution for 1 hour, then wash it with distilled water;

[0055] (2) Dry the abalone shell obtained in step (1) in a blast drying oven at 100°C for 24 hours;

[0056] (3) Put the abalone shell obtained in step (2) into a multi-functional pulverizer, and pass through a 100-mesh sieve;

[0057] (4) Grinding the abalone shell powder obtained in step (3) with a planetary ball mill for 48 hours, then placing it in a muffle furnace at 1100°C for calcination for 2 hours, and grinding in a mortar to obtain the abalone shell powder carrier;

[0058] (5) Weigh 29.7g of zinc nitrate hexahydrate into a three-neck flask, add 100ml of distilled water to dissolve under the condition of constant temperature stirring at 90°C;

[0059] (6)...

Embodiment 2

[0068] A preparation method of an intelligent hydrogel wound dressing doped with antibacterial abalone shell powder / ZnO composite material, comprising the following steps:

[0069] (1) Wash the abalone shell with tap water and soak it in 8% sodium hydroxide solution for 1 h, then wash it with distilled water;

[0070] (2) Dry the abalone shells obtained in step (1) in a blast drying oven at 100 °C for 24 h;

[0071] (3) Put the abalone shell obtained in step (2) into a multi-functional pulverizer, and pass through a 100-mesh sieve;

[0072] (4) The abalone shell powder obtained in step (3) was ball-milled with a planetary ball mill for 48 h, then placed in a muffle furnace at 1100 °C for 2 h, and ground in a mortar to obtain the abalone shell powder carrier;

[0073] (5) Weigh 29.7 g of zinc nitrate hexahydrate into a three-necked flask, and add 100 ml of distilled water to dissolve under constant temperature stirring at 90 °C;

[0074] (6) Weigh 4.0 g of sodium hydroxide an...

Embodiment 3

[0083] A preparation method of an intelligent hydrogel wound dressing doped with antibacterial abalone shell powder / ZnO composite material, comprising the following steps:

[0084] (1) Wash the abalone shell with tap water and soak it in 8% sodium hydroxide solution for 1 hour, then wash it with distilled water;

[0085] (2) Dry the abalone shell obtained in step (1) in a blast drying oven at 100°C for 24 hours;

[0086] (3) Put the abalone shell obtained in step (2) into a multi-functional pulverizer, and pass through a 100-mesh sieve;

[0087] (4) Grinding the abalone shell powder obtained in step (3) with a planetary ball mill for 48 hours, then placing it in a muffle furnace at 1100°C for calcination for 2 hours, and grinding in a mortar to obtain the abalone shell powder carrier;

[0088] (5) Weigh 29.7g of zinc nitrate hexahydrate into a three-neck flask, add 100ml of distilled water to dissolve under the condition of constant temperature stirring at 90°C;

[0089] (6)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of medical materials, and relates to a preparation method of an intelligent hydrogel wound dressing doped with abalone shell powder / ZnO composite material with antibacterial effect. According to the interface and phase interaction of the material, using the technology and method of material preparation, abalone shell powder / ZnO composite material, chitosan powder and sodium alginate solution were used to form a uniform slurry, and gluconolactone was selected as the proton donor. A purely physically cross-linked chitosan / sodium alginate double network smart hydrogel dressing doped with abalone shell powder / ZnO composite material with antibacterial effect was prepared. The selected material has good biocompatibility and no cytotoxicity, and the dressing can inhibit bacterial infection and promote wound healing.

Description

technical field [0001] The invention belongs to the technical field of medical materials, and in particular relates to an intelligent hydrogel wound dressing doped with abalone shell powder / ZnO composite material and a preparation method thereof. Background technique [0002] Skin wound infections in trauma and surgical wounds caused by various microorganisms are very common. According to relevant data, up to 10% of hospitalized patients worldwide are affected by skin and soft tissue infections. Up to 5% of hospitalized surgical patients develop surgical site infections. Wound infections lead to inflammation, tissue damage, and delayed healing, leading to prolonged hospital stays that impact healthcare costs. In the worst cases, the infection becomes aggressive and can progress to septic shock and death. [0003] Clinically, systemic (oral, intravenous) antibiotics and topical antimicrobials are currently used to treat wound infections. Systemic antibiotics have limited ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L26/00C08J3/075C08L5/08C08L5/04
CPCA61L26/008A61L26/0095A61L26/0057A61L26/0066C08J3/075C08J2305/08C08J2305/04A61L2300/30C08L5/08C08L5/04