Regenerated building material

A technology of recycled building materials and cement, which is applied in the field of recycled building materials, can solve problems such as pollution, large consumption of land expropriation fees, construction funds for garbage removal and transportation, dust and sand flying environment, etc., to reduce pollution, eliminate hidden dangers in use, Simple effect of regeneration process

Inactive Publication Date: 2021-06-04
菏泽永民新型建筑材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the vast majority of construction waste is transported to the suburbs or villages by the construction unit without any treatment, and is stacked in the open air or landfilled, which consumes a lot of construction expenses such as land acquisition fees, garbage removal and transportation fees, and at the same time, during the process of clearing, transporting and stacking Problems such as the scattering of dust and flying dust and sand have caused serious environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A regenerative building material in this embodiment, wherein, by weight percentage, it includes the following components: 30 parts of cement, 62 parts of regenerative orthopedics, 0.9 parts of flame retardant, 2 parts of thickener, 4 parts of compatibilizer, 3 parts of glass fiber, 1.6 parts of alkylphenol polyoxyethylene ether surface treatment agent;

[0026] Wherein, the cement is Portland cement.

[0027] Specifically, the flame retardant is aluminum hydroxide, magnesium hydroxide or antimony trioxide.

[0028] Specifically, the thickener is cellulose ether.

[0029] The preparation method of recycled building materials is as follows:

[0030] Step 1, manually removing metal, wood and plastic materials in the recycled aggregate;

[0031] Step 2, the recycled aggregate is pulverized by a pulverizer, and the pulverized particle size is 6-8mm, and the available concrete particles are screened out through a drum sieve;

[0032] Step 3, mixing and stirring: the regen...

Embodiment 2

[0036] A regenerative building material in this embodiment, wherein, by weight percentage, it includes the following components: 20 parts of cement, 50 parts of regenerative orthopedics, 0.6 parts of flame retardant, 1 part of thickener, and 2 parts of compatibilizer , 1.5 parts of glass fiber, 1.2 parts of alkylphenol polyoxyethylene ether surface treatment agent;

[0037] Wherein, the cement is Portland cement.

[0038] Specifically, the flame retardant is aluminum hydroxide, magnesium hydroxide or antimony trioxide.

[0039] Specifically, the thickener is cellulose ether.

[0040] The preparation method of recycled building materials is as follows:

[0041] Step 1, manually removing metal, wood and plastic materials in the recycled aggregate;

[0042] Step 2, the recycled aggregate is pulverized by a pulverizer, and the pulverized particle size is 6-8mm, and the available concrete particles are screened out through a drum sieve;

[0043] Step 3, mixing and stirring: the...

Embodiment 3

[0047] A regenerative building material in this embodiment, wherein, by weight percentage, it includes the following components: 35 parts of cement, 75 parts of regenerative orthopedics, 1.2 parts of flame retardant, 3 parts of thickener, 6 parts of compatibilizer, 4.5 parts of glass fiber, 2 parts of alkylphenol polyoxyethylene ether surface treatment agent;

[0048] Wherein, the cement is Portland cement.

[0049] Specifically, the flame retardant is aluminum hydroxide, magnesium hydroxide or antimony trioxide.

[0050] Specifically, the thickener is cellulose ether.

[0051] The preparation method of recycled building materials is as follows:

[0052] Step 1, manually removing metal, wood and plastic materials in the recycled aggregate;

[0053] Step 2, the recycled aggregate is pulverized by a pulverizer, and the pulverized particle size is 6-8mm, and the available concrete particles are screened out through a drum sieve;

[0054]Step 3, mixing and stirring: the regene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a regenerated building material, which is prepared from the following ingredients in parts by weight: 20 to 35 parts of cement, 50 to 75 parts of recycled aggregate, 0.6 to 1.2 parts of flame retardant, 1 to 3 parts of thickening agent, 2 to 6 parts of compatilizer, 1.5 to 4.5 parts of glass fiber and 1.2 to 2 parts of alkylphenol polyoxyethylene ether surface treating agent. According to the invention, construction waste is used as recycled aggregate, waste materials are introduced into an ecological circulation system, sustainable development is realized, the pollution to the environment is reduced, and the cost of raw materials is also reduced; the flame retardant is added in the production of the regenerated building material, so that the fireproof performance of the building material is improved, and the performance of the building material is improved; and the cement and the thickening agent are added, so that the characteristics of excellent strength, hardness, wear resistance, impact resistance, flexibility, freezing resistance, water resistance and the like of the original material are maintained, the workability, construction performance, bonding strength, thermal deformation performance and impermeability of the material are enhanced, and the potential safety hazard of the product in use is eliminated.

Description

technical field [0001] The invention relates to the technical field of recycled building materials, in particular to a recycled building material. Background technique [0002] Construction waste refers to the general designation of muck, waste concrete, waste masonry and other waste generated in the production activities of people engaged in demolition, construction, decoration, repair and other construction industries. Classified by source, construction waste can be divided into engineering dregs, decoration waste, demolition waste, engineering mud, etc.; classified by composition, construction waste can be divided into muck, concrete blocks, crushed stones, brick fragments, Waste mortar, mud, asphalt block, waste plastic, waste metal, waste bamboo and wood, etc. [0003] Construction waste refers to the construction waste produced by man-made or natural reasons in the project, including waste slag, spoil, residual mud and waste materials, etc. These materials are of no ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B18/167C04B22/066C04B22/06C04B24/383C04B24/32C04B14/42C04B2103/0068
Inventor 王换新叶秋合
Owner 菏泽永民新型建筑材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com