Surface treatment process of a titanium alloy dental implant

A dental implant and surface treatment technology, which is applied in the fields of dental implant, dentistry, dental restoration, etc., can solve the problems of declining research trend, implant inflammatory response, complex surface treatment process, etc., to improve surface energy and wettability , Accelerate the initial osseointegration speed, good biological safety effect

Active Publication Date: 2021-11-12
JIANGSU TRAUSIM MEDICAL INSTR
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Judging from the current situation, the research trend of the surface addition method has declined due to poor long-term stability, late coating dissolution and coating peeling.
The surface oxidation method is difficult to control the surface film layer, and requires multiple steps to obtain the required film layer. There are many process parameters to be controlled, the process is extremely complicated, and the long-term stability needs to be investigated.
[0011] Moreover, the surface treatment process of the dental implant disclosed in the prior art is complicated, and after sandblasting, simple acid etching cannot completely remove the sandblasting residual particles, which is not conducive to bone formation and osseointegration during subsequent implant implantation , also prone to inflammatory reactions around the implant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface treatment process of a titanium alloy dental implant
  • Surface treatment process of a titanium alloy dental implant
  • Surface treatment process of a titanium alloy dental implant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A surface treatment process for a titanium alloy dental implant, specifically comprising the following steps:

[0047] (1) Prepare dental implants;

[0048] (2) Pre-cleaning: Take the dental implant, wash it with Micro90 cleaning agent for 25 minutes, rinse it with tap water for 2 minutes, clean it with purified water for 20 minutes, and dry it for later use;

[0049] (3) Sandblasting treatment: take the cleaned dental implant, and perform sandblasting treatment on the surface. During the treatment, white corundum is used as the spray material, the compressed air pressure is 3bar, the spraying distance is 150mm, and the sandblasting time is 10s; The mesh number is 30 mesh;

[0050] (4) Acid etching treatment: Take the dental implant after sandblasting treatment, place it in the acid etching solution, and perform acid etching treatment at 80°C for 10 minutes. Rinse with water for 3 minutes, ultrasonically clean with purified water for 30 minutes, and dry for 45 minutes...

Embodiment 2

[0053] A surface treatment process for a titanium alloy dental implant, specifically comprising the following steps:

[0054] (1) Prepare dental implants;

[0055] (2) Pre-cleaning: Take the dental implant, wash it with Micro90 cleaning agent for 20 minutes, rinse it with tap water for 5 minutes, clean it with purified water for 10 minutes, and dry it for later use;

[0056] (3) Sandblasting treatment: take the cleaned dental implant, and perform sandblasting treatment on the surface, using white corundum as the spraying material, the compressed air pressure is 4bar, the spraying distance is 100mm, and the sandblasting time is 20s; The mesh number is 50 mesh;

[0057] (4) Acid etching treatment: Take the dental implant after sandblasting treatment, put it in the acid etching solution, and perform acid etching treatment at 50°C for 50 minutes, then spray it with purified water for 1 minute, ultrasonically clean it with Micro90 cleaning agent for 20 minutes, and rinse it with p...

Embodiment 3

[0060] A surface treatment process for a titanium alloy dental implant, specifically comprising the following steps:

[0061] (1) Prepare dental implants;

[0062] (2) Pre-cleaning: Take the dental implant, wash it with Micro90 cleaning agent for 50 minutes, rinse it with tap water for 1 minute, and ultrasonically clean it with purified water for 40 minutes, and dry it for later use;

[0063] (3) Sandblasting treatment: take the cleaned dental implant, and perform sandblasting treatment on the surface. During the treatment, white corundum is used as the spray material, the compressed air pressure is 6bar, the spraying distance is 50mm, and the sandblasting time is 30s; the white corundum The mesh number is 100 mesh;

[0064] (4) Acid etching treatment: Take the dental implant after sandblasting treatment, place it in the acid etching solution, and perform acid etching treatment at 60°C for 30 minutes. Rinse with water for 5 minutes, ultrasonically clean with purified water f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a surface treatment process of a titanium alloy dental implant. After the pure titanium implant is widely used in clinic, the titanium alloy oral implant is gradually developed. Compared with pure titanium, the addition of alloying elements can improve the mechanical properties of the material, increase the strength, corrosion resistance, processability, and reduce the elastic modulus, especially for narrow-diameter implants, and reduce the risk of fracture. The present invention uses TC4 rods as raw materials for processing, adopts machining manufacturing process, and subsequently performs surface treatment. The processed oral implant has good biological safety, osseointegration, and mechanical properties. The surface of the implant can not only improve the quality of the implant The mechanical chimerism with the surrounding bone tissue promotes the adsorption of bioactive molecules and cells, which is beneficial to the adhesion and proliferation of cells, and at the same time improves the surface energy and wettability of the implant, accelerates the initial osseointegration speed of the implant, and achieves rapid osteosynthesis. Integration; simple process, suitable for commercial production.

Description

technical field [0001] The invention relates to the technical field of implants, in particular to a surface treatment process for titanium alloy dental implants. Background technique [0002] Titanium alloy materials are more and more widely used in the field of organ defect repair due to their excellent biocompatibility and excellent mechanical properties. Titanium-based biomaterials, mainly pure titanium or titanium alloys, have become the preferred materials for oral implants. However, from the perspective of clinical needs, there are still problems such as the need to improve the biological activity of the material, and improve the efficiency and effect of the combination of the material and bone tissue. Factors affecting osseointegration mainly include implant material, shape, surface morphology, chemical properties, loading conditions, shell operation, and individual differences in patients. In order to improve the initiative of implant osseointegration and promote go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61C8/00
CPCA61C8/0013
Inventor 曹云鹏钱晓锦徐骏伟尹克云
Owner JIANGSU TRAUSIM MEDICAL INSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com