Single-component scale type epoxy zinc-rich anti-corrosive primer and preparation method thereof

An epoxy zinc-rich, anti-rust primer technology, applied in the direction of epoxy resin coatings, chemical instruments and methods, anti-corrosion coatings, etc., can solve the problems of poor flexibility of the paint film, difficult operation, slow drying, etc.

Active Publication Date: 2021-06-08
西北永新涂料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a one-component scale-type epoxy zinc-rich antirust primer to solve the existing problems of poor paint film flexibility, difficult operation, serious zinc powder precipitation, and poor salt spray resistance in existing anticorrosion coatings. , slow drying, poor adhesion, and serious environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component scale type epoxy zinc-rich anti-corrosive primer and preparation method thereof
  • Single-component scale type epoxy zinc-rich anti-corrosive primer and preparation method thereof
  • Single-component scale type epoxy zinc-rich anti-corrosive primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, a kind of one-component flake type epoxy zinc-rich antirust primer is composed as follows:

[0030]Prepare raw materials according to the following parts by mass: 20 parts of linseed oil modified epoxy resin, 0.5 part of dispersant AT204, 1 part of bentonite SD-2, 0.5 part of fumed silica R972, 70 parts of flaky zinc powder, 20 parts of glass flakes , 5 parts of nano-nickel-titanium alloy, 3 parts of superfine ferrophosphorus powder, 0.2 part of cobalt isooctanoate as drier, 1 part of adhesion promoter KH560, 5 parts of xylene, 2 parts of butyl acetate;

[0031] Preparation:

[0032] A. At 300 rev / min, in a clean stirred tank, linseed oil modified epoxy resin, dispersant AT204, bentonite SD-2, fumed silica R972, flaky zinc powder, glass flakes, nano-nickel-titanium alloy , Superfine ferrophosphorus powder, stir evenly;

[0033] B. Increase the speed to 1200 rpm, disperse at high speed for 40 minutes, pay attention to the temperature of the slurry during ...

Embodiment 2

[0036] Embodiment 2, the composition of a kind of one-component flake type epoxy zinc-rich antirust primer is as follows: Prepare raw materials according to the following mass parts: 25 parts of linseed oil modified epoxy resin, 0.2 part of dispersant AT204, bentonite SD-2 0.5 parts, fumed silica R9720.8 parts, 65 parts of flaky zinc powder, 25 parts of glass flakes, 6 parts of nano-nickel-titanium alloy, 5 parts of superfine iron phosphorus powder, 0.3 parts of cobalt isooctanoate as drier, adhesion Accelerator KH560 0.8 parts, xylene 4 parts, butyl acetate 1.5 parts;

[0037] Preparation:

[0038] A. Under the rotation speed of 500 rpm, in a clean stirring tank, linseed oil modified epoxy resin, dispersant AT204, bentonite SD-2, fumed silica R972 parts, flaky zinc powder, glass flakes, nano-nickel titanium Alloy, superfine ferrophosphorus powder, stir evenly;

[0039] B. Increase the speed to 1100 rpm, disperse at high speed for 50 minutes, pay attention to the temperature...

Embodiment 3

[0042] Embodiment 3, the composition of a kind of one-component flake type epoxy zinc-rich antirust primer is as follows: Prepare raw materials according to the following mass parts: 30 parts of linseed oil modified epoxy resin, 0.2 part of dispersant AT204, bentonite SD-2 0.5 parts, fumed silica R9720.8 parts, 60 parts of flaky zinc powder, 30 parts of glass flakes, 8 parts of nano-nickel-titanium alloy, 5 parts of superfine iron phosphorus powder, 0.3 parts of cobalt isooctanoate as drier, adhesion Accelerator KH560 0.6 parts, xylene 2 parts, butyl acetate 1 part;

[0043] Preparation:

[0044] A. Under the rotation speed of 500 rpm, in a clean stirring tank, linseed oil modified epoxy resin, dispersant AT204, bentonite SD-2, fumed silica R972 parts, flaky zinc powder, glass flakes, nano-nickel titanium Alloy, superfine ferrophosphorus powder, stir evenly;

[0045] B. Increase the speed to 1100 rpm, disperse at high speed for 50 minutes, pay attention to the temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a single-component scale type epoxy zinc-rich anti-corrosive primer and a preparation method thereof, belongs to the field of industrial anti-corrosive coatings, and solves the problems of poor paint film flexibility, serious zinc powder precipitation and poor salt spray resistance of existing anti-corrosive coatings. The anti-corrosive primer comprises linseed oil modified epoxy resin, a dispersing agent, bentonite, fumed silica, flaky zinc powder, glass flakes, nano nickel-titanium alloy, superfine ferrophosphorus powder, a drier cobalt iso-octoate, an adhesion promoter, xylene and butyl acetate. The preparation method comprises the following steps: sequentially adding the linseed oil modified epoxy resin, the dispersing agent, the bentonite, the fumed silica, the flaky zinc powder, the glass flake, the nano nickel-titanium alloy and the superfine ferrophosphorus powder, and performing uniform stirring; increasing the rotating speed for high-speed dispersion; adding the drier cobalt iso-octoate, the adhesion promoter, the xylene and the butyl acetate while stirring; and performing filtering and packaging. The anti-corrosive primer is excellent in performance and convenient to prepare.

Description

technical field [0001] The invention belongs to the field of industrial anticorrosion coatings, and in particular relates to a single-component scale-type epoxy zinc-rich antirust primer and a preparation method thereof. Background technique [0002] The anticorrosion of coatings often requires primer, intermediate paint, topcoat or a paint system that cooperates with each other between primer and topcoat. The role of primer in the entire paint system is particularly important. The commonly used primers are: : Two-component epoxy zinc-rich primer, one-component epoxy antirust primer and hot-dip galvanized coating. The most widely used is epoxy zinc-rich primer. It not only has excellent anti-corrosion performance, but also has excellent adhesion, heat resistance and does not affect welding. It is a steel structure bridge, ship, dock, factory building, pipeline, etc. The main supporting primer in heavy anti-corrosion coatings such as steel towers and iron towers. Commonly u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D5/10C09D7/61C09D7/63C09D7/45C09D7/80C09F9/00
CPCC09D163/10C09D5/106C09D5/08C09D7/61C09D7/63C09D7/45C09D7/80C09F9/00C08K2003/0893C08K7/00C08K3/08C08K5/098C08K3/346C08K5/05C08K13/04
Inventor 王雷李华明雍涛苏岳雄王瑞靳生红成文彦王博
Owner 西北永新涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com