Preparation method of PVA fibers

A fiber and spinning dope technology, which is applied in the field of PVA fiber preparation, can solve the problems of increasing the risk of foreign matter left on the wound surface, and achieve the effect of less impurities and high purity

Inactive Publication Date: 2021-06-08
HUNAN XINJINFU MEDICAL TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For dressings for wound care, the risk of foreign bodies on the wound is increased due to the presence of water in the exudate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of PVA fibers
  • Preparation method of PVA fibers
  • Preparation method of PVA fibers

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] Such as figure 2 Shown, a kind of preparation method of PVA fiber comprises the following contents:

[0041] Step 1, preparing spinning dope;

[0042] The raw material adopts PVAc, and after adding methanol to dissolve, obtain the spinning stock solution through filtration; as an example, the concentration ratio range of PVAc and methanol in the spinning stock solution is 15-80 to 20-85; as a kind of preference, in the spinning stock solution The mass fraction of PVAc is 40-45%, and the mass fraction of methanol is 55-60%.

[0043] Step 2, spinning;

[0044] Under the conditions of 0.05-0.6MPa and temperature of 45-55°C, the spinning stock solution is injected into the spinneret, and the ejected fibers enter the DC electrolytic cell, such as image 3 As shown, the coagulation bath is carried out, the DC voltage of the DC electrolytic cell is 1.23V-200V, and a series of reactions of alcoholysis, electrolytic catalytic alcoholysis and alcohol leverage are carried out;...

Embodiment 1

[0050] first step,

[0051] Weigh 180 kg of polyvinyl acetate particles and 270 kg of methanol solution respectively, and add polyvinyl acetate first, followed by methanol, and add them to the reaction kettle. The temperature rises to 50 ° C to fully dissolve polyvinyl acetate to in methanol solution. The concentration ratio range of PVAc to methanol in the spinning dope is 2:3.

[0052] The obtained PVAc / MT solution is filtered through the first channel, degassed, and the second channel is filtered, and the PVAc / MT solution is introduced into the spinning pressure regulating tank.

[0053] In the second step, the electrolyte

[0054] Add 700 kilograms of water in the insulator electrolytic cell, drop into 270 kilograms of potassium hydroxide solids and 30 kilograms of 99% isopropanol in water.

[0055] ②Electrolytic cell

[0056] Combined with the process flow chart, an anode and a cathode electrode are formed in the electrolytic cell through the wire, and the electrode m...

Embodiment 2

[0065] first step,

[0066] Weigh 200 kg of polyvinyl acetate particles and 250 kg of methanol solution respectively, and add polyvinyl acetate first, followed by methanol, and add them to the reaction kettle. The temperature rises to 55 ° C to fully dissolve polyvinyl acetate to in methanol solution. The concentration ratio of PVAc to methanol in the spinning dope ranges from 4 to 5.

[0067] The obtained PVAc / MT solution is filtered through the first channel, degassed, and the second channel is filtered, and the PVAc / MT solution is introduced into the spinning pressure regulating tank.

[0068] second step,

[0069] ①Electrolyte

[0070] Add 700 kilograms of water in the insulator electrolytic cell, drop into the alcohol of 280 kilograms of potassium hydroxide and 20 kilograms of 99% in water.

[0071] ②Electrolytic cell

[0072] Combined with the process flow chart, an anode and a cathode electrode are formed in the electrolytic cell through the wire, and the electrode...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal decomposition temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of PVA fibers. The preparation method comprises the following steps: step 1, a spinning stock solution is prepared; PVAc is adopted as a raw material, methanol is added for dissolution, and then the spinning stock solution is obtained through filtration; step 2, spinning is conducted; the spinning stock solution is injected into a spinneret plate, sprayed fibers enter a direct-current electrolytic tank to be subjected to coagulating bath, and a series of reactions of alcoholysis, electrolytic catalysis alcoholysis and alcohol lever are carried out; the solution formula in the electrolytic coagulating bath comprises alkali, alcohol and water; step 3, acid bath is conducted; the fiber subjected to the coagulating bath is put into an acid solution with the pH value of 4.5-7.0, and acid bath is performed; and 4, stretching, drying, washing with water, curling with hot water and packaging are carried out to form a polyvinyl alcohol fiber finished product, PVA is replaced with PVAc, and an electrolytic coagulating bath is used cooperatively, so that the coagulating bath does not need to use mirabilite, the PVAc is subjected to alcoholysis in an electrolytic tank to obtain PVA, and the produced PVA fiber has high purity and few impurities.

Description

technical field [0001] The invention relates to the production field of polyvinyl alcohol fibers, in particular to a preparation method of PVA fibers. Background technique [0002] Polyvinyl alcohol (PVA) is a kind of water-soluble polymer, which is obtained by alcoholysis of polyvinyl acetate. Each repeating unit contains a hydroxyl group. It contains a large number of hydrogen bonds in and between molecules, so PVA molecules have a high degree of crystallinity. performance, chemical stability, thermal stability, etc. The average molecular weight of polyvinyl alcohol fibers is 60,000-250,000, the thermal decomposition temperature is 200-220°C, and the melting point is 225-230°C. [0003] Existing programs such as figure 1 Shown, raw material adopts PVA, coagulation bath adopts Glauber's salt; But such technique has following defect: [0004] 1. The purity of the obtained PVA fiber is not high and there are many impurities; [0005] 2. The coagulation bath needs to use G...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/14D01F6/16D01F11/06
CPCD01F6/14D01F6/16D01F11/06
Inventor 陈绍永
Owner HUNAN XINJINFU MEDICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap