Aluminium foil surface passivation treatment process and aluminium plastic film

A technology of passivation treatment and aluminum foil, applied in metal material coating technology, chemical instruments and methods, synthetic resin layered products, etc., can solve problems such as increased energy consumption, decreased yield of aluminum foil, and increased production costs, and achieves It has corrosion resistance and tensile properties, reduces the chance of equipment being corroded, and improves passivation efficiency

Pending Publication Date: 2021-06-15
浙江华正能源材料有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, hexavalent chromium is toxic and carcinogenic, and trivalent chromium also pollutes the environment to a certain extent
As time goes by, the country pays more and more attention to environmental protection. Therefore, the traditional chromium-based conversion coating will inevitably be gradually replaced. Moreover, the traditional chromium-based roller coating process has relatively large defects. On the one hand, chromium-based passivation The acidity of the solution is extremely strong (pH < 1), which will seriously corrode the roller coating equipment. On the other hand, the traditional roller coating is a single-sided coating process, while the aluminum foil in the aluminum-plastic film needs double-sided passivation treatment, so the aluminum foil needs to pass through two The anti-corrosion effect can only be achieved by the first roller coating. The more times the aluminum foil passes through the roller, the greater the loss of the aluminum foil. The two roller coatings will cause a significant drop in the yield of the aluminum foil, and the increase in energy consumption will eventually lead to the production cost of the product. rise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium foil surface passivation treatment process and aluminium plastic film
  • Aluminium foil surface passivation treatment process and aluminium plastic film
  • Aluminium foil surface passivation treatment process and aluminium plastic film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In this example, 200 g of zirconium acetate, 400 g of acrylamide-modified acrylic resin, and 20 g of sodium bifluoride were dissolved in pure water and fixed to 40 L to obtain a zirconium passivation solution. The passivation solution was placed in a passivation tank, and 4000 The rice aluminum foil is processed and rolled by the above-mentioned self-developed equipment, and the processing time and aluminum foil yield are counted.

[0040] The aluminum foil which has undergone surface passivation treatment is thermally bonded with nylon and CPP through the outer layer glue and the inner layer glue to obtain the aluminum plastic film.

[0041] The obtained passivated aluminum foil samples were subjected to a salt spray resistance test according to ASTM B117.

[0042] The obtained aluminum-plastic film was cut into a sample strip with a width of 15 mm, and the mechanical properties of the sample strip were tested to obtain the initial tensile force of the aluminum foil an...

Embodiment 2

[0045] In this example, 400 g of zirconium acetate, 200 g of acrylamide-modified acrylic resin, and 40 g of sodium bifluoride were dissolved in pure water and fixed to 40 L to obtain a zirconium passivation solution, and the chromium-free passivator was placed in the passivation tank. 4,000 meters of aluminum foil was processed and rolled by traditional roller coating equipment, and the processing time and aluminum foil yield were counted.

[0046] The aluminum foil which has undergone surface passivation treatment is thermally bonded with nylon and CPP through the outer layer glue and the inner layer glue to obtain the aluminum plastic film.

[0047] The obtained passivated aluminum foil samples were subjected to a salt spray resistance test according to ASTM B117.

[0048] The obtained aluminum-plastic film was cut into a sample strip with a width of 15 mm, and the mechanical properties of the sample strip were tested to obtain the initial tensile force of the aluminum foil ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of lithium batteries, and particularly relates to an aluminium foil surface passivation treatment process and an aluminium plastic film. The aluminium foil surface passivation treatment process comprises the following steps: (1) carrying out alkali washing and oil removal on the surface of an aluminium foil, carrying out roll coating and impregnation double-sided passivation treatment in sequence, and uniformly coating two sides of the aluminium foil with a chromium-free passivation agent through a non-contact trowelling air knife; and (2) baking the aluminium foil through a non-contact air flotation oven. The aluminium plastic film comprises a nylon layer, an aluminium foil layer and a CPP layer. The aluminium plastic film comprises a nylon layer, a CPP layer and an aluminium foil layer prepared through the passivation treatment process in the invention. According to the invention, the two surfaces of the aluminium foil can be passivated at the same time; the aluminium foil surface passivation efficiency is greatly improved; meanwhile, the contact area between the aluminium foil and an equipment roller is greatly reduced; the equipment corrosion probability is reduced; and the aluminium foil passivation treatment yield is increased.

Description

technical field [0001] The invention belongs to the technical field of lithium batteries, and in particular relates to an aluminum foil surface passivation treatment process and an aluminum-plastic film. Background technique [0002] Lithium-ion batteries are one of the greatest inventions of the 21st century. Its appearance has greatly changed people's production and lifestyle. Lithium-ion batteries are widely used in electronic products, such as notebook computers, new energy vehicles, smart phones, electric toys and other products. Lithium-ion batteries are mainly composed of outer film, glue, aluminum foil treatment layer, aluminum foil layer, glue and heat-sealing layer. The aluminum-plastic film is in direct contact with the inside of the lithium battery, and mainly plays the role of wrapping the entire battery and blocking water vapor and electrolyte. [0003] Over time, a series of chemical reactions will occur inside the lithium battery, resulting in the formation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/73C23C22/34C23C22/82B32B27/34B32B7/12B32B27/32B32B15/20B32B33/00
CPCC23C22/73C23C22/34C23C22/82B32B27/34B32B7/12B32B27/32B32B15/20B32B33/00B32B2255/06B32B2255/26B32B2307/714
Inventor 夏旭峰雷中伟
Owner 浙江华正能源材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap