Preparation method of environment-friendly PP plastic

A plastic and environmentally friendly technology, applied in the field of the preparation of environmentally friendly PP plastics, can solve the problems of increased extrusion pressure, poor impact resistance, poor toughness of PP plastics, etc., to increase the jitter frequency, reduce the preparation workload, and reduce extrusion. effect of stress

Pending Publication Date: 2021-06-25
孙兰
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, PP plastic has poor toughness, outstanding low-temperature brittleness, poor impact resistance, and long degradation cycle is not conducive to environmental protection. At the same time, the prepared PP plastic injection molding machine does not have a screening structure when feeding, and the masterbatch with larger particles is extruded. Increased extrusion pressure is not conducive to the preparation of PP plastics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of environment-friendly PP plastic
  • Preparation method of environment-friendly PP plastic
  • Preparation method of environment-friendly PP plastic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Such as figure 1 As shown, an environmentally friendly PP plastic, the environmentally friendly PP plastic is composed of the following components by weight: 58-88 parts of PP resin, 5-19 parts of plant fiber starch, 8-16 parts of calcium carbonate, 1.3-3 parts of nano titanium dioxide 6.8-9.8 parts of silane coupling agent, 1-2 parts of nano-silver oxide, 8-12 parts of graphene, 1-3 parts of nano-zinc oxide, 8-18 parts of ethylene to vinyl acetate copolymer, 3-aminopropyl 8-12 parts of triethoxysilane and 10-15 parts of ethyl acetate.

[0048] A kind of preparation method of environment-friendly PP plastic, preparation method step is as follows:

[0049] Step 1. Mix plant fiber starch, calcium carbonate, nano-titanium dioxide, nano-silver oxide and graphene and grind them in an ultrafine grinder. The grinding time is 15-20 minutes, and then pass through a 200-mesh sieve to obtain mixture A. Mix the mixture A As for the masterbatch prepared by the injection molding ma...

Embodiment 2

[0054] Embodiment 2 is a further improvement to Embodiment 1.

[0055] Based on the above formula and process, the present invention also provides figure 2 , 3 , 4, 5, 6, 8, 9, and 10 show a preparation device for environmentally friendly PP plastics, including an installation box 1, a door panel 2, an injection cylinder 4, a second drive motor 13, a reducer 14, and a second auger 15. The front side wall of the installation box 1 is fixedly connected with the door panel 2 by bolts, the inner bottom of the installation box 1 is fixedly connected with the second drive motor 13, the output end of the second drive motor 13 is fixedly connected with the reducer 14, and the injection cylinder 4 The fixedly connected bearing is connected in rotation with the reducer 14, the reducer 14 is fixedly connected with the rotating shaft 3, the rotating shaft 3 is fixedly connected with the second auger 15 for pushing the material to move, and the rotating shaft 3 is attached to the inner w...

Embodiment 3

[0061] Embodiment 3 is a further improvement to Embodiment 1.

[0062] Such as image 3 , 4 , 6, 7, and 11, the barrel 1101 is connected with a circulating feeding structure 12, and the circulating feeding structure 12 includes a first drive motor 1201, a discharge pipe 1202, a feeding barrel 1203, a hopper 1204, a mounting frame 1205, a first Two screening holes 1206, inclined pipe 1207, first auger 1208, receiving hopper 1209, sliding pipe 1210, motor 1211, cutting blade 1212 and rotating shaft 1213, the left end bottom of sliding circular plate 1103 is fixedly connected with receiving hopper 1209, sliding circular The plate 1103 is uniformly provided with second screening holes 1206, and the second screening holes 1206 are arranged on the top of the receiving hopper 1209, the bottom of the receiving hopper 1209 is fixedly connected with a sliding pipe 1210, and the outer wall of the bottom of the sliding pipe 1210 is fitted and slidably connected with a The inclined pipe ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of environment-friendly PP plastic. The environment-friendly PP plastic is prepared from the following components in parts by weight: 58 to 88 parts of PP resin, 5 to 19 parts of plant fiber starch, 8 to 16 parts of calcium carbonate, 1.3 to 3 parts of nano titanium dioxide, 6.8 to 9.8 parts of silane coupling agent, 1 to 2 parts of nano silver oxide, 8 to 12 parts of graphene, 1 to 3 parts of nano zinc oxide, 8 to 18 parts of ethylene-vinyl acetate copolymer, 8 to 12 parts of 3-aminopropyltriethoxysilane and 10 to 15 parts of ethyl acetate. The PP resin, the plant fiber starch, the calcium carbonate, the nano titanium dioxide, the silane coupling agent, the nano silver oxide, the graphene, the nano zinc oxide, the ethylene-vinyl acetate copolymer, the 3-aminopropyltriethoxysilane and the ethyl acetate are used as raw materials for preparing the environment-friendly PP plastic, and the prepared environment-friendly PP plastic has the advantages of being high in toughness, low in low-temperature brittleness, high in impact resistance, short in degradation period, and beneficial to environmental protection.

Description

technical field [0001] The invention relates to the technical field of plastic preparation, in particular to a preparation method of environment-friendly PP plastic. Background technique [0002] Plastic has the advantages of wide application, good formability, and low price, and has been widely used. However, long-term use of plastics has serious aging and single functions, and general plastics have poor heat-resistant and antibacterial effects. Therefore, the development of functional plastics will have a huge market prospect. [0003] Polypropylene (PP) is a kind of thermoplastic resin prepared by propylene polymerization. It has the advantages of excellent physical properties, simple molding process, low density and rich source of raw materials. It has become the fastest growing and development potential among the five general-purpose synthetic resins The largest class of resins. According to statistics, the combined output of PP and polyethylene accounts for 35% to 50...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L3/02C08L23/08C08K13/02C08K3/26C08K3/22C08K3/04C08K5/544B29B9/06B29B13/10B29C45/03B29C45/17B29C45/18
CPCC08L23/12B29B9/06B29B13/10B29C45/18B29C45/03B29C45/17C08L2205/03C08L2205/02C08K2201/011C08K2003/265C08K2003/2241C08K2003/2296C08K2003/2286C08L3/02C08L23/0853C08K13/02C08K3/26C08K3/22C08K3/042C08K5/544
Inventor 不公告发明人
Owner 孙兰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com