A kind of preparation method of heavy calcium carbonate for silicone rubber with high activation degree

A heavy calcium carbonate, activation degree technology, applied in chemical instruments and methods, adhesives, non-polymer adhesive additives, etc., can solve the problem of single-component modifier with single effect, poor modification effect and high preparation cost problem, to achieve the effect of simple and easy preparation method, low oil absorption value and low specific gravity

Active Publication Date: 2022-04-15
广西贺州市科隆粉体有限公司 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the inorganic characteristics of calcium carbonate powder, its compatibility with silicone oil is poor, and it needs to be modified. However, the existing composite surface modifiers have problems such as complex components and high preparation costs. Problems such as single effect and poor modification effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of heavy calcium carbonate for silicone rubber with high activation degree
  • A kind of preparation method of heavy calcium carbonate for silicone rubber with high activation degree

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A preparation method of heavy calcium carbonate for high-activation silicone rubber, which sequentially includes ore storage, cleaning, beneficiation, crushing and homogenization, grinding, grading, powder collection, quality inspection I, activation, cooling, and quality inspection II steps ;

[0033] The described ore storage steps are: storing the ore raw materials separately according to ore types and grades;

[0034] The cleaning steps are: cleaning the mud stuck on the surface of the ore with water;

[0035]The ore dressing step is: selecting the unqualified ore entrained in the ore; the unqualified ore is the ore with low whiteness, skin and other impurities;

[0036] The crushing and homogenizing step is as follows: crush the qualified ore into 18mm ore, and then send it into a 10,000-ton level homogenizing tank for homogenizing;

[0037] The grinding step is: sending the mineral material into the grinding equipment for grinding;

[0038] The grading step is:...

Embodiment 2

[0045] A preparation method of heavy calcium carbonate for high-activation silicone rubber, which sequentially includes ore storage, cleaning, beneficiation, crushing and homogenization, grinding, grading, powder collection, quality inspection I, activation, cooling, and quality inspection II steps ;

[0046] The described ore storage steps are: storing the ore raw materials separately according to ore types and grades;

[0047] The cleaning steps are: cleaning the mud stuck on the surface of the ore with water;

[0048] The ore dressing step is: selecting the unqualified ore entrained in the ore; the unqualified ore is the ore with low whiteness, skin and other impurities;

[0049] The crushing and homogenizing step is as follows: crushing the qualified ore into 15mm ore, and then sending it into a 10,000-ton level homogenizing tank for homogenizing;

[0050] The grinding step is: sending the mineral material into the grinding equipment for grinding;

[0051] The grading s...

Embodiment 3

[0058] A preparation method of heavy calcium carbonate for high-activation silicone rubber, which sequentially includes ore storage, cleaning, beneficiation, crushing and homogenization, grinding, grading, powder collection, quality inspection I, activation, cooling, and quality inspection II steps ;

[0059] The described ore storage steps are: storing the ore raw materials separately according to ore types and grades;

[0060] The cleaning steps are: cleaning the mud stuck on the surface of the ore with water;

[0061] The ore dressing step is: selecting the unqualified ore entrained in the ore; the unqualified ore is the ore with low whiteness, skin and other impurities;

[0062] The crushing and homogenizing step is as follows: crush the qualified ore into a 10mm mineral material, and then send it into a 10,000-ton level homogenizing tank for homogenizing;

[0063] The grinding step is: sending the mineral material into the grinding equipment for grinding;

[0064] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
activation indexaaaaaaaaaa
activation indexaaaaaaaaaa
activation indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of heavy calcium carbonate for high-activation silicone rubber, which sequentially includes ore storage, cleaning, beneficiation, crushing and homogenization, grinding, grading, powder collection, quality inspection I, activation, cooling, Quality inspection Ⅱ step. The preparation method of the present invention is simple and easy, and the prepared calcium carbonate powder has good dispersibility, high degree of activation, high whiteness and very low oil absorption value, and can effectively improve the thixotropy and tensile properties of silicone glue. tensile strength.

Description

technical field [0001] The invention belongs to the technical field of calcium carbonate preparation, and in particular relates to a preparation method of heavy calcium carbonate for high activation degree silicone glue. Background technique [0002] Calcium carbonate is an inorganic powder with many hydroxyl groups on the surface, which is easy to absorb water and exhibits hydrophilic and oleophobic properties. It is difficult to disperse evenly in organic media, so it cannot cross-link with polymer materials such as rubber and plastic. Poorly dispersed calcium carbonate not only seriously affects the appearance of the product, but the large aggregates are also easy to form internal defects in the material, which cannot achieve the ideal reinforcement effect on polymer materials. In order to solve the above problems, it is necessary to modify the surface of the calcium carbonate powder. The surface properties of the calcium carbonate powder can be changed through surface tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/02C09C3/04C09C3/12C09C3/08C09J183/04C09J11/04
CPCC09C1/021C09C3/003C09C3/045C09C3/041C09C3/12C09C3/08C09C3/006C09J183/04C09J11/04C08K2003/265C01P2006/22C01P2006/65C01P2006/19C08K9/04C08K9/06C08K3/26
Inventor 贝进国童张法李奇洪黄华彬叶有谢云莫及刘慧芝陈小鹏覃玲意钟玲萍
Owner 广西贺州市科隆粉体有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com