A kind of support for artificial cornea and preparation method thereof

A technology of artificial cornea and chondrocytes, which is applied in the field of artificial cornea support and its preparation to achieve the effects of reducing discharge and water leakage

Active Publication Date: 2022-01-28
THE FIRST MEDICAL CENT CHINESE PLA GENERAL HOSPITAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention overcomes the defects of existing artificial corneal stents, and provides an artificial corneal stent with high survivability and little damage to patients

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of support for artificial cornea and preparation method thereof
  • A kind of support for artificial cornea and preparation method thereof
  • A kind of support for artificial cornea and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1 Preparation of Chondrocyte Extracellular Matrix / Bone Matrix-Adipose Mesenchymal Stem Cells (DCECM / DBM-rADMSCs) Composite Scaffold

[0039] 【Preparation of Chondrocyte Extracellular Matrix / Bone Matrix (DCECM / DBM) Scaffold】

[0040] 1-1 Preparation of chondrocyte extracellular matrix (DCECM)

[0041] (1) Take out 100 g of fetal bovine articular cartilage one day old, and wash it with sterile distilled water for 3 times, each time for 10 minutes;

[0042] (2) Soak in 1% acetic acid for 3 times, each time for 3 hours;

[0043] (3) Hypotonic freezing and thawing in a freezer at -20°C for 8 hours;

[0044] (4) Melt ice, discard water and wash with distilled water twice;

[0045] (5) soak and sterilize in 3% hydrogen peroxide solution for 6 hours;

[0046] (6) Washing with sterile three-distilled water for 3 times, each time for 10 minutes;

[0047](7) Pulverize in a pulverizer to a homogenate with cells in millimeter, micron, and nanometer scales;

[0048] (...

Embodiment 2

[0078] Example 2 Histopathological examination of chondrocyte extracellular matrix / bone matrix-rabbit adipose-derived mesenchymal stem cells (DCECM / DBM-rADMSCs) composite scaffold

[0079] 2-1 Prepare chondrocyte extracellular matrix / bone matrix (DCECM / DBM) scaffold in the same manner as in Example 1

[0080] 2-2 Primary culture of rabbit adipose-derived mesenchymal stem cells (rADMSCs)

[0081] (1) Sumianxin + ketamine (1:1) is anesthetized by intramuscular injection of 0.3ml / kg;

[0082] (2) Put the rabbit on the operating table, remove the hair in the operation area, disinfect the operation field with iodophor cotton ball three times, and wipe with alcohol three times;

[0083] (3) Make an incision about 3 cm long in the right lower groin of the rabbit, the depth reaches the subcutaneous tissue, bluntly separate the subcutaneous tissue, explore while separating until the subcutaneous fat is found, carefully cut out the blocky fat tissue, and pay attention to avoiding l...

Embodiment 3

[0100] Example 3 Animal experiment of cartilage generation effect of chondrocyte extracellular matrix / bone matrix-rabbit adipose-derived mesenchymal stem cells (DCECM / DBM-rADMSCs) composite scaffold

[0101] 3-1 Prepare chondrocyte extracellular matrix / bone matrix-rabbit adipose-derived mesenchymal stem cells (DCECM / DBM-rADMSCs) composite scaffold

[0102] 3-2 Rabbit corneal chondrocyte extracellular matrix / bone matrix-rabbit adipose-derived mesenchymal stem cells (DCECM / DBM- rADMSCs) composite scaffold autografting

[0103] (1) Lu Mianxin: Midazolam = 1:1, 0.2ml / Kg intramuscular injection for anesthesia;

[0104] (2) Place the rabbit on the operating table, sterilize the right eye with iodophor, deiodine with alcohol, spread a sterile drape, place a lid speculum, and treat the eye with Benuoxi;

[0105] (3) scrape off the corneal epithelium with a corneal epidermectomy;

[0106] (4) Make a lamellar incision about 3 mm long at a distance of 2 mm from the corneal limbu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a scaffold for artificial cornea and its preparation method, which includes decalcified and decellularized cancellous bone matrix sheet → soaking and sticking nano-scale cartilage, umbilical cord and other ECM cell extracellular matrix inside and outside the scaffold → composite autologous Mesenchymal stem cells (bone marrow, fat and other cells), cultured and placed in the interlayer, front surface, conjunctiva or submucosal of the cornea, used to replace bone, cartilage or tooth bone in artificial corneal surgery, as a scaffold or reinforcement of artificial cornea Material. The scaffold for artificial cornea according to the present invention has a microenvironment that is conducive to the growth of cells in vivo and in vitro through adsorption induction, can promote the differentiation of mesenchymal stem cells into cartilage-like and osteogenic tissues in vivo, facilitates the fixation of artificial cornea, and improves the artificial cornea. occupancy rate.

Description

technical field [0001] The invention relates to the technical field of artificial corneas, in particular to a bracket for artificial corneas and a preparation method thereof. Background technique [0002] Artificial cornea (Keratoprosthesis, Kpro) is an artificial device used to replace the diseased cornea to exert its optical and biological functions. The artificial cornea generally includes two parts: the lens column (optical part) and the bracket (reinforcement material). Among them, the lens column is made of a transparent material with excellent optical properties and stable physical and chemical properties, which is used to replace the turbidity that hinders the optical pathway of the eye after the lesion cornea. In order to achieve the ideal optical effect, most of the artificial corneas currently adopt the penetrating type, that is, the lens column of the artificial cornea penetrates the whole layer of the cornea, and the lens column is fixed in the center of the co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/36A61L27/38
CPCA61L27/3633A61L27/3641A61L27/3687A61L27/3691A61L27/3608A61L27/3834A61L2430/16A61L2430/40
Inventor 王丽强黄一飞黄靖香程帅帅
Owner THE FIRST MEDICAL CENT CHINESE PLA GENERAL HOSPITAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com