Carboxymethyl chitosan/hydroformylated carboxymethyl cellulose composite membrane and preparation method thereof

A technology of carboxymethyl chitosan and carboxymethyl cellulose is applied in the field of carboxymethyl chitosan/formaldehyde carboxymethyl cellulose composite film and its preparation, which can solve problems such as toxicity and achieve enhanced antibacterial properties. , good mechanical properties, the effect of extending shelf life

Active Publication Date: 2021-07-30
NANJING UNIV OF TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the natural traditional Chinese medicine matrine has certain toxicity to the human body, and it also has certain risks to the human body when it is used in food preservation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carboxymethyl chitosan/hydroformylated carboxymethyl cellulose composite membrane and preparation method thereof
  • Carboxymethyl chitosan/hydroformylated carboxymethyl cellulose composite membrane and preparation method thereof
  • Carboxymethyl chitosan/hydroformylated carboxymethyl cellulose composite membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Dissolve carboxymethylcellulose in water, stir at 30°C to form a carboxymethylcellulose solution with a mass fraction of 0.5%, and place it in a round-bottomed flask. Dissolve 1.5 times mol of sodium periodate in deionized water, shake to dissolve and add to a round bottom flask. The flask was wrapped in tin foil and protected from light. After 2.5 h of reaction, 8 mL of ethylene glycol was added to terminate the reaction for 1 h. The reaction solution was put into a 3500Da dialysis bag and purified by dialysis in deionized water for 72 hours. The water was changed every 12 hours. After three days, it was concentrated by rotary evaporation. Hydroformylated carboxymethyl cellulose with a degree of hydroformylation of 13%.

[0036] (2) get carboxymethyl chitosan (CMCS) to be dissolved in water respectively and form the carboxymethyl chitosan solution that mass fraction is 1.5%, 2.0%, 2.5%, then add appropriate amount of formaldehyde carboxymethyl cellulose, make Th...

Embodiment 2

[0045] (1) Dissolve carboxymethylcellulose in water, stir at 30°C to form a carboxymethylcellulose solution with a mass fraction of 0.8%, and place it in a round-bottomed flask. Dissolve 2 times mol of sodium periodate in deionized water, shake to dissolve and add to a round bottom flask. The flask was wrapped in tin foil and protected from light. After 2.5 h of reaction, 10 mL of ethylene glycol was added to terminate the reaction for 1 h. The reaction solution was put into a 3500Da dialysis bag and purified by dialysis in deionized water for 72 hours. The water was changed every 12 hours. After three days, it was concentrated by rotary evaporation. Hydroformylated carboxymethyl cellulose with a degree of hydroformylation of 15%.

[0046] (2) Dissolve carboxymethyl chitosan in water to form a carboxymethyl chitosan solution with a mass fraction of 2.0%, and then add an appropriate amount of carboxymethyl cellulose (CMC-CHO) to make the coating solution The mass fractions o...

Embodiment 3

[0054] (1) Dissolve carboxymethyl cellulose in water, stir at 30° C. to form a carboxymethyl cellulose solution with a mass fraction of 1%, and put it in a round bottom flask. Dissolve 2.5 times mol of sodium periodate in deionized water, shake to dissolve and add to a round bottom flask. The flask was wrapped in tin foil and protected from light. After 2.5 h of reaction, 12 mL of ethylene glycol was added to terminate the reaction for 1 h. The reaction solution was put into a 3500Da dialysis bag and purified by dialysis in deionized water for 72 hours. The water was changed every 12 hours. After three days, it was concentrated by rotary evaporation. Hydroformylated carboxymethyl cellulose with a degree of hydroformylation of 15%.

[0055] (2) Dissolve carboxymethyl chitosan in water to form a carboxymethyl chitosan solution with a mass fraction of 2.0%, then add an appropriate amount of carboxymethyl cellulose to form carboxymethyl cellulose in the coating solution The pri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carboxymethyl chitosan / hydroformylated carboxymethyl cellulose composite membrane and a preparation method thereof.The preparation method comprises the steps: making carboxymethyl cellulose dissolved in water to obtain a carboxymethyl cellulose solution, mixing the carboxymethyl cellulose solution and a sodium periodate aqueous solution evenly for a light-proof reaction, then, adding ethylene glycol to terminate the reaction, and carrying out dialysis purification, concentration and vacuum drying on the obtained reaction liquid to obtain hydroformylated carboxymethyl cellulose; dissolving carboxymethyl chitosan in water to obtain a carboxymethyl chitosan solution, then adding the hydroformylated carboxymethyl cellulose and a plasticizer, and uniformly stirring and mixing to obtain a film coating solution; and uniformly coating a substrate with the film coating solution, removing bubbles, and drying to form the composite membrane. The carboxymethyl chitosan / hydroformylated carboxymethyl cellulose composite membrane disclosed by the invention has good mechanical properties; the water vapor transmission rate is high, the ultraviolet light absorption performance is good, the damage effect of the ultraviolet light can be effectively blocked, and the good inhibition effect on aspergillus niger and penicillium is achieved.

Description

technical field [0001] The invention belongs to the technical field of food preservation and antibacterial materials, and in particular relates to a carboxymethyl chitosan / formylated carboxymethyl cellulose composite film and a preparation method thereof. Background technique [0002] Fruits and vegetables are the main sources of human intake of essential vitamins and inorganic salts, and are important foods to ensure human health. With the improvement of people's quality of life, the demand for fruits and vegetables is also increasing, but the shelf life of fruits and vegetables is short and perishable, and is also limited by seasons and regions. In 2019, the planting area of ​​vegetables and fruits in my country was 33,140 square kilometers, and the annual output of fruits reached 274 million tons. The loss rate after harvest was as high as 30% due to improper storage and transportation and imperfect fresh-keeping technology. The purpose of fruit and vegetable preservatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08L5/08C08L1/28
CPCC08J5/18C08J2305/08C08J2401/28
Inventor 姚忠曹立妤吴若寒孙芸朱本伟
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com