Light burning solid waste 3D printing ventilation sealing material and preparation method thereof

A 3D printing and light burning technology, which is applied in the field of light burning solid waste 3D printing ventilation and airtight materials and its preparation, can solve problems that affect mine safety production, high construction costs, brittle damage, etc., and achieve resource utilization, excellent Stacking and strength properties, and the effect of avoiding brittle failure

Active Publication Date: 2021-08-13
HENAN INST OF ENG +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a light-burning solid waste 3D printing ventilation and airtight material and its preparation method to overcome the high cost, low construction efficiency, Labor intensity is high, and brittle damage forms cracks to cause air leakage, which affects the safe production of mines. At the same time, it realizes the resource utilization of medical waste incineration ash, domestic waste incineration ash and phosphogypsum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light burning solid waste 3D printing ventilation sealing material and preparation method thereof
  • Light burning solid waste 3D printing ventilation sealing material and preparation method thereof
  • Light burning solid waste 3D printing ventilation sealing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The present invention also provides a method for preparing light-burned solid waste 3D printing ventilation and sealing materials. The preparation method is prepared by using the component raw materials contained in the light-burning solid waste 3D printing ventilation and sealing materials. The preparation method includes the following steps :

[0052] Step S1, pretreat the bottom ash of medical waste incineration, fly ash of domestic waste incineration and phosphogypsum, and then weigh the pretreated bottom ash of medical waste incineration, fly ash of domestic waste incineration and phosphogypsum according to the proportion and mix them evenly, Then it is calcined at a high temperature in a furnace, cooled at room temperature and ground to obtain an active admixture.

[0053] In a specific embodiment of the present invention, the pretreatment of medical waste incineration bottom ash, domestic waste incineration fly ash and phosphogypsum in step S1 is specifically at ...

Embodiment 1

[0073] This embodiment provides a light-burning solid waste 3D printing ventilation and sealing material, which includes the following raw materials in parts by weight: 25 parts of medical waste incineration bottom ash, 8 parts of phosphogypsum, Portland cement 40 parts of clinker, 6.5 parts of domestic waste incineration fly ash, 120 parts of spontaneous combustion coal gangue, 4.5 parts of carbide slag, 0.3 parts of aluminum sulfate, 0.2 parts of sodium carbonate, 0.5 parts of sodium methyl silicate, 4.5 parts of acrylic acid emulsion, carboxymethyl Base cellulose sodium 0.1 part, water 34 parts.

[0074] In this embodiment, the preparation method of light-burned solid waste 3D printing ventilation and airtight materials includes the following steps:

[0075] Step S1. Dry the bottom ash of medical waste incineration, fly ash of domestic waste incineration and phosphogypsum at 110°C to constant weight, screen out the metal impurities in the bottom ash of medical waste inciner...

Embodiment 2

[0084] This embodiment provides a light-burning solid waste 3D printing ventilation and sealing material. The ventilation and sealing material includes the following raw materials in parts by weight: 25 parts of medical waste incineration bottom ash, 5 parts of phosphogypsum, Portland cement 30 parts of clinker, 8 parts of domestic waste incineration fly ash, 60 parts of spontaneous combustion coal gangue, 3 parts of carbide slag, 0.2 parts of aluminum sulfate, 0.2 parts of sodium carbonate, 0.5 parts of sodium methyl silicate, 4 parts of acrylic emulsion, carboxymethyl Base cellulose sodium 0.1 part, water 28 parts.

[0085] The difference between the preparation method of light-burned solid waste 3D printing ventilation and airtight materials in this example and the preparation method in Example 1 is that the amount of raw materials in this example is according to the proportion of the above components in this example, and the calcination in step S1 The temperature is 850° C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
cylinder compressive strengthaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a light burning solid waste 3D printing ventilation sealing material and a preparation method thereof. The ventilation sealing material is prepared from the following components: 15 to 30 parts of medical waste incineration bottom ash, 5 to 10 parts of phosphogypsum, 30 to 45 parts of Portland cement clinker, 5 to 8 parts of household waste incineration fly ash, 60 to 180 parts of spontaneous combustion coal gangue, 3 to 6 parts of carbide slag, 0.2 to 0.4 parts of aluminum sulfate, 0.1 to 0.3 parts of sodium carbonate, 0.3 to 0.8 parts of sodium methyl silicate, 4 to 5 parts of acrylic emulsion, 0.06 to 0.13 parts of sodium carboxymethyl cellulose or hydroxypropyl methyl cellulose and 28 to 40 parts of water. The prepared 3D printing ventilation sealing material is in a slurry shape, the slurry has excellent extrudability, stacking performance and strength performance and has certain yielding performance, meanwhile, resource utilization of solid waste is achieved, and good environmental and economic benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of civil engineering materials, and in particular relates to a light-burning solid waste 3D printing ventilation and airtight material and a preparation method thereof. Background technique [0002] Medical waste is infectious, toxic and other hazardous solid waste produced by medical institutions during medical activities. If not handled properly, medical waste will cause environmental pollution and spread of diseases, thereby threatening human physical and mental health. The output of medical waste is huge. With the outbreak of the new crown epidemic, the total amount of medical waste in my country will exceed 1.6 million tons. Medical waste disposal methods include cleaning and disinfection, high-temperature disinfection, landfill and incineration, etc. Incineration has the advantages of volume reduction, weight reduction, and high-temperature sterilization, and is widely popularized and applied. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B38/02C04B24/42C04B24/38C04B24/26C04B22/14C04B22/10C04B18/10B33Y10/00B33Y70/10
CPCC04B28/143C04B24/42C04B24/383C04B22/10C04B22/148C04B18/10C04B24/26C04B38/02B33Y10/00B33Y70/10C04B2111/00017C04B2111/00724C04B7/02C04B18/12C04B18/0427Y02W30/91
Inventor 卢前明孔林陈景卫陈永丰李强王静文
Owner HENAN INST OF ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com