Sodium hyaluronate with full molecular weight distribution as well as preparation method and application of sodium hyaluronate

A technology of sodium hyaluronate and molecular weight distribution, which can be used in medical preparations containing active ingredients, applications, preparations for skin care, etc. Uniformity, product uniformity is difficult to guarantee and other problems, to achieve the effect of superior intelligent moisturizing, improving preparation efficiency and yield, and improving impurity removal efficiency

Active Publication Date: 2021-10-19
MEYER BIO-MEDICINE CO LTD +2
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, if the existing method wants to obtain sodium hyaluronate with a wider molecular weight distribution, it is necessary to mix and compound sodium hyaluronate of each molecular weight segment. However, the viscosity and other properties of sodium hyaluronate products with different molecular weights The difference is large, and the homogeneity of the product obtained by

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sodium hyaluronate with full molecular weight distribution as well as preparation method and application of sodium hyaluronate
  • Sodium hyaluronate with full molecular weight distribution as well as preparation method and application of sodium hyaluronate
  • Sodium hyaluronate with full molecular weight distribution as well as preparation method and application of sodium hyaluronate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment provides a method for preparing sodium hyaluronate with full molecular weight distribution, which specifically includes the following steps:

[0036] Step 1): Take 1 kg of food-grade sodium hyaluronate raw material with a molecular weight of 1 million, and evenly spray 50 mL of 1% hydrogen peroxide on the surface of the sodium hyaluronate raw material, using 300 μW / cm 2 Dose of ultraviolet radiation for 60min;

[0037] Step 2): Dissolving the sodium hyaluronate raw material after ultraviolet irradiation in water at a concentration of 1% (w / v), and stirring at room temperature to completely dissolve it;

[0038] Step 3): Use 2% NaOH solution to adjust the pH to 10, and then place it under 10 kHz ultrasonic treatment for 15 minutes;

[0039] Step 4): Prepare a 1 million sodium hyaluronate solution with a concentration of 1% (w / v), and mix it with the above-mentioned treated sodium hyaluronate alkaline solution at an addition ratio of 60% (v / v);

[0040] ...

Embodiment 2

[0044] This embodiment provides a method for preparing sodium hyaluronate with full molecular weight distribution, which specifically includes the following steps:

[0045] Step 1): Take 1 kg of food-grade sodium hyaluronate raw material with a molecular weight of 1.2 million, evenly spray 80 mL of 3% hydrogen peroxide on the surface of the sodium hyaluronate material, and use 600 μW / cm 2 Dose of ultraviolet radiation for 60min;

[0046]Step 2): Dissolving the sodium hyaluronate raw material after ultraviolet irradiation in water at a concentration of 3% (w / v), stirring at room temperature to completely dissolve it;

[0047] Step 3): Use 5% NaOH solution to adjust the pH to 12, and then place it under 30 kHz ultrasonic treatment for 30 minutes;

[0048] Step 4): Prepare a 1.2 million sodium hyaluronate raw material solution with a concentration of 0.8% (v / v), and mix it with the above-mentioned treated sodium hyaluronate alkaline solution at an addition ratio of 40%;

[0049...

Embodiment 3

[0053] This embodiment provides a method for preparing sodium hyaluronate with full molecular weight distribution, which specifically includes the following steps:

[0054] Step 1): Take 1 kg of cosmetic grade sodium hyaluronate raw material with a molecular weight of 1.2 million, evenly spray 80 mL of 5% hydrogen peroxide onto the surface of the sodium hyaluronate material, and use 900 μW / cm 2 Dose of ultraviolet radiation for 60min;

[0055] Step 2): Dissolving the sodium hyaluronate material after ultraviolet irradiation in water at a concentration of 5% (w / v), stirring at room temperature to completely dissolve it;

[0056] Step 3): Use 5% (w / v) NaOH solution to adjust the pH to 12, and then place it under 60kHz ultrasonic treatment, and the ultrasonic treatment time is 60min;

[0057] Step 4): Prepare a 1.2 million high molecular weight sodium hyaluronate solution with a concentration of 0.6% (w / v), and mix it with the above-mentioned treated sodium hyaluronate alkaline ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of sodium hyaluronate with full molecular weight distribution, wherein the method comprises the steps: 1) carrying out hydrogen peroxide spraying and ultraviolet radiation treatment on a sodium hyaluronate solid raw material to obtain a sodium hyaluronate degradation material; 2) dissolving the sodium hyaluronate degradation material in water, and adjusting the pH value to be alkaline by using a NaOH solution to obtain a sodium hyaluronate alkaline solution; 3) performing ultrasonic treatment on the sodium hyaluronate alkaline solution; 4) preparing a sodium hyaluronate solution with the concentration of 0.1%-1% (w/v) from a hyaluronic acid solid raw material, and uniformly mixing the sodium hyaluronate solution with the sodium hyaluronate alkaline solution subjected to ultrasonic treatment according to the adding proportion of 20%-60% (v/v); and 5) performing adsorption treatment by adopting diatomite and activated carbon respectively, filtering and concentrating by adopting a nano filter membrane, and drying to obtain the product. According to the preparation method disclosed by the invention, sodium hyaluronate with relatively good activities such as water replenishing, moisturizing, anti-inflammation resistance and cell protection can be obtained.

Description

technical field [0001] The present application relates to the technical field of biomaterials, in particular to a sodium hyaluronate with a full molecular weight distribution and its preparation method and application. Background technique [0002] Hyaluronic acid (Haluronic acid, HA) is a linear polysaccharide linked by D-glucuronic acid and N-acetyl-D-glucosamine, with a molecular weight of hundreds of thousands to millions of daltons, widely distributed in In animal tissues, especially in human skin, umbilical cord, eye vitreous body and joint synovial fluid, the content is the highest, and it is also widely distributed in plants and microorganisms. In nature, HA has the same structure, no racial differences, and no immunogenicity. [0003] When HA is in a high concentration (1%), the intermolecular network exists in the form of a high viscoelasticity. The aqueous solution of HA is a viscoelastic fluid, which fills the space between cells and collagen fibers and covers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08B37/08A23L29/00A23L33/125A61K8/73A61K31/728A61P17/00A61P29/00A61P43/00A61Q19/00
CPCC08B37/0072A61K31/728A61P17/00A61P29/00A61P43/00A61K8/735A61Q19/00A23L33/125A23L29/045A23L29/04A23V2002/00A23V2200/23A23V2200/30A23V2250/51
Inventor 凌沛学邵华荣曾庆恺
Owner MEYER BIO-MEDICINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap