Acellular matrix fiber dressing and preparation method thereof
An acellular matrix and fiber technology, applied in the field of acellular matrix fiber dressing and its preparation, can solve the problems affecting wound recovery, infection, etc., and achieve the effects of increasing recovery effect, inhibiting colonization and uniform performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] Such as figure 1 As shown, the present embodiment provides a spongy acellular matrix fiber dressing, the steps of its preparation comprising:
[0030] S1. Take the wet acellular matrix and cut it into a size less than 1cm 2 After the fragments, carry out high-speed mashing in a short time (no more than 1min);
[0031] S2. Take 0.5% (wet weight) of the acellular matrix, 0.01% glacial acetic acid and the rest of purified water by weight percentage, mix and cool down to 2°C;
[0032] S3. Perform homogenization at a frequency of 21 Hz, and then homogenize the collected feed liquid twice, filter out coarse particles, and use a 4% NaOH solution to adjust the pH of the filtered slurry to 6.5 , to obtain decellularized matrix fibers after centrifugation;
[0033] S4. Prepare an aqueous dispersion containing the acellular matrix fiber, adjust the pH to 4, add silver sulfate solution according to the solid content until the final mass fraction of silver in the acellular matrix...
Embodiment 2
[0035] This embodiment provides another spongy acellular matrix fiber dressing, the preparation steps of which include:
[0036] S1. Take the wet acellular matrix and cut it into a size less than 1cm 2 After the fragments, carry out high-speed mashing in a short time (no more than 1min);
[0037] S2. Take 3.0% (wet weight) of the acellular matrix, 0.1% glacial acetic acid and the rest of purified water by weight percentage, mix and cool down to 8°C;
[0038] S3. Perform homogenization at a frequency of 28 Hz, and then homogenize the collected material liquid twice, filter out coarse particles, and use a 6% NaOH solution to adjust the pH of the filtered slurry to 7.0 , to obtain decellularized matrix fibers after centrifugation;
[0039] S4. Prepare the aqueous dispersion containing the acellular matrix fiber, adjust the pH to 8, and add the silver chloride dispersion according to the solid content until the final mass fraction of silver in the acellular matrix fiber dressing...
Embodiment 3
[0041] Adopt GB 15979-2002 appendix C3 to detect the bactericidal performance of the acellular matrix fiber dressing prepared in Example 1, and the results are shown in the table below:
[0042] Table 1
[0043]
[0044] In summary, the present invention homogenizes the acellular matrix through fibrosis to obtain products with uniform properties; at the same time, silver salts are evenly dispersed, thereby slowly and continuously releasing silver ions when contacting wounds, which can inhibit gold The colonization of Staphylococcus aureus, Escherichia coli and Candida albicans increases the recovery effect of the wound.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com