High-transparency cellulose acetate material and preparation method thereof

A cellulose acetate and high-transparency technology, which is applied in the field of high-transparency cellulose acetate materials and its preparation, can solve problems such as being unfavorable to industrial production and reducing production efficiency, so as to reduce the risk of precipitation, improve production efficiency, and save time. Effect

Active Publication Date: 2022-01-07
SUZHOU HSM TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This also greatly reduces the production efficiency, which is not conducive to the realization of industrialized production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-transparency cellulose acetate material and preparation method thereof
  • High-transparency cellulose acetate material and preparation method thereof
  • High-transparency cellulose acetate material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh 100 parts of cellulose acetate (Wuhan Penglei Biotechnology Co., Ltd.), 20 parts of plasticizer triphenyl phosphate (Adamas, RG), 1 part of cross-linking agent triglycidyl isocyanurate (Guangzhou Hongcheng Biotechnology Co., Ltd. Technology Co., Ltd.), 0.3 part of antioxidant β-(3,5-di-tert-butyl-4-hydroxyphenyl) n-octadecyl propionate (BASF, Irganox1076), 0.3 part of lubricant erucamide ( Add Adamas, RG) into a high-speed mixer and mix evenly, then put the mixed raw materials into an oven at 110°C for 2 hours, then extrude and granulate on a screw extruder, the temperature in the first zone is 160°C, and the temperature in the second zone is 170°C , the temperature of the third zone is 170°C, the temperature of the fourth zone is 170°C, the temperature of the fifth zone is 170°C, the temperature of the sixth zone is 175°C, the temperature of the seventh zone is 175°C, the temperature of the eighth zone is 175°C, the temperature of the ninth zone is 175°C, the temp...

Embodiment 2

[0037] Weigh 100 parts of cellulose acetate (Wuhan Penglei Biotechnology Co., Ltd.), 18 parts of plasticizer triacetin (Shandong Youso Chemical Technology Co., Ltd.), 1 part of crosslinking agent succinic anhydride (Adamas, RG) , 0.3 parts of antioxidant tetrakis (β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) pentaerythritol ester (BASF, Irganox1010), 0.3 parts of lubricant erucamide (Adamas, RG), Add 0.1 part of nucleating agent ethylene bis stearamide (Adamas, RG) into a high-speed mixer and mix evenly, then put the mixed raw materials in an oven for 2 hours at 120°C, and then extrude and granulate on a screw extruder , the temperature in the first zone is 160°C, the temperature in the second zone is 170°C, the temperature in the third zone is 170°C, the temperature in the fourth zone is 170°C, the temperature in the fifth zone is 170°C, the temperature in the sixth zone is 175°C, the temperature in the seventh zone is 175°C, the temperature in the eighth zone is 175°C, a...

Embodiment 3

[0039] The preparation process is basically the same as in Example 2, except that the crosslinking agent succinic anhydride is replaced by triallyl isocyanurate (Guangzhou Hongcheng Biotechnology Co., Ltd.).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
transmittivityaaaaaaaaaa
hazeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-transparency cellulose acetate material and a preparation method thereof. The high-transparency cellulose acetate material comprises the following raw materials by weight: 100 parts of cellulose acetate, 17-25 parts of a plasticizer, 0.1-2 parts of a cross-linking agent, and 0.1-2 parts of other auxiliary agents. The cross-linking agent is selected from isocyanate, dianhydride or peroxide; and the melting point of the cross-linking agent is not higher than 120 DEG C. The preparation process comprises the following steps of uniformly blending all the raw materials, performing heating treatment to perform melting pre-crosslinking modification, and then performing extrusion, granulation and drying to obtain the high-transparency cellulose acetate material. According to the cellulose acetate material prepared by adopting the raw materials and the process, the use amount of a plasticizer is remarkably reduced, and the risk of precipitation is reduced; and the prepared cellulose acetate material has the advantages of high light transmittance, low haze, simple and convenient process flow, short time consumption and high production efficiency, and is suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the field of cellulose acetate materials, and in particular relates to a high-transparency cellulose acetate material and a preparation method thereof. Background technique [0002] Cellulose acetate (CA) is a cellulose derivative obtained by acetylation of cellulose, and it is also the earliest commercialized cellulose derivative. The performance of cellulose acetate depends on the degree of acetylation of the hydroxyl group in the production process. It has the characteristics of good toughness, good gloss, high mechanical strength, high transparency, stable to light, and non-flammable. At present, cellulose acetate is widely used in cigarette filters, textile fibers, medical materials, separation membranes and other fields. [0003] At present, the methods for preparing cellulose acetate transparent products or improving the transparency of cellulose acetate products mainly include: 1, solvent method, after utilizing aceton...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/12C08K5/523C08B15/00C08K5/103C08K5/526C08K5/11
CPCC08K5/523C08K5/103C08K5/526C08K5/11C08B15/005C08L2201/10C08L1/12Y02W90/10
Inventor 台启龙赵铭何明山陈丽娟
Owner SUZHOU HSM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products