A kind of cobalt-free lithium-rich cathode material and its preparation method and application

A lithium-rich positive electrode material and lithium source technology, applied in the direction of positive electrodes, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of low capacity and troublesome preparation, and achieve the effect of improving cycle performance

Active Publication Date: 2022-03-22
SVOLT ENERGY TECHNOLOGY CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the cycle stability is improved to a certain extent, the preparation is cumbersome and the capacity is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cobalt-free lithium-rich cathode material and its preparation method and application
  • A kind of cobalt-free lithium-rich cathode material and its preparation method and application
  • A kind of cobalt-free lithium-rich cathode material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This embodiment provides a cobalt-free lithium-rich positive electrode material whose chemical formula is , the positive electrode material through Ni 0.35 mn 0.65 (OH) 2 It is obtained by sintering after compounding with lithium carbonate, wherein the doping amount of Ti is 2000ppm, the coating amount of Zr is 2000ppm, and the coating amount of Al is 1500ppm;

[0053] Ni 0.35 mn 0.65 (OH) 2 The specific surface area a is 25m 2 / g, the tap density b is 1.55g / cm 3 , which looks like figure 1 The spherical particles shown are spherical particles obtained from flake-like primary particles, with a median particle size of 5.5 μm;

[0054] The specific surface area c of the cobalt-free lithium-rich cathode material is 1.5m 2 / g, the tap density d is 1.7g / cm 3 , which looks like figure 2 The spherical structure shown has a median particle size of 5.5 μm;

[0055] a / c+b / d=17.6.

[0056] The preparation method of the cobalt-free lithium-rich cathode material is as...

Embodiment 2

[0061] This embodiment provides a cobalt-free lithium-rich positive electrode material whose chemical formula is , the positive electrode material through Ni 0.25 mn 0.75 (OH) 2 It is obtained by sintering after compounding with lithium carbonate, wherein the doping amount of Al is 1500ppm, the coating amount of Zr is 2000ppm, and the coating amount of Ti is 2000ppm;

[0062] Ni 0.25 mn 0.75(OH) 2 The specific surface area a is 20m 2 / g, the tap density b is 1.5g / cm 3 ;

[0063] The specific surface area c of the cobalt-free lithium-rich cathode material is 5.0m 2 / g, the tap density d is 1.5g / cm 3 ;

[0064] a / c+b / d=5.

[0065] The preparation method of the cobalt-free lithium-rich cathode material is as follows:

[0066] (1) NiSO 4 ·6H 2 O, MnSO 4 ·H 2 O is formulated into a 2mol / L aqueous solution according to the stoichiometric ratio, NaOH aqueous solution is used as a precipitating agent with a concentration of 4mol / L, and NH 3 ·H 2 O is used as a compl...

Embodiment 3

[0069] This embodiment provides a cobalt-free lithium-rich positive electrode material whose chemical formula is , the positive electrode material through Ni 0.30 mn 0.70 (OH) 2 It is obtained by sintering after compounding with lithium carbonate, wherein the doping amount of Nb is 2500ppm, the coating amount of Mg is 1000ppm, and the coating amount of Ti is 2500ppm;

[0070] Ni 0.30 mn 0.70 (OH) 2 The specific surface area a is 26m 2 / g, the tap density b is 1.4g / cm 3 ;

[0071] The specific surface area c of the cobalt-free lithium-rich cathode material is 1.1m 2 / g, the tap density d is 1.0g / cm 3 ;

[0072] a / c+b / d=25.

[0073] The preparation method of the cobalt-free lithium-rich cathode material is as follows:

[0074] (1) NiSO 4 ·6H 2 O, MnSO 4 ·H 2 O is formulated into a 4mol / L aqueous solution according to the stoichiometric ratio, NaOH aqueous solution is used as a precipitating agent, the concentration is 8mol / L, and NH 3 ·H 2 O is used as a compl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention provides a cobalt -free lithium -rich positive material and its preparation methods and applications.The cobalt -free lithium -rich positive material is obtained by the nickel -manganese hydroxide anterior drive body and lithium source after sintering; wherein the nickel -mangible hydride oxide front drives are satisfied: 17m 2 / g <to the surface area a <27m 2 / G, 1.4g / cm 3 <Zhenshou density B <1.6g / cm 3 ; 2 / g <to the surface area C <5M 2 / g, 1g / cm 3 <2g / cm 3 ; And 5≤a / c+b / d≤25.The present invention regulates the surface area and vibration density of the predetermined body and its front -drive body. At the same time, the relationship between the surface area and the density of the vibration of the premium and its front -wheel drive in the positive pole material is improved.The amplitude of the voltage drop.

Description

technical field [0001] The invention belongs to the technical field of cobalt-free batteries, and relates to a cobalt-free lithium-rich positive electrode material and a preparation method and application thereof. Background technique [0002] Lithium-ion batteries have the advantages of high voltage platform, good cycle performance, no memory effect and high specific energy, and are currently the most widely used power batteries. With the development of smart grid energy storage and the continuous promotion of new energy vehicles, lithium-ion batteries have developed rapidly, and the market's performance requirements for lithium-ion batteries are also getting higher and higher. [0003] The energy density of lithium-ion batteries is mainly determined by the electrode materials, and the current commercial cathode materials (for example, LiCoO 2 、LiFePO 4 and the ternary material Li[Ni 1 / 3 co 1 / 3 mn 1 / 3 ]O 2 (NCM-111) etc.) the actual discharge specific capacity (<18...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/525H01M4/505H01M4/36H01M4/62H01M10/0525C01G53/00C01G45/12
CPCH01M4/525H01M4/505H01M4/366H01M4/628H01M10/0525C01G53/50C01G45/1257H01M2004/021H01M2004/028C01P2006/12C01P2006/11C01P2004/03C01P2006/40C01P2004/82Y02E60/10
Inventor 乔齐齐刘月园王鹏飞施泽涛郭丰李子郯杨红新
Owner SVOLT ENERGY TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap