Nitrate-free environment-friendly steel plate enamel high-temperature acid-resistant ground coat as well as preparation method and application thereof
An environmentally friendly, nitrate technology, applied in the field of enamel, can solve the problems of nitrogen oxide emissions, environmental pollution, etc., and achieve an important environmental protection effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] (1) Weigh the raw materials according to the mass parts of the following components:
[0041] Quartz 53kg, zero-water borax 24kg, soda ash 5.0kg, manganese oxide 1.5kg, nickel oxide 0.8kg, cobalt oxide 0.8kg, calcium carbonate 5.3kg, sodium fluorosilicate 1.0kg, titanium dioxide 3.0kg, potassium feldspar 1.7kg, Lithium carbonate 5.8kg, fluorite 0.8kg.
[0042] SiO in quartz 2 The mass proportion of ≥99.5%, SiO in potassium feldspar 2 The mass proportion of calcium fluoride in fluorite is ≥ 71%, the mass proportion of calcium fluoride in fluorite is ≥ 95%, the mass proportion of titanium dioxide in titanium dioxide is ≥ 99.0%, the mass proportion of Co in cobalt oxide is ≥ 71%, and the mass proportion of Ni in nickel oxide The mass proportion of ≥71%, other raw materials are industrial grade purity.
[0043] (2) Stir and mix the above raw materials evenly.
[0044] (3) Put the uniformly mixed materials into the melting furnace for melting. The melting furnace adopts ...
Embodiment 2
[0048] The preparation process of this example is basically the same as Example 1, except that the mass parts of each component in step (1) are: 53kg of quartz, 24.8kg of zero-water borax, 4.7kg of soda ash, 1.5kg of manganese oxide, and Nickel 0.8kg, cobalt oxide 0.8kg, calcium carbonate 4.4kg, sodium fluorosilicate 1.2kg, titanium dioxide 3.5kg, potassium feldspar 1.4kg, lithium carbonate 5.8kg, fluorite 0.6kg.
[0049] In step (5), the process of rapidly cooling the melted borosilicate glass body is by tableting.
Embodiment 3
[0051] The preparation process of this embodiment is basically the same as that of Example 1, except that the mass parts of each component in step (1) are: 53 kg of quartz, 26 kg of zero-water borax, 4.0 kg of soda ash, 1.5 kg of manganese oxide, and nickel oxide 0.8kg, cobalt oxide 0.8kg, calcium carbonate 4.0kg, sodium fluorosilicate 1.4kg, titanium dioxide 3.0kg, potassium feldspar 1.1kg, lithium carbonate 5.8kg, fluorite 0.4kg.
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap