Preparation method of fiber graphene copper sulfide flexible electrode material

A technology of olefinic copper sulfide and flexible electrodes, which is applied in the manufacture of hybrid capacitor electrodes and hybrid/electric double-layer capacitors, can solve the problems of high production cost, poor flexibility, low durability and environmental dependence, and achieve low cost , the effect of high energy density, high power density

Pending Publication Date: 2022-04-19
江苏润远新能源材料有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Because of its unique two-dimensional layered structure, graphene endows it with a high theoretical specific surface area and ultrafast electron mobility, making it a flexible electrode material; at present, the research and development of flexible electrochemical capacitors and electrode materials has become a International hotspot, there have been a lot of research on how to improve the wearing comfort of wearable energy storage devices and how to improve the electrochemical performance at home and abroad, but the high production cost, poor flexibility, low durability and environmental dependence Sex etc. limit their real application
Carrying new materials and designing new structures are important methods to improve the performance of wearable energy storage devices and improve their environmental adaptability, and textile materials are one of the materials that are very suitable. Textile materials are natural wearable materials, which give people the impression and reality. The application of flexible electrode materials is very comfortable and soft, but due to the particularity of the material and surface properties of textile materials, there are certain shortcomings and problems in the application of flexible electrode material technology. Therefore, we propose a fiber graphene Preparation method of copper sulfide flexible electrode material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of fiber graphene copper sulfide flexible electrode material, the method comprises the following steps:

[0020] One: Select qualified fiber fabrics and graphene, first soak the fiber fabrics in deionized water and ultrasonically wash, take out the fiber fabrics and dry them through the drying device, and then put the fiber fabrics into the homogenizer Stir at a high speed to obtain the fiber slurry, then pour the graphene oxide suspension into the container containing the fiber slurry, and after completion, leave the fiber slurry for 60 minutes;

[0021] Two: Grind and pulverize the selected graphene to obtain graphene powder, then use deionized water and ultrasonically wash to obtain a graphene dispersion, and then pour the graphene dispersion into a container containing fiber slurry, Then stir at a high speed in a homogenizer to fully mix the two, repeat steps 1 and 2 several times to obtain a fiber / graphene oxide material and perform in-situ red...

Embodiment 2

[0032] A preparation method of fiber graphene copper sulfide flexible electrode material, the method comprises the following steps:

[0033] One: Select qualified fiber fabrics and graphene, first soak the fiber fabrics in deionized water and ultrasonically wash, take out the fiber fabrics and dry them through the drying device, and then put the fiber fabrics into the homogenizer Stir at a high speed to obtain the fiber slurry, then pour the graphene oxide suspension into the container containing the fiber slurry, and after completion, leave the fiber slurry for 120 minutes;

[0034] Two: Grind and pulverize the selected graphene to obtain graphene powder, then use deionized water and ultrasonically wash to obtain a graphene dispersion, and then pour the graphene dispersion into a container containing fiber slurry, Then stir at a high speed in a homogenizer to fully mix the two, repeat steps 1 and 2 several times to obtain a fiber / graphene oxide material and perform in-situ re...

Embodiment 3

[0045] A preparation method of fiber graphene copper sulfide flexible electrode material, the method comprises the following steps:

[0046] One: Select qualified fiber fabrics and graphene, first soak the fiber fabrics in deionized water and ultrasonically wash, take out the fiber fabrics and dry them through the drying device, and then put the fiber fabrics into the homogenizer Stir at a high speed to obtain the fiber slurry, then pour the graphene oxide suspension into the container containing the fiber slurry, and after completion, leave the fiber slurry for 180 minutes;

[0047] Two: Grind and pulverize the selected graphene to obtain graphene powder, then use deionized water and ultrasonically wash to obtain a graphene dispersion, and then pour the graphene dispersion into a container containing fiber slurry, Then stir at a high speed in a homogenizer to fully mix the two, repeat steps 1 and 2 several times to obtain a fiber / graphene oxide material and perform in-situ re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a fiber graphene copper sulfide flexible electrode material in the technical field of flexible electrode materials, and the method comprises the steps: selecting qualified fiber fabric and graphene, firstly, soaking the fiber fabric in deionized water, carrying out ultrasonic washing, then taking out the fiber fabric, and carrying out drying through a drying device; pouring the graphene oxide suspension into a container filled with the fiber slurry, and standing the fiber slurry for 60-180 minutes after the graphene oxide suspension is poured into the container filled with the fiber slurry; therefore, the prepared fiber / graphene material exerts a synergistic effect, the excellent mechanical property of flexibility of the fiber material is reserved, meanwhile, the excellent conductivity of graphene is reserved, meanwhile, more reaction active points are provided for pseudocapacitance redox reaction of the fiber / graphene material through the added nickel salt solution, copper salt and sulfur-containing precursor solution, and the conductivity of the fiber / graphene material is improved. Therefore, the prepared electrode material is light in weight, soft, excellent in cycle performance, simple in manufacturing process, easy to operate and good in durability.

Description

technical field [0001] The invention relates to the technical field of flexible electrode materials, in particular to a method for preparing a fiber graphene copper sulfide flexible electrode material. Background technique [0002] Because of its unique two-dimensional layered structure, graphene endows it with a high theoretical specific surface area and ultrafast electron mobility, making it a flexible electrode material; at present, the research and development of flexible electrochemical capacitors and electrode materials has become a International hotspot, there have been a lot of research on how to improve the wearing comfort of wearable energy storage devices and how to improve the electrochemical performance at home and abroad, but the high production cost, poor flexibility, low durability and environmental dependence Sex etc. limit their real application. Carrying new materials and designing new structures are important methods to improve the performance of wearabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G11/86H01G11/24H01G11/30H01G11/32
CPCH01G11/86H01G11/24H01G11/30H01G11/32Y02E60/13
Inventor 冯双龙
Owner 江苏润远新能源材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products