High-performance lithium-calcium-tantalum-nickel-zinc-niobium-magnesium-tungsten modified PZT piezoelectric ceramic prepared at low temperature

A piezoelectric ceramic, high-performance technology, applied in the field of piezoelectric ceramic materials, can solve the problems of ceramic electrical performance deterioration, affecting the reliability of multi-layer devices, etc., to achieve the effect of improving crystal grains, good piezoelectric performance, and low sintering temperature

Pending Publication Date: 2022-06-21
SICHUAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional PZT modified piezoelectric ceramics are sintered at a high temperature of about 1200°C, so the internal electrodes cannot use pure Ag (melting point ≈961°C) at such a high temperature, and the Ag-Pd electrode layer will also diffuse into the ceramic layer, resulting in ceramic Deterioration of electrical properties, thereby affecting the reliability of multilayer devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance lithium-calcium-tantalum-nickel-zinc-niobium-magnesium-tungsten modified PZT piezoelectric ceramic prepared at low temperature
  • High-performance lithium-calcium-tantalum-nickel-zinc-niobium-magnesium-tungsten modified PZT piezoelectric ceramic prepared at low temperature
  • High-performance lithium-calcium-tantalum-nickel-zinc-niobium-magnesium-tungsten modified PZT piezoelectric ceramic prepared at low temperature

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 6

[0029] The XRD pattern of the high-performance PZT modified piezoelectric ceramics prepared at low temperature is shown in figure 1 , figure 1 It shows that the PZT modified piezoelectric ceramic is a pure perovskite phase; the ZJ-3 quasi-static d 33 meter, the measured piezoelectric coefficient d 33 See figure 2 , is 570pC / N; use Agilent 4980A precision impedance meter to connect temperature control furnace to measure the change of dielectric constant with temperature, which can be obtained from image 3 The Curie temperature of the obtained sample was 299°C.

[0030] Example 7

[0031] Example 8

Embodiment 2

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Piezoelectric coefficientaaaaaaaaaa
Curie temperatureaaaaaaaaaa
Piezoelectric coefficientaaaaaaaaaa
Login to View More

Abstract

The general formula of the piezoelectric ceramic is Pb1-x-yLixCayTauu [(Ni, Zn) 1 / 3Nb2 / 3] v (Mg1 / 2W1 / 2) w (Ti, Zr) 1-u-v-wO3, 0.001 < = x < = 0.005, 0.001 < = y < = 0.005, 0 < = u < = 0.005, 0.01 < = v < = 0.05, and 0.01 < = w < = 0.05. PZT modified piezoelectric ceramic powder sintered at the low temperature of 850-950 DEG C is prepared by adopting a solid-phase reaction method, and then the ceramic material is prepared through the processes of granulation, tabletting, glue discharging, sintering, silver firing, polarization and the like. The result shows that the PZT modified ceramic material prepared at the sintering temperature of 850-950 DEG C is compact in crystal grain, uniform in crystal grain, sufficient in crystallization and obvious in liquid-phase sintering characteristic, and the piezoelectric property is greatly improved.

Description

technical field [0001] The field of the invention belongs to the field of piezoelectric ceramic materials, in particular to a high-performance lithium-calcium-tantalum-nickel-zinc-niobium-magnesium-tungsten modified PZT piezoelectric ceramic prepared at low temperature. Background technique [0002] PZT is a traditional piezoelectric ceramic, which has good dielectric, ferroelectric, piezoelectric, pyroelectric and other effects. Its raw material is cheap and suitable for factory production. It can be modified to obtain ceramics suitable for various purposes. Material. Multilayer piezoelectric ceramics have alternating ceramic layers and inner metal electrode layers. With the rapid development of science and technology, multilayer piezoelectric ceramics have been studied more and more widely, and are widely used in brakes, converters, and sensors. Generally, Ag-Pd electrodes are used for the internal electrodes of multilayer ceramics, and the co-firing temperature ranges f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/493C04B35/622
CPCC04B35/493C04B35/622C04B2235/3203C04B2235/3208C04B2235/3255C04B2235/3279C04B2235/3251C04B2235/3206C04B2235/326C04B2235/3284
Inventor 刘洪陈浩朱建国
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com