Method for preparing electric arc spraying fiber material containing core of nano material

A nanomaterial, arc spraying technology, applied in arc spraying, metal material coating process, welding/cutting medium/material, etc., can solve the problems of reducing the thickness of the pipe wall, bursting, affecting the thermal efficiency, etc., and achieve anti-oxidation performance. The effect of improving, high bonding strength of coating and wide application prospect

Inactive Publication Date: 2006-05-31
ZHEJIANG UNIV +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to high-temperature erosion and wear of fly ash and high-temperature corrosion of flue gas, the boiler pipes of coal-fired power plants have reduced the wall thickness of the "four pipes" (water wall pipes, superheater pipes, reheater pipes, and economizer pipes). Small, a pipe burst accident occurred, causing huge losses to the power plant
Traditional methods, such as adding welding angle iron, anti-wear tile protection or directly replacing the pipe, not only seriously affect the thermal efficiency, but also uneconomical, and the effect of anti-wear and anti-corrosion is not good
Spraying common drug core wire, the effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The sprayed coating formed by the supersonic arc spraying of the core wire made according to the above specifications on the steel substrate workpiece has the following characteristic effects:

[0026] 1. The weight ratio of drug core powder to the forming wire is 38%.

[0027] 2. The bonding strength is above 48MPa.

[0028] 3. HRC is greater than 55.

[0029] 4. With high hardness and good wear resistance, it is mainly suitable for the "four tubes" of coal-fired power plant boilers to resist high temperature erosion and wear.

Embodiment 2

[0032] The sprayed coating formed by the supersonic arc spraying of the core wire made according to the above specifications on the steel substrate workpiece has the following characteristic effects:

[0033] 1. The weight ratio of drug core powder to forming wire is 40%.

[0034] 2. The bonding strength is above 50MPa.

[0035] 3. HRC is greater than 45.

[0036] 4. High-temperature corrosion resistance and high-temperature oxidation resistance are strong, and it is mainly suitable for the "four tubes" of coal-fired power plant boilers to prevent high-temperature corrosion and oxidation.

Embodiment 3

[0039] The sprayed coating formed by the supersonic arc spraying of the core wire made according to the above specifications on the steel substrate workpiece has the following characteristic effects:

[0040] 1. The weight ratio of drug core powder to the forming wire is 42%.

[0041] 2. The bonding strength is above 50MPa.

[0042] 3. HRC is greater than 52.

[0043] 4. It has high hardness, certain wear resistance, high temperature corrosion resistance and high temperature oxidation resistance. It is mainly suitable for anti-wear, corrosion and oxidation of the "four tubes" of coal-fired power plant boilers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an electric arc spraying wire material containing a nanomaterial medicine core. The drug core is a composite powder containing nanometer materials, and its outer cladding is any one of carbon steel strip, chrome steel strip, stainless steel strip, nickel strip, and aluminum strip. After being sprayed with the drug core wire material containing nanometer material of the present invention, the coating bonding strength is high, and the wear resistance, corrosion resistance and oxidation resistance are greatly improved. This kind of wire can be widely used in coal-fired power plant boiler pipes, chemical equipment parts, mechanical parts, molds and other fields, and has broad application prospects in repairing worn parts and surface treatment of parts.

Description

technical field [0001] The invention relates to the processing or treatment of wires, in particular to a method for preparing electric arc spraying wires containing nanomaterial drug cores. Background technique [0002] Due to high-temperature erosion and wear of fly ash and high-temperature corrosion of flue gas, the boiler pipes of coal-fired power plants have reduced the wall thickness of the "four pipes" (water wall pipes, superheater pipes, reheater pipes, and economizer pipes). Small, a pipe burst accident occurred, causing huge losses to the power plant. Traditional methods, such as adding welding angle iron, anti-wear tile protection or directly replacing the pipe, not only seriously affect the thermal efficiency, but also uneconomical, and the anti-wear and anti-corrosion effect is not good. Spraying common drug core wire material, the effect is also unsatisfactory. Contents of the invention [0003] The purpose of the present invention is to provide a method fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/40B23K35/22C23C4/04B05B5/06
Inventor 刘少光温黎张升才李志章
Owner ZHEJIANG UNIV