Super high molecular mass polythylene/carbon nano tube composite fiber used in jelly glue spinning and its preparation

A composite technology of ultra-high molecular weight and carbon nanotubes, applied in the direction of single-component polyolefin artificial filaments, etc., can solve the problems of unsmooth processing and decreased fiber strength, and achieve simple implementation methods, simple equipment, and no damage small effect

Inactive Publication Date: 2003-07-23
DONGHUA UNIV
View PDF0 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For fiber materials, after the composite material obtained by intercalation is spun, nanoparticles may cause many defects in it, forming stress concentration points, reducing the strength of the fiber, and even making the processing process unable to proceed smoothly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Immerse 2g of carbon nanotubes in a mixed solution of 100ml of sulfuric acid and potassium permanganate, and treat it at reflux temperature for 1.5 hours, the concentration of potassium permanganate in sulfuric acid is 5g / 100ml; mix 2g of purified carbon nanotubes with titanium Butyl acid ester coupling agent was refluxed in ethanol for 2 hours to obtain carbon tubes grafted by coupling agent; the concentration of titanate coupling agent in ethanol was 0.03g / ml;

[0029] Heating range (°C)

0～100

100～110

110～120

120～130

130～180

Holding time (min)

10

30

30

30～60

120

[0030] (3) Gel spinning: the fully dissolved UHMWPE / carbon nanotube composite solution is spun by a conventional gel spinning method to obtain the fiber of the present invention.

[0031] The spinning temperature of the gel spinning method is 130° C., and the prepared gel filament is extracted and drawn three times to obtain the fiber of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A gel-spinning ultrahigh-molecular-weight composite polyethene (UHMWPE)/carbon nanotube fibre is composed of UHMWPE and carbon nanotubes (0.01-5 wt.%) as modifier. It is prepared through purifying and organizing carbon nanotubes, preparing gel, and spinning. Its advantages are simple preparing process and high refractory and anticreep performance.

Description

technical field [0001] The invention relates to a jelly spun ultrahigh molecular weight polyethylene / carbon nanotube composite fiber and a preparation method thereof. The composite fiber is processed from a blend solution of treated carbon nanotubes and ultra-high molecular weight polyethylene through a gel spinning process, and belongs to the technical field of high-performance fibers. Background technique [0002] As we all know, ultra-high molecular weight polyethylene (UHWMPE) fiber is made of ultra-high molecular weight polyethylene as raw material, and is produced through processes such as solvent dissolution, quenching, spun jelly yarn, extraction, drying, and segmental thermal super-stretching. A novel special fiber. This fiber has excellent properties such as light weight, high strength, high modulus, UV resistance, impact resistance, seawater corrosion resistance, and electrical insulation. It has broad application prospects in military, aviation, aerospace, marin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/46
Inventor 王依民倪建华潘湘庆邹黎明王燕萍
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap