Composition for producing synthetic timber and its prepn process

The technology of a composition and wood powder is applied in the field of compositions for producing synthetic wood, and can solve the problems of inability to plan, saw, damage the surface wood grain decoration, etc., and achieve the effects of saving manpower, long shelf life and simple equipment requirements.

Inactive Publication Date: 2003-07-30
常怀春
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some preparation methods of synthetic wood are disclosed in the prior art (such as US.6,066,367 and US.5,869,138), but there are many defects in these methods, such as the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0011] The preparation method of the pellet composition of the present invention comprises the following steps: firstly, any one of PVC resin and wood powder, fruit shell powder, crop stalk powder or waste paper powder or their mixture is put into the hot mixing machine as the first feeding. Mix uniformly in the machine at low speed at 50°C; then put the stabilizer, internal lubricant, filler, and colorant into the heat mixer as the second feeding, and mix uniformly at 100-110°C at high speed; then put the impact modified Agents, processing aids, foaming agents, and external lubricants are put into the heat mixer as the third feeding, and mixed evenly at a high speed of 110-125°C. Put the hot-mixed raw materials into the cold mixer and lower the temperature to below 40°C to obtain the powder composition. The apparent density of the raw materials after thermal mixing increases, and some parts or edges of the materials have become transparent or translucent, that is, partially m...

Embodiment 1

[0016] 10 kg of PVC, 13 kg of wood powder (average particle size 140 mesh), 0.9 kg of CPE, 0.3 kg of ACR, 0.3 kg of tribasic lead sulfate, 0.2 kg of dibasic lead phosphite, 0.2 kg of lead stearate, hard 0.1 kg of barium stearate, 0.5 kg of calcium stearate, 0.1 kg of paraffin, 0.3 kg of azodicarbonamide, 1 kg of calcium carbonate, and 0.03 kg of sunfast yellow were prepared into granular or powder compositions according to the aforementioned preparation method.

Embodiment 2

[0018] 10 kg of PVC, 14 kg of wood powder (average particle size 140 mesh), 0.6 kg of ABS, 0.1 kg of ACR, 0.2 kg of dibutyltin mercaptide, 0.1 kg of calcium stearate, 0.1 kg of PE wax, azodicarbonamide 0.2 kg, 0.1 kg of sodium bicarbonate, 0.5 kg of calcium carbonate, 0.04 kg of medium chrome yellow, and 0.004 kg of red, made into granular or powdered compositions according to the aforementioned preparation method.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

A composition for producing synthetic timber includes polyvinyl chloride resin; wood dust, nut shell powder, crop straw powder, waste paper powder or their mixture; and at least one of chlorinated polyethylene, acrylonitrile-butadiene-styrene polymer and methyl methacrylate-butadiene-styrene polymer as impact modifier. The materials in certain weight ratio are produced into granulated material through mixing, extrusion and pelletizing; or produced into powdered material through thrice mixing. The said composition can be used for producing synthetic timber with the grains and other characteristics simmilar to natural timber for use in building.

Description

Technical field [0001] The present invention relates to a composition for the manufacture of synthetic wood and a method for its preparation. Background technique [0002] In order to meet the needs of human production and life, people cut down a lot of wood, causing serious damage to forest resources and great damage to the natural ecological environment. For the benefit of future generations, people are developing various materials to replace natural wood to reduce human dependence on natural wood. However, due to the existing natural wood substitutes, there are many defects, such as not having the texture and texture of natural wood, and cannot be processed according to natural wood, so it cannot meet the consumer demand that people favor wood products. As an improvement, people began to develop wood-like plastics, so-called synthetic wood. Some preparation methods of synthetic wood are disclosed in the prior art (such as US.6,066,367 and US.5,869,138), but there are ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L97/02
Inventor 常怀春
Owner 常怀春
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap