Ultraviolet light cured paint for leather or leatherette

A technology for curing coatings and artificial leather, applied in polyurea/polyurethane coatings, coatings, devices for coating liquids on surfaces, etc. High efficiency, good durability, high gloss effect

Inactive Publication Date: 2003-08-20
湖南亚大新材料科技股份有限公司
View PDF2 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But no matter which of the above-mentioned treatment technologies, there are low solid content and long drying time. If heated and baked, it will easily deform or even damage the leather or artificial leather material; the solvent resistance, alkali resistance and abrasion resistance of the coating have yet to be determined. improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Aliphatic urethane acrylate 30wt%

[0033] Acrylic modified epoxy resin 15wt%

[0034] TPGDA 19.7wt%

[0035] EHA 15wt%

[0036] Irgacur 2959 5wt%

[0037] BYK 333 0.5wt%

[0038] BYK 920 1wt%

[0039] BYK306 0.3wt%

[0040] BYK 055 0.5wt%

[0041] Ethylene glycol ether acetate 8wt%

[0042] Isopropanol 5wt%

[0043] (1). Mix aliphatic urethane acrylate, acrylic modified epoxy resin, reactive acrylate monomer and photoinitiator, heat up to 50-60°C, and stir evenly;

[0044] (2). Then add leveling agent, defoamer, wetting agent, wear-resistant agent to step (1), and stir until fully dissolved;

[0045] (3). Then add a solvent to step (2), stir, cool down, and filter to obtain a UV-curable coating for leather or artificial leather.

Embodiment 2

[0047] Aliphatic urethane acrylate 30

[0048] Acrylic modified epoxy resin 5

[0049] EO-TMPTA 10

[0050] PO-TMPTA 20

[0051] MHEA 10

[0052] EHA 5

[0053] Irgacur 2959 3

[0054] Irgacur 184 2

[0055] BYK 920 3

[0056] BYK 141 0.3

[0057] BYK 055 0.2

[0058] EFKA 3777 1

[0059] BYK333 0.5

[0060] Ethylene glycol ether acetate 10

[0061] The above is proportioned by weight percentage, and mixed evenly according to the steps of Example 1.

Embodiment 3

[0063] Aliphatic Cluster Urethane Acrylate 40

[0064] Acrylic modified epoxy resin 3

[0065] PETA 5

[0066] PO-TMPTA 15

[0067] TPGDA 15

[0068] EHA 5

[0069] Irgacur 369 5

[0070] BYK 333 0.5

[0071] BYK 052 0.5

[0072] BYK 354 0.5

[0073] EFKA 3035 0.5

[0074] BYK 920 2

[0075] Butyl acetate 8

[0076] The above is proportioned by weight percentage, and mixed evenly according to the steps of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is ultraviolet light cured paint for leather and leatherette. The ultraviolet light cured paint consists of: aliphatic polyuretheane acrylic ester 25-50 wt%, acrylic acid modified epoxy resin 0-20 wt%, reactive acrylic ester monomer 10-50 wt%, light initiator 5 wt%, leveling agent 0.3-1 wt%, defoaming agent 0.1-0.5 wt%, wetting agent 0.5-1.5 wt%, wear-resistant agent 0.5-3 wt% and solvent 2-20 wt%. The ultraviolet light cured paint for leather and leatherette of the present invention is white or milk white colloid liquid, has solid content of 80-98%, may be stored at room temperature and lightproof condition for one year, and has the features of curing at normal temperature, high production efficiency, forming film with excellent flexibility, high luster degree, high wear resistance, high corrosion resistance and high durability, etc.

Description

technical field [0001] The invention belongs to the coating for treating the surface of leather or artificial leather, in particular to an ultraviolet curing coating for leather or artificial leather. Background technique [0002] Traditional leather or artificial leather surface treatment as described in Chinese application number CN 85102368 is a class of monomers such as acrylate, chloroprene, acrylonitrile, styrene and acrylic acid copolymerized to make emulsion, and then by roller coating or It is sprayed on the surface of leather or artificial leather to treat it; another kind, as described in US Pat. But no matter which of the above-mentioned treatment technologies, there are low solid content and long drying time. If heated and baked, it will easily deform or even damage the leather or artificial leather material; the solvent resistance, alkali resistance and abrasion resistance of the coating have yet to be determined. improve. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/12C09D175/16
Inventor 谭昊涯胡辉伍松
Owner 湖南亚大新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More