Preparing method of low-cost oxide ceramic shell for titanium alloy precision casting

A technology of oxide ceramics and precision casting, which is applied in the direction of casting molding equipment, casting molds, and casting mold components, and can solve problems that affect the mass production and application of titanium alloy investment casting precision casting, expensive prices, and high production costs of titanium alloys.

Inactive Publication Date: 2005-02-23
HARBIN INST OF TECH
View PDF0 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to ZrO 2 , Y 2 o 3 Raw materials such as surface layer materials, yttrium sol, zirconium sol, zirconium diacetate and zirconium organic compounds are expensive, res

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0004] The steps of this embodiment are as follows: 1. Preparation of the surface coating: add corundum powder with a finely graded particle size into the binder, stir while adding, and stir for 1 hour after adding all the corundum powder. The viscosity of the paint is controlled at 80-100s (Tu-4 viscometer); 2. Preparation of the shell: After the paint is prepared, immerse the wax pattern of the casting in the paint for 10-20 minutes and take it out. When the remaining paint on the wax pattern flows When it is uniform and no longer drips continuously, the freezing starts, and the sand can be sprinkled. The fused white corundum powder that has undergone particle size grading is evenly sprinkled on the wax pattern coated with paint. The sanding should be even and comprehensive. Then paint and sand on this basis. After each layer of paint and sand, it must be fully dried and hardened; 3. Dewaxing of the shell: put the dried wax mold coated with surface coating Put it into a high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

A low-cost oxide ceramic mould for the precise casting of Ti-alloy is prepared through preparing paint and wax mould of casting, immersing the wax mould in paint for 10-20 min, leveling the paint, uniformly applying the white electro-corundum powder to the paint layer of wax mould, drying, and high-pressure dewaxing.

Description

Technical field: [0001] The invention relates to a preparation process of an oxide ceramic mold shell used for investment precision casting of titanium alloy. Background technique: [0002] With the development of science and technology, the application of titanium alloys is becoming more and more extensive. From rockets and aircraft in the aerospace industry to artificial joints in the medical field, as well as in navigation, chemical industry, sports, etc., titanium alloys are famous for their excellent properties. Popular for performance. It has the characteristics of high specific strength, high specific stiffness, good corrosion resistance, and strong heat resistance, making titanium alloy one of the most promising modern structural materials. However, titanium is a very active metal element, especially at high temperature, it is easy to chemically react with other elements. The molten titanium liquid has chemical reactions with almost all refractory materials to vary...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C9/04
Inventor 陈玉勇田竟王惠光陈子勇肖树龙
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap