Process for preparing water soluble epoxy resin grouting agent
A technology for water-based epoxy resin and grouting material, which is applied in the field of preparation of new water-based epoxy resin grouting materials, can solve the problems of poor epoxy curing, and no water-based epoxy resin grouting material has been developed, and is beneficial to environmental protection and durable. The effect of good performance and cost reduction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0049] Example 1:
[0050] 1. Synthesis of water-based epoxy resin
[0051]Add 93g itaconic acid and 24g n-butanol into a four-neck flask equipped with nitrogen, stirring and temperature control device, heat to 90℃, add 0.88g benzyltriethylammonium chloride and 0.22g p-hydroxybenzene Methyl ether, add 147g epoxy resin E-44 dropwise, keep the temperature between 90-94°C, drop it in 2h, then control the temperature at 100-110°C, and react for 3h.
[0052] Cool down to 50°C, add 60g ammonia water for neutralization, fully stir for 1.5h, then add 101.6g deionized water, and then vigorously stir for 1h to prepare an aqueous epoxy resin solution with a concentration of 60%.
[0053] 2. Preparation of water-based epoxy resin grouting material
[0054] Take 100g of the aqueous epoxy resin solution prepared in the above steps, add 39g of water, 5g of N,N'-methylenebisacrylamide, 4.5g of ammonium persulfate, 4.5g of triethanolamine, 4.5g of methacryloxyethyl three 11g of methyl ammonium chl...
Example Embodiment
[0056] Example 2:
[0057] 1. Synthesis of water-based epoxy resin
[0058] Add 89g itaconic acid and 32g ethylene glycol monobutyl ether into a four-neck flask equipped with nitrogen, stirring and temperature control device, heat to 90°C, add 0.8g tetraethylammonium chloride and 0.21g p-benzene Diphenol, add 127g epoxy resin E-51 dropwise, keep the temperature between 92-96°C and finish dropping within 1.5h, then control the temperature at 100-110°C, and react for 3h.
[0059] The temperature was lowered to 40° C., 52 g of ammonia water was added for neutralization, and the mixture was fully stirred for 1.5 hours, and then 81.8 g of deionized water was added, followed by vigorous stirring for 1 hour to prepare an aqueous epoxy resin solution with a concentration of 60%.
[0060] 2. Preparation of water-based epoxy resin grouting material
[0061] Take 100g of the aqueous epoxy resin solution prepared in the above steps, add 85g of water, 5g of N,N'-methylenebisacrylamide, 5g of p...
Example Embodiment
[0063] Example 3:
[0064] 1. Synthesis of water-based epoxy resin
[0065] In a four-neck flask equipped with nitrogen, stirring and temperature control device, add 93g itaconic acid and 22g cyclohexanone, heat to 90℃, add 0.86g tetraethylammonium chloride and 0.24g p-butyl phthalate Phenol, add 127g epoxy resin E-51 dropwise, keep the temperature between 90-96°C, drop it in 1.5h, then control the temperature at 100-110°C, and then react for 4h.
[0066] Cool down to 40°C, add 70g of dimethylethanolamine for neutralization, fully stir for 1.5h, then add 171.3g of deionized water, and then vigorously stir for 1h to prepare an aqueous epoxy resin solution with a concentration of 60%.
[0067] 2. Preparation of water-based epoxy resin slurry
[0068] Take 100g of the aqueous epoxy resin solution prepared in the above steps, add 119.7g of water, 4.8g of N,N'-methylenebisacrylamide, 4.5g of ammonium persulfate, 4.5g of triethanolamine, and methacryloxy ethyl 11g of methyl trimethyl am...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Bond strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap