Polyvinyl chloride hot-dipping plastic compounded product, and its production and use
A polyvinyl chloride and preparation technology, applied in the field of chemical treatment or coating, can solve the problems of easy corrosion of galvanized pipes, health hazards of construction workers, and environmental pollution, and achieve the effects of low cost, good waterproof performance, and easy construction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] a, get 1kg carbon black according to formula and soak in 3kg dioctyl phthalate (DOP) for 12 hours, stir evenly, grind into paste with colloidal mill, form charcoal paste through 100 mesh filtration;
[0027] B, after getting 1kg of vapor-phase method white carbon black in 8kg dioctyl phthalate (DOP) and stirring evenly, grind into a paste with a colloid mill;
[0028] c. Combine a+b and the remaining 19kg DOP with 50kg PVC resin powder (PHS-10), 3.2kg epoxy soybean oil (ESC), 7kg dioctyl sebacate (DCS), 2.5kg stabilizer (TiQ3), Put 0.8kg of flame retardant (PEG) and 2.5kg of diisodecyl adipate (DIDA) together into a mixing tank and stir for 0.5-1 hour, then filter with a 100-mesh filter;
[0029] d. Add 2kg of viscosity reducer and stir evenly with a mixer to reach the specified viscosity;
[0030] e. Put the colloid with adjusted viscosity into a vacuum barrel, vacuumize it to 0.07Mpa with a vacuum pump, let it rest for at least two hours, then press back, and put it ...
Embodiment 2
[0032] a, get 0.2kg carbon black according to formula and soak in 0.6kg dioctyl phthalate (DOP) for 10 hours, stir evenly, grind into paste with colloid mill, form charcoal paste through 100 mesh filtration;
[0033] B, after getting 0.2kg of vapor-phase method white carbon black in 1.6kg dioctyl phthalate (DOP) and stirring evenly, grind into paste with colloidal mill;
[0034] c. Combine a+b, the remaining 23.8kg DOP with 60kg PVC resin powder (PHS-10), 2kg epoxy soybean oil (ESC), 5kg dioctyl sebacate (DCS), 1kg stabilizer (TiQ3), 0.6 kg of flame retardant (PEG) and 2 kg of diisodecyl adipate (DIDA) were put into a mixing tank together and stirred for 0.5 hours, then filtered through a 100-mesh filter;
[0035] d. Add 3kg of viscosity reducer to adjust the viscosity, evacuate and let it stand for back pressure loading.
Embodiment 3
[0037] a. Take 0.28kg carbon black according to the formula and soak in 0.84kgDOP for 13 hours, stir evenly, grind into a paste with a colloid mill, and filter through 100 mesh to form a charcoal paste;
[0038] B, after getting 0.28kg of vapor-phase method white carbon black in 2.24kg dioctyl phthalate (DOP) and stirring evenly, grind into paste with colloid mill;
[0039] c, combine a+b, remaining 25.18kg DOP with 56.5kg PVC resin powder (PHS-10), 2.83kg epoxy soybean oil (ESC), 5.65kg dioctyl sebacate (DCS), 1.69kg stabilizer ( TiQ 3 ), 0.56kg of flame retardant (PEG), and 1.69kg of diisodecyl adipate (DIDA) were put into the mixing tank together and stirred for 1 hour, then filtered with a 100-mesh filter;
[0040] d. Add 2.26kg of viscosity reducing agent and stir evenly with a mixer to reach the specified viscosity;
[0041] e. Put the colloid with adjusted viscosity into a vacuum barrel, vacuumize it to 0.07Mpa with a vacuum pump, let it rest for at least two hours, t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.