Porous high oil adsorption resin and its preparation method

A technology of oleoresin and porosity, which is applied in the field of porous high oil-absorbing resin and its preparation, can solve the problems that there is no industrialization report, and the oil absorption rate and oil absorption ratio of high oil-absorbing resin cannot meet the requirements at the same time, so as to avoid secondary Pollution, high absorption rate, good selectivity effect

Inactive Publication Date: 2006-01-25
SUZHOU TIMEBLUE ENVIRONMENTAL TECH CO LTD
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high oil-absorbing resins obtained by these methods often cannot meet the requirements on oil absorp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous high oil adsorption resin and its preparation method
  • Porous high oil adsorption resin and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add dispersant gelatin to water to prepare 0.3-5.0% aqueous solution, stir at 30--50°C to dissolve and cool. Then add 20---30 parts of butyl methacrylate, 70---80 parts of 2-ethylhexyl acrylate and 0.1%-0.6% of the total monomer amount of 1,4-butanediacrylate under stirring. Alcohol ester, benzoyl peroxide with 0.5%-1.6% of the total amount of monomers and carbon tetrachloride as a solvent, are heated up while stirring under the protection of nitrogen, and when the temperature reaches 70-100°C, the polymerization reaction starts. The reaction was maintained at this temperature for 5-7 hours. After the reaction is completed, the product is cooled, filtered, washed several times with hot water at 60-80°C, extracted with methanol as the solvent carbon tetrachloride, and dried in an oven at 50-70°C to obtain a porous super oil-absorbing resin.

[0024] The primary oil absorption rate (g / g) of the resin: 25 for benzene and 16 for cyclohexane; oil retention rate of 90%, oil ...

Embodiment 2

[0026] Add dispersant gelatin to water to prepare 0.3-5.0% aqueous solution, stir at 30--50°C to dissolve and cool. Then add 20---30 parts of butyl methacrylate, 70---80 parts of butyl acrylate, 0.1%--0.6% of the total amount of monomers, 1,4-butylene glycol diacrylate, mono 0.5%-1.6% of the total amount of benzoyl peroxide and ethyl acetate as a solvent, and the temperature is raised while stirring under the protection of nitrogen. When the temperature reaches 70-100°C, the polymerization reaction starts. The reaction was maintained at this temperature for 5-7 hours. After the reaction is completed, the product is cooled, filtered, washed several times with hot water at 60-80°C, extracted with methanol as the solvent ethyl acetate, and dried in an oven at 50-70°C to obtain a porous super oil-absorbing resin.

[0027] The primary oil absorption rate (g / g) of the resin: 25 for benzene and 15 for cyclohexane; the oil retention rate is 89%, and the oil absorption speed (time to ...

Embodiment 3

[0029] Add dispersant gelatin to water to prepare 0.3-5.0% aqueous solution, stir at 30--50°C to dissolve and cool. Then add 20---30 parts of isobutyl methacrylate, 70---80 parts of 2-ethylhexyl acrylate and 0.1%--0.6% of the total monomer amount of 1,4-butyl diacrylate under stirring. Glycol ester, benzoyl peroxide with 0.5%-1.6% of the total amount of monomers and toluene as a solvent, are heated up while stirring under nitrogen protection, and the polymerization reaction starts when the temperature reaches 70-100°C. The reaction was maintained at this temperature for 5-7 hours. After the reaction is completed, the product is cooled, filtered, washed several times with hot water at 60-80°C, extracted with methanol as the solvent toluene, and dried in an oven at 50-70°C to obtain a porous super oil-absorbing resin.

[0030] The primary oil absorption rate (g / g) of the resin: 21 for benzene and 12 for cyclohexane; the oil retention rate is 89%, and the oil absorption speed (t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a sewage treatment agent that uses methacrylic acid long chain ester and crylic acid short chain ester as monomer, and water as disperse phase, and adds dispersing agent, initiator agent, crosslink agent and organic solvent. The method is that: adding dispersing agent into water to make 0.3-5.0% aqueous solution and whisking under 30-50 degree centigrade for cooling; adding the mixture of 24-34% methacrylic acid long chain ester, 65-75%crylic acid short chain, 0.1-0.6% crosslink agent, and 0.5-1.6% initiator agent while whisking; under the protection of nitrogen gas, rising the temperature until reaching 70-100degree centigrade, the polymerization beginning and lasting for 7-9 hours; after reaction, cooling and filtrating the production, washing several times by 50-70 degree centigrade hot water, excerpting by methanol, putting into bake oven for baking, then the porosity high oil absorption rosin. It has high blotter scale factor and high blotter efficiency. Moreover, it could be used repeatedly, thus the secondary pollution would be avoided.

Description

technical field [0001] The invention relates to a sewage treatment agent, in particular to a porous high-oil-absorbing resin and a preparation method thereof. The oil-absorbing ratio and oil-absorbing efficiency are high, and the resin can be used repeatedly, avoiding secondary pollution, and the cost is low. Background technique [0002] With the development of my country's chemical industry, the environmental pollution caused by oily sewage, waste liquid and industrial accidents such as the leakage of oil tankers is becoming more and more serious. In organic wastewater, benzene, toluene and cyclohexane are commonly used organic solvents account for a large proportion. At present The common way to recover these oily solvents is to use oil-absorbing materials, but traditional oil-absorbing materials mainly use the capillary action of the surface, gap and cavity of the material to absorb oil, which has the characteristics of not only absorbing oil but also absorbing water, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/10C02F1/56
Inventor 路建美纪顺俊
Owner SUZHOU TIMEBLUE ENVIRONMENTAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap