Novel coating material for ink jetting medium and its preparation method

A coating material, inkjet printing technology, applied in the direction of copying/marking method, printing, pigmented coating, etc., to achieve high whiteness, excellent control, and good coating leveling

Inactive Publication Date: 2006-07-12
四川新泰克控股有限责任公司
View PDF11 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In the past, calcium carbonate was only used as a paper additive and as a coating material for individual light-coated paper (such as cigarette paper). At present, there is no calcium carbonate to replace ultrafine silic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] The preparation method of the coating material of inkjet printing medium of the present invention:

[0037] First prepare PVA solution; then disperse calcium carbonate: Weigh a certain amount of deionized water, add fine-grained inorganic pigments and dispersants to the water, stir, first pre-disperse, and then shear and disperse to obtain pigments Slurry; then mix the slurry with PVA solution and other adhesives, add color fixing agent, surfactant, crosslinking agent, and prepare coating liquid; finally, coat the coating liquid on the paper base and dry , to obtain an inkjet printing medium.

Example Embodiment

[0039] Embodiment 1 Preparation of the coating material of the inkjet printing medium of the present invention

[0040] (The following formulas are designed according to the one-time coating method, and the proportion of each component of the formula is calculated according to the net weight of the solid content (dry matter).

[0041] Ground calcium carbonate 100g

[0042] (according to D97, the particle size is 1.9μm, and the specific surface area is 20000cm 2 / g, particle shape is cylindrical)

[0043] Sodium hexametaphosphate 0.5g

[0044] Adhesive PVA (polymerization degree 2000) 9g

[0045] Fixing agent SH-D 5g

[0046] Cross-linking agent Melamine 0.5g

[0047] Brightener BBN 1.26g

[0048] Deionized water 134g

[0049] operate:

[0050] Weigh 54g of deionized water, add it into a stainless steel bucket, then sprinkle 9g of PVA into the water under stirring, continue stirring for 1 hour, start to heat up to 93°C, maintain for 1 hour, cool down to room temperature...

Example Embodiment

[0051] Embodiment 2 Preparation of the coating material of the inkjet printing medium of the present invention

[0052] Light calcium carbonate 100g

[0053] (according to D97, the particle size is 0.6--0.9μm, and the specific surface area is 9--15m 2 / g, the particle shape is chrysanthemum shape)

[0054] Dispersant sodium hexametaphosphate 1g

[0055] Adhesive PVA (polymerization degree 1700) 18g

[0056] Fixing agent SH-D 4g

[0057] Fixing agent NFC 1g

[0058] Cross-linking agent Melamine 0.5g

[0059] Brightener BBN 1.26g

[0060] Defoamer tributyl phosphate 0.2g

[0061] Deionized water 170g

[0062] operate:

[0063] Weigh 90g of deionized water, add it into a stainless steel bucket, then sprinkle 18g of PVA into the water under stirring, continue to stir for 1 hour, start to heat up to 93°C, maintain for 1 hour, cool down to room temperature, and obtain a PVA solution; according to the formula Add the remaining 80g of deionized water into the stainless steel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a plating solution of ink-jet print intermediate which comprises the calcium carbonate as main paint. It is formed by calcium carbonate, adhesive agent, and several additives (agents). Wherein, the calcium carbonate can be one or several ones of heavy calcium carbonate, light calcium carbonate or active calcium carbonate, while the average grain diameter is 0.1mu m-2mu m. The invention uses the calcium carbonate to replace the silicon dioxide, alumina and titanium oxide to be directly plated on the colorful ink-jet print paper and print photograph paper, without changing present paper plating processes, with lower cost and simple device. Therefore, it can make the lower-level paper into high-level paper and save the wood resource.

Description

technical field [0001] The invention relates to a coating material for ink-jet printing media and a preparation method thereof, in particular to a coating material for waterproof printing photo paper. Background technique [0002] Inkjet printing is a non-contact printing method that has many advantages including high-speed printing, low noise, and ease of color printing, so it has been rapidly used in printers and plotters. Inkjet printing enables printing on plain printing paper, coated paper, PPC paper (plain copier paper), medium quality paper, and even plastic films. Inkjet printing technology is gradually popularized and expanded in the field of color image printing due to its characteristics such as easy colorization, low noise, no pollution, and low price. [0003] In recent years, due to the overall development of electronic technology, the storage capacity of digital images has gradually increased, and the color printing images have also increased, and the technol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/52B41M5/50D21H21/22D21H21/28D21H19/38D21H19/46D21H19/54D21H19/44
Inventor 程世平
Owner 四川新泰克控股有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products