High-use-temperature, high strength, anti high temperature oxidation and high-temperature corrosion-deformation resistance high-temperature alloy

A technology of high temperature oxidation resistance and high temperature corrosion resistance, applied in the field of alloys, can solve the problems of insufficient high temperature corrosion resistance, insufficient high temperature strength, etc., and achieve the effect of prolonging service life, high temperature strength, and excellent high temperature corrosion resistance.

Inactive Publication Date: 2006-10-25
CHONGQING MATERIALS RES INST
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the above-mentioned alloys are excellent, there are still deficiencies, mainly in the room for improvement in the high-temperature oxidation resistance of the alloy, insufficient high-temperature corrosion resistance, and insufficient high-temperature strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1:

[0039] According to chemical composition C: 0.01%, Si: 0.3%, Mn: 0.5%, Ni: 38%, Cr: 23%, Al: 4.8%, Co: 2%, W: 2%, Mo: 2%, Zr: 0.05%, B: 0.005%, Y: 0.08%, and the balance is the alloy ingot produced by Fe. After hot processing and cold processing, it is made into alloy material, which is used to make thermocouple protection tube.

[0040] The alloy is melted by vacuum induction, and then the alloy ingot is obtained by electroslag melting. The alloy hot forging temperature is 1160°C, and the holding time is 60 minutes; the hot rolling temperature is 1160°C, and the holding time is 45 minutes. During the cold working process, the alloy must be solution treated in time to eliminate cold work hardening. The solution treatment system is a holding temperature of 1150°C, a holding time of 30-45 minutes, and water cooling.

Embodiment 2

[0042] According to chemical composition C: 0.01%, Si: 0.3%, Mn: 0.5%, Ni: 38%, Cr: 23%, Al: 4.8%, Co: 1%, W: 1%, Mo: 1%, Zr: Alloy ingots produced by 0.05%, B: 0.005%, Y: 0.08%, and the balance is Fe. After hot processing and cold processing, they are made into alloy materials, which are used to make high-temperature wear-resistant experimental furnace appliances and thermocouple protection tubes.

[0043] The alloy is melted by vacuum induction, and then the alloy ingot is obtained by electroslag melting. The alloy hot forging temperature is 1160°C, and the holding time is 60 minutes; the hot rolling temperature is 1160°C, and the holding time is 45 minutes. During the cold working process, the alloy must be solution treated in time to eliminate cold work hardening. The solution treatment system is a holding temperature of 1150°C, a holding time of 30-45 minutes, and water cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
service temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses the high temperature alloy resisting high temperature oxidation and resisting high temperature corrupt, the weight percent of the chemical element: C<=0.08%, Si<=0.8%, Mn<=0.8%, Ni 40-50%, Cr 14-20%, Al 3.8-7.5%, Y<=0.3%, the remaining is Fe. The highest using temperature of the alloy can reached to the 1350 degree, the alloy has many merits such as the excellent high temperature resisting the oxidation ability, the high temperature resisting the causticity, the higher temperature intension, the realization of producing the high temperature of the alloy material by the cool, hot distortional process. So it can be applied in the producing of the high temperature model, the high temperature clamp, the thermocouple protecting pipe resisting the high temperature oxidation and resisting the high temperature corrupt, the shortcoming of the coating on the corundum, the double silicon molybdenum pipe and the surface of the high temperature alloy can be conquered, it solves the problem of using the thermocouple protecting pipe under the temperature 1200-1350 degree.

Description

technical field [0001] The invention relates to an alloy, in particular to a high-temperature alloy with high service temperature, high strength, high-temperature oxidation resistance and high-temperature corrosion resistance and deformation resistance. Background technique [0002] The usual superalloys refer to metal structural materials used at very high temperatures. They have certain high-temperature strength, high-temperature fatigue strength, high-temperature durability, high-temperature creep resistance, and high-temperature stress-relaxation resistance. The performance of this superalloy Requirements focus on high-temperature comprehensive performance and high-temperature strength. They appeared in the 1930s, and their development motivation mainly came from the needs of aero engines, especially since the advent of jet engines in the late 1940s, the demand for high-temperature alloys has increased day by day, and at the same time, their scope of use has expanded. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/52
Inventor 万红王东哲魏捍东孙威祁宏
Owner CHONGQING MATERIALS RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products