Method for non-vacuum melting and casting Cu-Cr-Zr alloy

A non-vacuum smelting, cu-cr-zr technology, used in ingot workshops, foundry workshops, casting equipment, etc., can solve the problem of high requirements for raw material composition and impurity content, inability to perform composition measurement, composition adjustment, and furnace body sealing To solve problems such as high sexual requirements, achieve the effect of realizing large-scale production, solving the problem of high cost, and solving the difficulty of large-scale production

Inactive Publication Date: 2006-11-22
CHINA NON-FERROUS METALS PROCESSING TECH CO LTD
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the method of vacuum smelting Cu-Cr-Zr alloy has the following problems: ①Due to the high degree of vacuum required in the smelting process of the vacuum furnace, the requirements for the tightness of the furnace body are very high, and composition measurement, composition adjustment and Slag pulling and other operations, so the requirements for the composition and impurity content of raw materials are very high; ②Va

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for non-vacuum melting and casting Cu-Cr-Zr alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The raw materials of electrolytic copper, copper-chromium intermediate alloy and zinc are respectively taken, and the amount of materials taken is shown in Table 1, and loaded into the furnace 8 from the feeding port 7, so that it is contained in the crucible 16; the furnace cover 2 can also be opened to directly add raw materials. Cover the feeding port 7 and the observation window 1, open the protective gas valve, and pass in argon gas from the upper air inlet 3 until the air is discharged from the upper gas outlet 5, the protective gas is filled with the furnace 8, and the match will be lit at the upper gas outlet 5. Immediately extinguished. Turn on the induction heating device 10, the power is 10KW, the time is 10 minutes, the power adjustment is 50KW, and it is heated to melting. The whole heating process can be observed in the observation window 1. Add copper-clad zirconium and magnesium from the feeding port 7, smelt for 5 minutes, open the air valve at the same...

Embodiment 2

[0023] The present invention is carried out under the same conditions as in Example 1 by using zirconium wire instead of copper-clad zirconium. The chemical contents of raw materials and ingots are shown in Table 2. The loss rates of each metal during the smelting process are: Cu≤1.0%, Cr≤3.4% and Zr≤7.2%.

[0024] raw material

Embodiment 3

[0026] Adopt the same condition as embodiment 1, adopt N 2 In order to protect the gas, use a gas nozzle to extend into the melt from the feeding port 7 during the heat preservation process after smelting, and inject N 2 It is passed into the melt for degassing. The chemical content of raw materials and ingots is shown in Table 3. According to the metallographic photos, it can be seen that the structure of the ingot is significantly improved, and the pores and inclusions are reduced. The loss rates of each metal during the smelting process are: Cu≤1.1%, Cr≤3.4% and Zr ≤7.1%.

[0027] raw material

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a melting and casting Cu-Cr-Zr alloy method, which comprises the following steps: loading electrolytic copper, cupraloy and metal zirconium in the protective gas induction furnace; fusing; casting from bottom; connecting lower cast hole and crystallizer with gas protecting device. The whole course is protected by pure gas with low hydrogen and oxygen partial pressure, which provides good quality casting ingot.

Description

technical field [0001] The invention relates to the processing of Cu-Cr-Zr alloys, in particular to methods for smelting and casting Cu-Cr-Zr alloys, and belongs to the technical field of nonferrous metal processing. Background technique [0002] The traditional processing method of Cu-Cr-Zr alloy is to mix the electrolytic copper and other alloying elements in proportion and put them into the vacuum furnace. -3 The heating and smelting starts below the Pa, and the casting is directly carried out in a vacuum furnace after the smelting is completed. This smelting method, due to the high vacuum in the furnace, the gas partial pressure of oxygen is extremely low, which kinetically prevents the oxidation and burning of the smelted metals (Cu, Cr and Zr). During the smelting process, the copper melt contains a certain amount of oxygen and hydrogen, and a large chemical potential is generated between the inside of the melt and the smelting environment due to the concentration gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/03B22D9/00B22D21/00
Inventor 郭富安慕思国曹兴民向朝建杨春秀朱雯
Owner CHINA NON-FERROUS METALS PROCESSING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap