A dry powder coating, environmentally friendly technology, applied in powder coatings, coatings, etc., can solve the problems of high stability of latex paint and high storage and transportation costs, and achieve the effect of saving chemical raw materials, saving processes, and smooth paint film

Inactive Publication Date: 2007-01-03
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 52 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an environment-friendly dry powder paint, which can be made into the current traditional latex paint by adding water and stirring during use. Enable latex paint to be packaged and sold in a stable and low-cost storage and transportation form

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The content of each component of the environment-friendly dry powder coating of this embodiment is 9% of redispersible polymer latex powder, 35.3% of white cement, 40% of calcium carbonate, 10% of anatase titanium dioxide, 2% of diatomite, and 1% of bentonite , 0.2% of hydroxypropyl cellulose, 0.2% of defoamer, 2.3% of coloring pigments, put the above-mentioned components into the mixer according to the weight percentage, after mixing evenly, the finished product environment-friendly dry powder coating can be obtained by packaging. During construction, add water to the environment-friendly dry powder paint, mix well and then spray, wherein paint: water = 5:3. The colored dry powder coating of the present embodiment can be used for the decoration of the inner wall of a building.

Embodiment 2

[0035] The content of each component of the environment-friendly dry powder coating of the present embodiment is 16.7% of redispersible polymer latex powder, 27% of white cement, 25% of calcium carbonate, 21% of rutile titanium dioxide, 4% of diatomite, 1.5% of bentonite, 0.2% of hydroxyethyl cellulose, 0.3% of carboxymethyl cellulose, 0.5% of defoamer, 3.8% of coloring pigment, the above-mentioned components are put into the mixer according to the weight percentage, after mixing evenly, the finished product can be obtained by packaging. Dry powder coating. During construction, add water to the environment-friendly dry powder paint, mix well and then spray, wherein paint: water = 5:4. The colored dry powder coating of the present embodiment can be used for the decoration of building exterior walls.

Embodiment 3

[0037] The content of each component of the environment-friendly dry powder coating of this embodiment is 6% of redispersible polymer latex powder, 38% of white cement, 42% of calcium carbonate, 6% of anatase titanium dioxide, 6.4% of diatomite, and 1% of bentonite , 0.3% of methyl cellulose, 0.3% of defoaming agent, put the above-mentioned components into the mixer according to the weight percentage, after mixing evenly, the finished product environment-friendly dry powder coating can be obtained by packaging. During construction, add water to the environment-friendly dry powder paint, mix well and then spray, wherein paint: water = 10:7. The white dry powder coating of the present embodiment can be used for the decoration of building inner wall.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The present invention discloses one kind of green powdered paint and its preparation process. The green powdered paint consists of re-dispersible polymer latex powder 5-20 wt%, white cement 20-40 wt%, calcium carbonate 20-45 wt%, titanium white powder 5-25 wt%, diatomite 2-8 wt%, bentonite 1-2 wt%, cellulose ether 0.2-0.5 wt%, defoaming agent 0.2-0.5 wt% and coloring pigment 0-4 wt%. It is prepared through mixing all the components in a stirrer, and packing. It is used after mixing with water in construction site. It has the combined decoration functions of both putty and emulsion paint and may be used widely for decorating inner and outer wall.

Description

technical field [0001] The invention belongs to the field of dry powder coatings, in particular to an environment-friendly dry powder coating and a preparation method thereof. Background technique [0002] With the development of science and technology, people's understanding of environmental protection and sustainable development is getting deeper and deeper. In the coatings industry, it is the general trend to replace the heavily polluting solvent-based coatings with water-based coatings and powder coatings, and water-based coatings have been widely used. However, the architectural water-based latex coatings currently used are composed of polymer emulsions, pigments and fillers, various additives and water. Among them, additives and water are used for the production and storage of coatings, accounting for more than half of the weight and price of coatings. Most of the water-based architectural latex paint is water (about 60%), and the solid content is only 40%. The storag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/06C09D5/03
Inventor 张心亚谢德龙黄洪陈焕钦
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap