Plastic wood sheet and its preparation method

A board and plastic wood technology, applied in the field of plastic wood board and its preparation, can solve the problems of low product strength, high price, small area, etc., and achieve the effect of good dimensional stability, wide application and large area

Inactive Publication Date: 2007-02-14
杨孝干 +1
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Extrusion is difficult
Equipment, molds, and auxiliary machines are expensive, requiring high precision, low product strength, poor rigidity,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 30 parts of crop fibers, including various crop straws, such as wood powder, peanut shells, bean stalks, cotton stalks, etc.; 70 parts of waste plastics, including various waste plastics, including other plastic products that cannot Plastics used, such as machine head, die head material, paper-plastic synthetic milk bags, beverage bags, paper-plastic packaging bags, etc.; paraffin wax as external lubricant, stearate additives as internal lubricant; 1 part of linking and cross-linking agent, 10 parts of bromine-based flame retardant, 2 parts of general-purpose ultraviolet absorber for plastics, and 2 parts of general-purpose anti-aging agent for plastics. After mixing the materials, put them into a mixer for mixing and drying. The drying temperature is 80 degrees The time is 15 minutes, the pressure is normal pressure; enter the extruder to produce wood-plastic particles, the compression ratio of granulation extrusion is 3:1, and the particle size is 2mm; put the wood-pla...

Embodiment 2

[0026] 90 parts of crop fibers, including various crop straws, such as wood flour, peanut shells, bean stalks, cotton stalks, etc.; 10 parts of waste plastics, including various waste plastics, including other plastic products that cannot be used Plastics, such as machine head, die head material, paper-plastic synthetic milk bag, beverage bag, paper-plastic packaging bag, etc.; 10 parts of stearate additive internal lubricant and stearic acid external lubricant; peptide ester acid Auxiliary coupling, 10 parts of cross-linking agent, 20 parts of aluminum hydrate flame retardant, 2 parts of plastic universal ultraviolet absorber, 2 parts of plastic universal anti-aging agent, mix the materials and put them into the mixer for mixing and drying. The temperature is 100 degrees, the time is 10 minutes, and the pressure is normal pressure; enter the extruder to produce wood-plastic particles, the compression ratio of granulation and extrusion is 3:1, and the particle size is 6mm; put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Widthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

A method for preparing plastic wood slab includes applying 30-90 shares of crops fiber, 10-70 shares of regenerated plastic, 1-10 shares of wetting agent, 1-10 shares of coupling agent, 10-20 shares of fire retardant, appropriate amount of absorber and appropriate amount of antiager as raw materials, mixing them then pressing them to be slab. The prepared slab is on specification as width of 500-2000mm and length of 2000-4000mm.

Description

technical field [0001] The invention relates to a plastic wood board and a preparation method thereof. Background technique [0002] Wooden materials, steel, cement, and plastics are called the four basic raw materials, and woody materials are the only renewable ones. At present, the amount of large-diameter timber in my country is very small, which cannot meet the needs of the market. In order to solve this crisis, people advocate replacing wood with steel and plastic, and consume non-renewable petroleum and iron ore resources. , but led to the occurrence of one raw material crisis after another. On the other hand, facing the number of big trees, people use composite methods to glue small materials together. For this reason, a large amount of rubber must be used, of which 90% More than % is urea-formaldehyde glue, which is the main source of formaldehyde pollution in the air. [0003] Now the annual output of plastics in the world is about 130 million tons, and the output i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04C2/24B27N3/08B27N1/02B27N7/00
Inventor 窦典峰
Owner 杨孝干
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap