Process of preparing short glass fiber with waste tank furnace filament

A short glass fiber and kiln drawing technology, which is applied in glass manufacturing equipment, solid waste removal, manufacturing tools, etc., can solve the problems of high temperature sintering and high processing costs, and achieve good environmental protection, convenient cutting and high utilization rate high effect

Inactive Publication Date: 2007-03-21
林军
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method also requires high temperature sintering and high processing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The wire drawing waste from the pool kiln is winding yarn. Winding yarn refers to the winding process in glass fiber, using glass fiber roving or prepreg tape under tension control to wind on a placement shaft in a predetermined arrangement, and can produce tubular or other hollow shaped products.

[0027] The steps of preparing short glass fibers by utilizing the waste winding yarns drawn from pool kilns are as follows:

[0028] (1) Coarse treatment of the waste wire drawing yarn in the pool kiln: remove 100 kg of the waste wire drawing yarn in the pool kiln to remove surface impurities such as plaster and paper scraps, and dry it in air to make the water content of the wire drawing waste wire in the pool kiln 5%;

[0029] (2) configuration of binding agent: dilute 2kg of epoxy resin binding agent with water to sprayable state, and its weight percent concentration is 15%;

[0030] (3) Spraying of binder: according to the ratio of 15:100 of the weight ratio of binder n...

Embodiment 2

[0034] Spray yarn is prepared from wire drawing waste in pool kiln. Spray yarn means that in the spray process, a spray gun is combined with a portable glass fiber roving chopping machine, the resin and glass fiber are sprayed onto the mold at the same time, and then the impregnated yarn is sprayed with a stick, brush or scraper. The glass fibers of the resin compact and allow it to cure.

[0035] The steps of preparing short glass fibers by using the waste sprayed yarns from drawing in the pool kiln are as follows:

[0036] (1) Rough treatment of waste jet yarn from drawing in pool kiln: select 100kg waste jet yarn from drawing in pool kiln according to specifications and models, remove impurities such as marl and paper scraps on the surface, and dry to make the water content of drawing waste in pool kiln 4% range.

[0037] (2) configuration of binding agent: dilute 2.5kg of polyester resin binding agent with water to sprayable state, and its weight percentage concentration...

Embodiment 3

[0042] The wire drawing waste from the tank kiln is long glass fiber for reinforced plastics. Long glass fiber for reinforced plastics belongs to untwisted roving. In the plastic extrusion granulator, in the specially designed die head, the fiber can be fully expanded to facilitate the thermoplastic resin to penetrate into the fiber and wrap the fiber.

[0043] The steps of preparing short glass fibers by using long glass fibers for reinforced plastics from pool kiln wire drawing waste are as follows:

[0044] (1) Coarse treatment of long glass fibers used in tank kiln wire drawing waste reinforced plastics: 100kg of tank kiln wire drawing waste jet yarn is selected according to specifications and models to remove impurities such as marl and paper scraps on the surface, and dried to make tank kiln wire drawing waste The moisture content of the silk is in the range of 3%;

[0045] (2) configuration of binding agent: the mixture binding agent 3kg of polyvinyl acetate and polyur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The process of preparing short glass fiber with waste tank furnace filament includes the following steps: initial treatment of waste tank furnace filament; compounding adhesive via diluting adhesive with water for spraying; spraying adhesive to waste tank furnace filament or soaking waste tank furnace filament in adhesive and stilling for well absorbing adhesive; forming short glass fiber through cutting, sieving and roasting. The present invention produces useful material with waste and has low production cost.

Description

technical field [0001] The invention relates to the technical field of reuse of wire drawing waste from a pool kiln, in particular to a method for preparing short glass fibers by using the waste wire drawing from a pool kiln. Background technique [0002] Generally speaking, there are two production processes in the glass fiber industry: platinum furnace wire drawing and pool kiln wire drawing. Among them, the drawing process of platinum furnace is relatively backward, and its application is less and less; while the drawing process of pool kiln is more and more widely used. Both processes generate large amounts of glass fiber waste. These waste wires are mainly composed of the hard wires produced before the upper head and the thick wires produced by the end cover of the drawing machine head. The composition of all waste silk is the same as that of glass fiber products. It belongs to silicate materials in inorganic non-metallic materials and is a non-degradable solid pollut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B37/10C03B37/14B09B3/00
CPCC03B37/10
Inventor 林军
Owner 林军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com