Method of preparing single-coating-type paint for copper layer free glass silver mirror back

A single-coating, mirror-back paint technology, used in coatings, mirrors, polyester coatings, etc., can solve the problem that ordinary glass mirror mirror back paint cannot be used, the edges of copper-free glass mirror mirrors are black, and the glass silver mirror is affected. Mirror performance and other issues, to achieve the effect of short baking time, increased hydrophobicity, and improved wettability

Inactive Publication Date: 2007-08-08
SHANGHAI JIAO TONG UNIV
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And no copper layer glass silver mirror does not plate metal copper, does not produce ferrous sulfate, but with common glass silver mirror mirror back paint, as disclosed " based on the quick-drying high solid content coating of modified alkyd resin " of CN1371409A, A kind of acrylic acid modified alkyd resin composition cured at room temperature; or CN1621430 disclosed "modified dry oil alkyd resin and curtain coating for mirror back metal coating protective coating", a kind of dry oil modified Alkyd resin, modified acrylic acid and modified epoxy resin, will make the edge of the copper-free glass silver mirror black, and the silver-plated layer without copper layer protection is easy to change color after over-baking
[0003] To sum up, the environment-friendly copper-free glass silver mirror cannot use ordinary glass silver mirror mirror back paint, and the silver-plated layer without copper-coated layer cannot be overbaked, otherwise the performance of the glass silver mirror will be affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0018] Stir the short-oil alkyd resin, superfine talcum powder, superfine barium sulfate, zinc oxide, lead oxide, iron red, iron brown, iron black, titanium dioxide, and organic solvent in a stainless steel tank according to the formula described in Table 1. Put into a sand mill and grind until the fineness is less than 15 μ, then add the anti-skinning agent, drier, and brightening agent in the weight percentage described in Table 1, stir evenly, pass the inspection, filter, measure, and pack to obtain a single Copper-free glass silver mirror mirror back paint.

[0019] Table 1 (various raw materials are by weight percentage in the table)

[0020] Raw material name

Example 1

Example 2

Example 3

Example 4

Tunglinoleic Phenolic Short Oil Alkyd Resin

Acid value 20.0KOHmg / g,

The content of tung linoleic acid is 20.8wt%,

Phenolic content 20.5wt%

23.0

28.0

Tung linoleum phenolic short oil alkyd resin

A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a making method of single-painting typed copper-free layer glass back paint, which comprises the following parts: 7.0-8.0wt% metal oxide, 9.0-11.0wt% ultra-fine talcum powder, 15.0-37.0wt % ultra-fine barium sulfate, 20.0-30.0wt% short-oil alkide resin, 3.0-10.0wt% coloring dye, 0.05- 0.15wt% anti-crust agent, 0.01-0.08wt% drier, 0-3.5wt% glossing agent and organic solvent.

Description

Technical field: [0001] The invention relates to a preparation method of a paint, in particular to a preparation method of a single-coated copper-free glass silver mirror back paint. Background technique: [0002] The production method of the ordinary glass silver mirror is to first coat a layer of metallic silver on the glass surface with a silver mirror chemical reaction method as a reflective layer, and then use a copper mirror chemical reaction method to coat a layer of metallic copper to increase the reflection effect of the silver film. and protective effect. In order to protect the metal layer of the glass silver mirror from chemical corrosion and physical damage, primers and topcoats need to be coated on the metal layer of the glass silver mirror to protect the metal layer, and the chemical reaction of the copper mirror will produce ferrous sulfate which is not friendly to the environment . And no copper layer glass silver mirror does not plate metal copper, does n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/04A47G1/00
Inventor 罗漫
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More