Composite ceramic material for increasing combustion efficiency of IC engine and preparation process thereof

A technology of composite ceramics and combustion efficiency, applied in the direction of fuel, fuel additives, petroleum industry, etc., can solve the problems of poor durability, poor fuel saving effect of fuel economizer, etc., and achieve the effect of promoting oxygen supply and good processing characteristics

Inactive Publication Date: 2010-08-25
杨中化 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems of poor fuel-saving effect and poor durability of current fuel economizers, the present invention proposes a low-temperature far-infrared ray with excellent mechanical properties, high heat resistance, high gas barrier rate, chemical resistance, and excellent Composite ceramic material for improving combustion efficiency of internal combustion engine and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] First prepare the base material. In the present invention, the mixture of zeolite, tourmaline, copper-exchanged ZSM-5 zeolite and hydrotalcite material is used as the base material. It has a special layered structure. After blending with polymer materials, layers Inter-cation exchange and ionic bonding reactions. Its gas barrier properties, water barrier properties, UV resistance, heat resistance, dimensional stability, bending resistance, toughness, wear resistance, scratch resistance, durability, corrosion resistance, chemical resistance and other characteristics are incomparable with micron-scale structures. Superiority.

[0022] After the above matrix material is prepared, substances with far-infrared functions, such as nano-silver, nano-platinum, nano-cadmium, barium oxide, zinc oxide, cerium oxide, titanium dioxide, tourmaline, aluminum oxide, iron oxide silicon dioxide, are mixed into the moistening In the wet zeolite and tourmaline matrix materials, the content...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A composite ceramic material able to improve the combustion efficiency of IC engine is prepared from basic raw material (laminated zeolite and tourmalinite), nano-Ag, nano-Pt, nano-Cd, barium oxide, zinc oxide, cerium oxide, TiO2, aluminum oxide, iron oxide, and SiO2 through wetting basic raw material, beating, mixing with others, stirring, shaping, and clacining. It has excellent mechanical performance and low-temp far infrared effect, very low thermal expansibility, high resistance to high temp and chemicals, and high gas isolation power.

Description

technical field [0001] The invention relates to a composite ceramic material for improving the combustion efficiency of an internal combustion engine and a preparation process thereof, in particular to a ceramic material for improving the combustion efficiency of an internal combustion engine when put into an oil tank and a preparation process thereof. Background technique [0002] Promoting the combustion of fuel oil and gas has important practical significance for saving energy consumption and reducing pollutant emissions. Especially in recent years, with the rapid development of the automobile industry and the shortage of energy in the world, the technology of improving fuel and gas combustion efficiency has attracted great attention from scientists and governments all over the world. [0003] The main reason why the fuel cannot be completely combusted in the cylinder is: there is van der Waals attraction between fuel hydrocarbon molecules, which combines several hydrocar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/16C10L10/00C04B35/622
Inventor 陆奕中杨中化
Owner 杨中化
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products