Polypropylene resin composition, its preparing method and fan

A technology of polypropylene resin and composition, applied in the field of polypropylene resin composition and its preparation, can solve the problems of high production cost of glass fiber, three wastes, dust, etc., and achieve high strength, high vibration suppression, and high heat insulation. Effect

Inactive Publication Date: 2007-11-14
PANASONIC CORP
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, glass fiber is the most widely used, but glass fiber has comparative advantages in terms of specific strength, service temperature, chemical stability (especially in alkaline medium), vibration damping performance, heat resistance and sound insulation characteristics. Large limitations, and the production process of glass fiber is easy to produce dust, three wastes and other hazards to the natural environment. In addition, boron dioxide, which is in short supply, needs to be used in the manufacture of glass fiber, and the production cost of glass fiber is relatively high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene resin composition, its preparing method and fan
  • Polypropylene resin composition, its preparing method and fan

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Get 69 parts by weight of polypropylene resin, 30 parts by weight of basalt fibers with a single fiber diameter of 9 μm and a length of 3 millimeters in which 30 parts by weight of silane are processed, and 0.3 parts by weight of polypropylene wax as a lubricant, 0.02 parts by weight as Calcium stearate of filler, 0.03 parts by weight of calcium hydroxide as stabilizer, 0.05 parts by weight of 264 (DTBP) as anti-aging agent and 0.2 parts by weight of tert-butylperoxyethane as antioxidant, 0.1 parts by weight Part of antioxidant 1010 and 0.3 part by weight of antioxidant DLTP were mixed in a kneader and pelletized with a screw extruder with a full-range screw at 250°C. Thus, a polypropylene resin composition was obtained. The obtained pellets were molded into flexural modulus test strips (according to ASTM D 790 specification) with an injection molding machine, and their flexural strength and flexural modulus properties were measured. The experimental results are shown ...

Embodiment 2

[0055] Get 69 parts by weight of polypropylene resin, 20 parts by weight of basalt fibers with a single fiber diameter of 9 μm and a length of 3 millimeters, 10 parts by weight of E-glass fiber and 0.3 parts by weight of polystyrene as lubricant. Propylene wax, 0.02 parts by weight of calcium stearate as a filler, 0.03 parts by weight of calcium hydroxide as a stabilizer, 0.05 parts by weight of 264 (DTBP) as an anti-aging agent and 0.2 parts by weight of tert-butyl as an antioxidant Ethylene peroxide, 0.1 parts by weight of antioxidant 1010 and 0.3 parts by weight of antioxidant DLTP were mixed in a kneader, and granulated by a screw extruder with a full-range screw at 250°C. Thus, a polypropylene resin composition was obtained. The obtained pellets were molded into flexural modulus test strips (according to ASTM D 790 specification) with an injection molding machine, and their flexural strength and flexural modulus properties were measured. The experimental results are show...

Embodiment 3

[0062] Get 69 parts by weight of polypropylene resin, 30 parts by weight of basalt fibers with a single fiber diameter of 9 μm and a length of 3 millimeters in which 30 parts by weight of silane are processed, and 0.3 parts by weight of polypropylene wax as a lubricant, 0.02 parts by weight as Calcium stearate of filler, 0.03 parts by weight of calcium hydroxide as stabilizer, 0.05 parts by weight of 264 (DTBP) as anti-aging agent and 0.2 parts by weight of tert-butylperoxyethane as antioxidant, 0.1 parts by weight Part of antioxidant 1010 and 0.3 part by weight of antioxidant DLTP were mixed in a kneader and pelletized with a screw extruder with a full-range screw at 250°C. Thus, a polypropylene resin composition was obtained. The obtained pellets are injection molded into blade fans, which are assembled on the fan motor of the air conditioner to form a fan for the air conditioner. The blade fan of the air conditioner manufactured by the polypropylene resin composition of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The present invention offers a polypropylene resin composite. The said polypropylene resin composite contains polypropylene resin and basalt fiber. Specially, setting the total amount of polypropylene resin composite as 100 units, the said polypropylene resin composite contains 50 to 95 units of polypropylene resin, and 50 to 5 units of corresponding basalt fiber. Moreover, the said basalt fiber is 3 to 10 mm in length, and 9 to 17 mu m in diameter. The present invention also offers the preparation method of polypropylene resin composite and the fan made by using the composite. The polypropylene resin composite prepared by the present invention, overcomes the existing technical defect, and has high elastic modulus and better impact performance and chemical stability; meanwhile, it has very high heat and sound proofing properties, and is suitable for various industrial components, especially the fan of air-condition.

Description

technical field [0001] The invention relates to a polypropylene resin composition, a preparation method thereof and a fan prepared therefrom. More specifically, the present invention relates to a polypropylene resin composition containing basalt fiber as a reinforcing component, a method for its preparation, and a fan. Background technique [0002] In the prior art, as a general-purpose thermoplastic resin, polypropylene (PP) has better heat resistance than polyethylene (PE); its melting point reaches about 164°C, and it can be used for a long time at 100-120°C. In addition, polypropylene It also has excellent corrosion resistance and electrical insulation, and its mechanical properties (including tensile strength, compressive strength, hardness) are better than high-density polyethylene (HDPE), and it also has outstanding rigidity. Polypropylene is easy to process, and most of it is used for injection molding. In addition to daily necessities, it can also be used to manufa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K7/04F24F13/00
Inventor 薛欣荣太田雅春
Owner PANASONIC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka