Sand pulp concrete waterproof agent and method for making same

A technology for concrete waterproofing agent and mortar, which is applied in the field of concrete waterproofing agent and its preparation, and mortar, can solve the problems of inconvenient measurement and transportation, difficult control of construction quality, poor structure density, etc., so as to improve the compactness and impermeability performance. , Good water impermeability and improved impermeability

Active Publication Date: 2008-02-06
JINHUA XINSHENG ZEOLITE DEV
View PDF0 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the early-strength and quick-setting effect of this type of waterproofing agent, the early-stage hydrate structure is formed faster, so the structure is less dense. The faster the early-stage strength of concrete increases, the lower the later-stage strength. The coagulation effect will adversely affect the later strength of cement mortar or concrete, and the impermeability is also poor; in addition, the calcium sulfoaluminate generated in the early stage of hydration will be converted into ettringite, and there are 32 A water molecule needs a lot of water when it is formed, especially in the early stage of concrete pouring. If the humidity is not enough, it will be difficult to make it reach the expected expansion value even if the curing time is prolonged, thus affecting the waterproof performance. Therefore, it is important for the early wet curing of concrete. The requirements are particularly high, which makes the construction quality difficult to control
Furthermore, this type of waterproofing agent is mostly a liquid product, and it is inconvenient to measure and transport during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: Weigh 83 parts of activated zeolite powder by weight and place them in a mixer, then weigh 1 part of silane coupling agent, 4 parts of stearic acid, 0.03 parts of alkylphenol polyoxyethylene ether, and 7 parts of magnesium lime 3 parts of gypsum, 8 parts of polypropylene fiber, and then add the modifier-silane coupling agent, alkylphenol polyoxyethylene ether and stearic acid to the activated zeolite powder and stir in succession, the temperature is controlled at 150-210℃ and stirring for 2 hours to form activated modified zeolite powder; then add weighed magnesia lime, gypsum and polypropylene fiber into the activated modified zeolite powder, and fully stir and mix to obtain mortar and concrete waterproofing agent.

[0027] The fineness of the activated zeolite powder in the present invention is preferably 260~500 meshes, and when the waterproofing agent dosage is 5% of cement consumption, the fineness of the activated zeolite powders is 350~500 meshes and is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mortar and concrete waterproofer. The waterproofer is characterized in that: the waterproofer comprises (part by weight) 70 to 90 parts of activation zeolite power, 0.3 to 2 parts of silane resin acceptor, 2 to 5 parts of stearic acid, 0.007 to 0.05 parts of alkylphenols polyethenoxy ether, 3 to 10 parts of magnesium lime, 1 to 6 parts of plaster, 5 to 10 parts of mekralon. The invention further relates to a preparation method for the mortar and concrete waterproofer. The waterproofer not only can increase the compactness, the pressive strength and the waterproof impermeability of the concrete, but also can prevent temperature difference gap through the delay and reduction of heat release of hydration, reduce the shrinkage of the cement gelatin to reduce the drying shrinkage of the concrete. A slight expansion of the concrete a compensation of a shrinking gap can increase the cracking resistance. The invention can also improve the operation performance of the mortar and the concrete, restrain an alkali-aggregate reaction and increase long term strength of the concrete and enhance the wear, and is particularly suited to serving as an admixture of the mortar and the concrete.

Description

technical field [0001] The invention belongs to building material additives, in particular to a mortar and concrete waterproofing agent and a preparation method thereof. Background technique [0002] There are two main types of existing mortar and concrete waterproofing agents: organosilicon-based waterproofing agents and inorganic aluminum salt-based waterproofing agents. The main components of silicone waterproofing agent are sodium methyl siliconate (potassium) and sodium siliconate (potassium), which is a water-soluble polymer with a small molecular weight. The waterproof membrane of methyl silicone ether, the waterproof membrane is surrounded by the constituent particles of concrete and has hydrophobic properties. Since the volume of concrete will shrink due to cold shrinkage or dry shrinkage during the pouring hardening process, the main disadvantage of silicone-based waterproofing agents is that they cannot compensate for the shrinkage cracks of concrete, so the shri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B22/06C04B22/14C04B24/42C04B24/08C04B24/02C04B24/26C04B103/65C04B103/46
CPCC04B28/02C04B2103/65C04B40/0028
Inventor 陈土兴胡景波
Owner JINHUA XINSHENG ZEOLITE DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products