Wax polish and preparation method thereof

A technology of montan wax and palm wax, applied in chemical instruments and methods, polishing compositions, etc., can solve the problems of damaged paint surface, rough polishing powder, cracks, etc. good thermal performance

Inactive Publication Date: 2008-03-26
李而淮
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although solvent-based glazing wax has strong decontamination ability, because the paint can dissolve in organic solvents, when the varnish wax is applied to the paint surface, the paint surface will be corroded, penetrated and damaged, and it is easy to turn yellow. , becomes rough, dulls the finish, and hardens, cracks, and flakes off, deteriorating the exterior of the car; the organic solvents in solvent-based polishes are odorous and/or flammable, Moreover, organic solvents are toxic substances, so the use of solvent-based glazing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Make glazing wax according to the following steps: 3.5 grams of silicone oil, 0.3 grams of vaseline, 5 grams of polyethylene, 0.2 grams of montan wax, 4.5 grams of coumarone-indene resin, 0.6 grams of carnauba wax, C 12 Nine kinds of raw materials including 2.8 grams of fatty alcohol polyoxyethylene (n) ether, 3 grams of nonylphenol polyoxyethylene (n) ether and 2.5 grams of coconut oil diethanolamide (1:1 type) were added to the oil bath jacket for esterification In the pot, heat until the raw materials are melted and esterified, and then filter, and the filtered filtrate is placed in an oil bath jacket pot for emulsification; the temperature of the filtrate in the oil bath jacket pot for emulsification is kept at 100 ° C, under the condition of stirring, Add 10 grams of water at a temperature of 100°C to the filtrate, and the time for adding water is 20 seconds; then cool the emulsification oil bath set to 50°C, and add 15 grams of bentonite slurry that has absorbed wa...

Embodiment 2

[0042] Make glazing wax according to the following steps: 8 grams of silicone oil, 5 grams of vaseline, 8 grams of polyethylene, 0.5 grams of montan wax, 0.2 grams of coumarone-indene resin, 0.2 grams of carnauba wax, C 12 Nine kinds of raw materials including 3 grams of fatty alcohol polyoxyethylene (n) ether, 5 grams of nonylphenol polyoxyethylene (n) ether and 4.5 grams of coconut oil diethanolamide (1:2 type) were added to the oil bath jacket for esterification In the pot, heat until the raw materials are melted and esterified, and then filter, and the filtered filtrate is placed in an oil bath jacket pot for emulsification; the temperature of the filtrate in the oil bath jacket pot for emulsification is kept at 99 ° C, under the condition of stirring, Add 6 grams of water with a temperature of 99°C to the filtrate, and the time used for adding water is 15 seconds; then cool down to 48°C with an oil bath jacket for emulsification, and add 22.5 grams of bentonite slurry that...

Embodiment 3

[0047] Make glazing wax according to the following steps: 5 grams of silicone oil, 3 grams of vaseline, 7.5 grams of polyethylene, 0.1 grams of montan wax, 1 gram of coumarone-indene resin, 0.8 grams of carnauba wax, C 12 Nine raw materials including 0.5 g of fatty alcohol polyoxyethylene (n) ether, 1 g of nonylphenol polyoxyethylene (n) ether and 3.5 g of coconut oil diethanolamide (1:1 type) were added to the oil bath jacket for esterification In the pot, heat until the raw materials are melted and esterified, and then filter, and the filtered filtrate is placed in an oil bath jacket pot for emulsification; the temperature of the filtrate in the oil bath jacket pot for emulsification is kept at 101 ° C, under the condition of stirring, Add 8 grams of water with a temperature of 98°C to the filtrate, and the time used for adding water is 12 seconds; then cool down to 51°C in the oil bath jacket for emulsification, and add 12.5 grams of bentonite slurry that has absorbed water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The process provides one kind of polishing wax and its preparation process. The polishing wax consists of silicone oil 3-8 wt%, vaseline 0.2-5 wt%, polyethylene 0.1-8 wt%, montan wax 0.1-0.5 wt%, coumarone-indene resin 0.1-5 wt%, carnauba wax 0.1-1 wt%, C12 fatty alcohol polyoxyethylene ether 0.5-3 wt%, nonylphenol polyoxyethylene ether 1-5 wt%, alkyl alcohol amide 2-5 wt%, ammonium hexadecyl trimethyl chloride or ammonium octadecyl trimethyl chloride 2-8 wt%, bentonite 1-5 wt%, glutaraldehyde 0.05-0.1 wt% and water 46.4-89.85 wt%. The polishing wax has no corrosion to the paint surface, and can eliminate dirt from paint surface, make paint surface clean and bright, and form protecting film with high heat resistance, less ageing and good luster.

Description

technical field [0001] The invention relates to a glazing wax and a preparation method of the glazing wax. Background technique [0002] When the vehicle is running and parked, the paint surface on its exterior is easily polluted and damaged, and needs to be cleaned every once in a while. During cleaning, the paint surface is often waxed and polished with glazing wax. [0003] Most of the existing glazing waxes are solvent-type glazing waxes. The basic components of solvent-type glazing waxes are polystyrene and organic solvents, and a small amount of surfactants and polishing powders. Although solvent-based glazing wax has strong decontamination ability, because the paint can dissolve in organic solvents, when the varnish wax is applied to the paint surface, the paint surface will be corroded, penetrated and damaged, and it is easy to turn yellow. , becomes rough, dulls the finish, and hardens, cracks, and flakes off, deteriorating the exterior of the car; the organic solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09G1/10
Inventor 李而淮
Owner 李而淮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap