Water polyurethane latex composite compounding color coat art canvas and producing technique thereof

A water-based polyurethane and color coating technology, applied in the field of painting supplies, can solve the problems of losing softness and becoming hard

Inactive Publication Date: 2008-07-09
宋健
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the plasticizer in the product coating will escape during shelf placement and lose the initial softness and harden
In addition, many countries gradually restrict the use of plasticizers, a toxic chemical

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment one: the production process steps of water-based polyurethane emulsion compound color coating art canvas in the embodiment of the present invention are as follows: its composition formula is counted in parts by mass:

[0034] 1. Preparation of coating slurry:

[0035] Take 0.5 parts of hydroxypropyl cellulose and fully swell with 6 parts of pure water (12 parts of pure water in total) for 7 hours, then heat to 90°C and stir until completely dissolved, and mix with 10 parts of water-based polyurethane emulsion (APU), styrene-acrylate 30 parts of copolymer emulsion (styrene-acrylic emulsion), 0.3 parts of pigment slurry, 0.15 parts of glycerin, 0.2 parts of ethanol, and 0.25 parts of sodium benzoate are mixed and stirred evenly to form a gel; take 35 parts of lithopone, 15 parts of calcium carbonate and moisten with 6 parts of pure water Finally, add it to the above-mentioned glue solution, stir and mix evenly at room temperature to form a coating slurry for us...

Embodiment 2

[0039] Embodiment two: the production process steps of water-based polyurethane emulsion complex color coating art oil canvas in the embodiment of the present invention are as follows: its composition formula is counted in parts by mass:

[0040] 1. Preparation of coating slurry:

[0041] Take 0.4 parts of hydroxypropyl cellulose and fully swell with 6.25 parts of pure water (12.5 parts of pure water in total) for 8 hours, then heat to 85°C and stir until completely dissolved, and mix with 12 parts of water-based polyurethane emulsion (APU), styrene-acrylate 28 parts of copolymer emulsion (styrene-acrylic emulsion), 0.2 parts of pigment slurry, 0.2 parts of glycerin, 0.25 parts of ethanol, and 0.3 parts of sodium benzoate are mixed and stirred evenly to form a gel; 38 parts of lithopone and 10 parts of calcium carbonate are moistened with 6.25 parts of pure water Finally, add it to the above-mentioned glue solution, stir and mix evenly at room temperature to form a coating slu...

Embodiment 3

[0046]Embodiment three: the production process steps of water-based polyurethane emulsion complex color coating art oil canvas in the embodiment of the present invention are as follows: its composition formula is counted in parts by mass:

[0047] 1. Preparation of coating slurry:

[0048] Take 0.5 parts of hydroxypropyl cellulose and fully swell with 7 parts of pure water (14 parts of pure water in total) for 7.5 hours, then heat to 98°C and stir until completely dissolved, and mix with 15 parts of water-based polyurethane emulsion (APU), styrene-acrylate 32 parts of copolymer emulsion (styrene-acrylic emulsion), 0.15 parts of pigment slurry, 0.25 parts of glycerin, 0.3 parts of ethanol, and 0.25 parts of sodium benzoate are mixed and stirred evenly to form a glue; 40 parts of lithopone, 8.5 parts of calcium carbonate are moistened with 7 parts of pure water Finally, add it to the above-mentioned glue solution, stir and mix evenly at room temperature to form a coating slurry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-based polyurethane emulsion compounded colored coating art canvas and a manufacturing technique, in particular to a canvas for painting artist and hobbies to paint, which belongs to the technical field of painting articles. And the process for manufacturing comprises getting hydroxypropyl cellulose to swell, heat up, stir and dissolve with half purified water of the total amount, and mixing and evenly stirring water-based polyurethane emulsion, styrene monomer- acrylate copolymer emulsion, graining paste, glycerin, alcohol and sodium benzoate, getting lithopone powder and calcium carbonate to mix with the upper glue solution after wetting with the residual water of the total purified water, evenly stirring to be coating slurry in normal temperature, and then applying coating slurry on primary backing, drying and baking to be end products. The service performance of the art canvas of the invention is greatly improved, since aqueous polyurethane emulsion (APU) is utilized in the formula, therefore the thermoplasticity polyurethane emulsion has the advantages of easy filming, low temperature resistance, excellent elasticity, flexibility and the like.

Description

technical field [0001] The invention relates to a water-based polyurethane emulsion compound color coated art oil canvas and its production process, specifically for painting artists and lovers; it is suitable for oil painting, acrylic painting and gouache painting, and can also be used for interior decoration and decoration. Huang belongs to the technical field of painting supplies. Background technique [0002] In the existing technology, the artist's painting usually adopts to be coated with more than 3 layers of colored coating materials on the base substrate and dry to make the art oil canvas. The color coating material is made of polymer solution or its emulsion, such as polyvinyl alcohol, ethylene acetic acid homopolymer emulsion, polyacrylate copolymer emulsion, one-component or two-component or more emulsion compounding, as the coating base, adding more Quantitative fillers such as titanium dioxide, lithopone, talcum powder, calcium carbonate, zinc oxide, etc. are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00B05D1/38B05D3/02C09D101/00C09D125/00C09D175/04
Inventor 宋健
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com