Vitrification micro-sphere thermal insulating mortar with self humidity-conditioning function

A technology of vitrified microbeads and thermal insulation mortar, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., and can solve problems affecting the durability of thermal insulation mortar, thermal insulation performance, hollowing, etc.

Inactive Publication Date: 2008-08-06
张辉
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many problems in actual use. For example, due to the poor water retention of vitrified microbead insulation mortar, cracking and hollowing often occur. Adding chemical water-retaining materials or expansion agents will affect the vitrified microbeads. Other properties of thermal insulation mortar will even directly affect the durability of thermal insulation mortar
Moreover, due to improper operation in construction operations, it will also affect the performance of its thermal insulation performance. People have been studying ways to improve this situation, but in terms of improving its various performances, it is always the same. performance match

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: A vitrified microbead thermal insulation mortar with self-humidity adjustment function, its components and proportions (percentage by weight) are: vitrified microbeads: 30%, perlite sand: 5%, cement: 40% , redispersible latex powder: 1%, high silica mordenite powder (particle size ≤ 15μm): 23.8%, methyl hydroxyethyl cellulose ether: 0.05%, mixed fiber: 0.005%, thickener: 0.0002%, Water reducing agent: 0.002%. The mixed fiber is composed of crack-resistant fiber and lignin fiber, and its weight percentage is: 35% of crack-resistant fiber and 65% of lignin fiber.

[0011] The thickener is methyl hydroxyethyl cellulose ether; the water reducer is wood-based water reducer.

[0012] The preparation process of the above-mentioned mixed fiber is as follows: First, the lignin fiber of the above proportion is placed in the mixing equipment and fully stirred to make it fully puffed, and then the anti-cracking fiber of the above proportion is added to the mixing equ...

Embodiment 2

[0014] Embodiment 2: A vitrified microbead thermal insulation mortar with self-humidity adjustment function, its components and proportions (percentage by weight) are: vitrified microbeads: 50%, perlite sand: 5%, cement: 20% , redispersible latex powder: 3%, high silica mordenite powder (particle size ≤ 15μm): 21.8%, methyl hydroxyethyl cellulose ether: 0.1%, mixed fiber: 0.1%, thickener: 0.0003%, Water reducing agent: 0.005%. The mixed fiber is composed of crack-resistant fiber and lignin fiber, and its weight percentage is: 60% of crack-resistant fiber and 40% of lignin fiber.

[0015] The thickener is polyacrylamide; the water reducer is melamine-based high-efficiency water reducer.

[0016] The preparation process of the above-mentioned mixed fiber is as follows: First, the lignin fiber of the above proportion is placed in the mixing equipment and fully stirred to make it fully puffed, and then the anti-cracking fiber of the above proportion is added to the mixing equipme...

Embodiment 3

[0018] Embodiment 3: A vitrified microbead thermal insulation mortar with self-humidity adjustment function, its components and proportion (weight percentage) are: vitrified microbead: 40%, perlite sand: 10%, cement: 30% , redispersible latex powder: 2%, high silica mordenite powder (particle size ≤ 15μm): 17.8%, methyl hydroxyethyl cellulose ether: 0.05%, mixed fiber: 0.005%, thickener: 0.0002%, Water reducing agent: 0.005%. The mixed fiber is composed of crack-resistant fiber and lignin fiber, and its weight percentage is: 50% of crack-resistant fiber and 50% of lignin fiber.

[0019] The thickener is polyvinyl alcohol; the water reducer is a sulfamic acid-based high-efficiency water reducer.

[0020] The preparation process of the above-mentioned mixed fiber is as follows: First, the lignin fiber of the above proportion is placed in the mixing equipment and fully stirred to make it fully puffed, and then the anti-cracking fiber of the above proportion is added to the mixin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to vitrified microsphere thermal insulation mortar with a self-humidity-control function, which has components as follows: vitrified microsphere, perlite sand, cement, re-dispersible latex powder, high silicon mordenite powder, methyl hydroxyethylcellulose ether, blended fiber, thickener and water reducer. The invention successfully introduces natural zeolite into preparation of the vitrified microsphere thermal insulation mortar, which, on the one hand, improves compactness of the mortar and on the other hand does not reduce thermal insulation performance of the mortar and displays certain hydrophilicity, thus reducing the bleeding of the mortar; when the environmental temperature changes, the mortar is characterized by automatic moisture absorption or release which plays a role of conditioning moisture content of surrounding environment. Therefore, the thermal insulation performance of the mortar is not reduced but the strength is improved. Addition of hydration products in the mortar leads to density of internal structure and improves impermeability and frost resistance of the mortar. At the same time, the zeolite has good acid resistance; and after the natural zeolite is processed into the powder, the dosage of the cement can be replaced which undoubtedly makes contribution to improving the thermal insulation performance.

Description

technical field [0001] The invention relates to a thermal insulation mortar for building, in particular to thermal insulation mortar with better self-regulating humidity function, in particular vitrified microbead thermal insulation mortar with self-humidity adjustment function. Background technique [0002] With the continuous development of my country's basic construction, there are more and more buildings and structures of various types. The organization and construction of various buildings and structures of high quality is the foundation of the technological level, latest technological achievements and management level of various industries in my country in terms of construction engineering. logo and embodiment. At the same time, according to the characteristics of the project and the environmental conditions of use, it is also an important task for the construction industry and its engineering and technical personnel to meet the various functional requirements of modern...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/06C04B14/18C04B14/04C04B24/38
CPCC04B28/02C04B2111/28Y02W30/91C04B14/047C04B14/06C04B14/18C04B18/24C04B20/0048C04B20/008C04B24/383C04B2103/0057C04B2103/302C04B2103/44C04B14/22
Inventor 张辉杜发宪赵东东
Owner 张辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap